US5643666A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Solid surfaces which are prepared from copolyesters laminated onto a high resolution image
Assignee: Hunter Douglas Industries Switzerland GmbH
•
Filing: 1995-12-20
•
Granted: 1997-07-01
•
Expires: 2015-12-20
Abstract
Abstract This invention relates to a solid surface which is prepared from a copolyester laminated onto an image layer. More particularly, the solid surface contains an outer layer of transparent PETG copolyester, a polymeric film with a high resolution image printed thereon, and a backing layer. The image can be selected to give the solid surface the appearance of natural building materials, such a wood and stone.
Inventors
- 👤 Michael Dennis Eckart
- 👤 Raymond Lynn Goodson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:28
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/26; Y10T428/269; Y10T428/28; Y10T428/2848; Y10T428/31504; Y10T428/31786; Y10T428/3179; Y10T428/31797
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
168 words
A solid surface prepared from copolyesters laminated onto an image layer comprising: (A) an outer layer comprising a transparent PETG copolyester having an inherent viscosity of 0.5 to 1.2 dL/g, comprising (1) a dicarboxylic acid component comprising repeat units from at least 80 mole percent of terephthalic acid or dimethylterephthalate; and (2) a diol component comprising repeat units from ethylene glycol and 2 to 99 mole percent of cyclohexanedimethanol, based on 100 mole percent dicarboxylic acid and 100 mole percent diol; (B) a polymeric film having a top side and a bottom side, wherein an image is printed on one of said sides and said film is joined to said outer layer such that said image can be seen through said outer layer; and (C) a backing layer comprising a polymer selected from the group consisting of polyvinyl chloride and PETG copolyester, said backing layer having a side joined to said polymeric film opposite said outer layer; wherein said outer layer and said backing layer are thermally compatible.
Claim 2
Dependent Claim
168 words
A solid surface prepared from copolyesters laminated onto an image layer comprising: (A) an outer layer comprising a transparent PETG copolyester having an inherent viscosity of 0.5 to 1.2 dL/g, comprising (1) a dicarboxylic acid component comprising repeat units from at least 80 mole percent of terephthalic acid or dimethylterephthalate; and (2) a diol component comprising repeat units from ethylene glycol and 2 to 99 mole percent of cyclohexanedimethanol, based on 100 mole percent dicarboxylic acid and 100 mole percent diol; (B) a polymeric film having a top side and a bottom side, wherein an image is printed on one of said sides and said film is joined to said outer layer such that said image can be seen through said outer layer; and (C) a backing layer comprising a polymer selected from the group consisting of polyvinyl chloride and PETG copolyester, said backing layer having a side joined to said polymeric film opposite said outer layer; wherein said outer layer and said backing layer are thermally compatible.
Claim 3
Dependent Claim
34 words
The solid surface of claim 1 wherein the diol component of the PETG copolyester comprises repeat units from 67 to 75 mole percent of ethylene glycol and 33 to 25 mole percent of 1,4-cyclohexanedimethanol.
Claim 4
Dependent Claim
26 words
The solid surface of claim 1 wherein said polymeric film, component (B), is transparent and said image is printed on the bottom side of said film.
Claim 5
Dependent Claim
31 words
The solid surface of claim 1 wherein said outer layer, polymeric film, and backing layer are bonded together with sufficient strength, rigidity, and impact resistance for use as a building material.
Claim 6
Dependent Claim
15 words
The solid surface of claim 1 wherein said image is of a natural building material.
Claim 7
Dependent Claim
13 words
The solid surface of claim 5 wherein said natural building material is wood.
Claim 8
Dependent Claim
13 words
The solid surface of claim 5 wherein said natural building material is stone.
Claim 9
Dependent Claim
27 words
The solid surface of claim 1 wherein said image is printed using a high resolution process in the range of 872cm 2 to 3488 cm 2 .
Claim 10
Dependent Claim
15 words
The solid surface of claim 8 wherein said high resolution process is a gravure process.
Claim 11
Dependent Claim
17 words
The solid surface of claim 8 wherein said high resolution process comprises printing from a digitized image.
Claim 12
Dependent Claim
23 words
The solid surface of claim 1 wherein each of said outer layer and said backing layer is 0.76 mm to 6.4 mm thick.
Claim 13
Dependent Claim
19 words
The solid surface of claim 11 wherein said polymeric film, component (B), is 0.025 mm to 0.254 mm thick.
Claim 14
Dependent Claim
24 words
The solid surface of claim 1 wherein said polymeric film, component (C), is selected from the group consisting of polyvinyl chloride and PETG copolyester.
Claim 15
Dependent Claim
12 words
The solid surface of claim 1 wherein said solid surface is thermoformable.
Claim 16
Dependent Claim
16 words
The solid surface of claim 1 wherein said image is printed with a solvent-based laminating ink.
Claim 17
Dependent Claim
27 words
The solid surface of claim 1 further comprising a layer of colorless laminating ink between said top side of said polymeric film and said transparent outer layer.
Claim 18
Dependent Claim
36 words
The solid surface of claim 1 wherein said outer layer comprises a top surface, said solid surface further comprising a transparent bilayer coat laminated to said top surface, said bilayer coat comprising a hard, scratch-resistant coat.
Claim 19
Dependent Claim
41 words
The solid surface of claim 17 wherein said hard, scratch-resistant coat is selected from the group consisting of UV-cured cross-linked acrylic, electron-beam-cured cross-linked acrylic, vacuum-cured urethane, UV-cured or electron-beam-cured silicon with acrylic or heat cured urethane or plastisol, and combinations thereof.
Claim 20
Dependent Claim
24 words
The solid surface of claim 17 further comprising a layer of colorless solvent-based laminating ink between said transparent outer layer and said bilayer coat.
References Cited (Backward Citations)
US3396067A
Cited
US4289818A
Cited
US4433070A
Cited
US4544584A
Cited
US4433070B1
Cited
US4433070B2
Cited
US4544584B1
Cited
US4544584B2
Cited
US4433070B3
Cited
US5286290A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-30 | 2000-12-30 | 2001-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-30 | 2004-12-30 | 2005-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-30 | 2008-12-30 | 2009-07-01 | $7700.00 | Window Closed / Lapsed |