US5635269A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Precision-etched textured stop/start zone for magnetic-recording disks
Assignee: Tulip Memory Systems Inc
•
Filing: 1995-01-19
•
Granted: 1997-06-03
•
Expires: 2015-01-19
Abstract
Abstract A magnetic-recording disk comprising a metal substrate disk having a textured annular first surface area with an outer diameter which is substantially less than the diameter of the metal substrate is disclosed herein. The metal substrate disk further has a smooth annular second surface area between the first surface area's outer diameter and the metal substrate's circumferential edge. The textured annular first surface area has a laser-etched circular pattern. Furthermore the metal disk substrate of an aluminum alloy, a titanium alloy, or an austenitic stainless steel has a thin-film coating selected from the group consisting of nitrides, carbides, or borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum or tungsten.
Inventors
- 👤 Richard D. Weir
- 👤 Carl W. Nelson
- 👤 Neil D. Heiman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:29
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/74; G11B5/82; G11B5/62; G11B5/73; G11B5/7368; G11B5/7373; G11B5/7377; G11B5/739; G11B5/73911; G11B5/73917; G11B5/84; G11B5/8404; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
148 words
A magnetic-recording disk comprising: a metal substrate disk that is uncoated prior to the application of a thin-film coating onto a surface of the metal substrate disk; said thin-film coating on said surface of the metal substrate disk, wherein the material of the thin-film coating has a material hardness greater than that of the metal substrate disk and is selected from the group consisting of nitrides, carbides, and borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and wherein either an annular area of an outer surface of the thin-film coating is textured or an annular area of said surface of the metal substrate disk is textured; and a layer of magnetic-recording material composed of cobalt or a cobalt alloy and overlying said thin-film coating, wherein the layer of magnetic-recording material overlies and replicates the texturing of the thin-film coating or the metal substrate disk.
Claim 2
Dependent Claim
148 words
A magnetic-recording disk comprising: a metal substrate disk that is uncoated prior to the application of a thin-film coating onto a surface of the metal substrate disk; said thin-film coating on said surface of the metal substrate disk, wherein the material of the thin-film coating has a material hardness greater than that of the metal substrate disk and is selected from the group consisting of nitrides, carbides, and borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and wherein either an annular area of an outer surface of the thin-film coating is textured or an annular area of said surface of the metal substrate disk is textured; and a layer of magnetic-recording material composed of cobalt or a cobalt alloy and overlying said thin-film coating, wherein the layer of magnetic-recording material overlies and replicates the texturing of the thin-film coating or the metal substrate disk.
Claim 3
Dependent Claim
33 words
A magnetic-recording disk as recited in claim 1 wherein an annular area of the metal substrate disk is textured, and wherein the thin-film coating replicates the texturing of the underlying metal substrate disk.
Claim 4
Dependent Claim
31 words
A magnetic-recording disk as recited in claim 1 wherein the metal substrate disk is not textured, and wherein an annular area of the outer surface of the thin-film coating is textured.
Claim 5
Dependent Claim
31 words
A magnetic-recording disk as recited in claim 1 wherein the thin-film coating comprises a layer of the metal constituent of the thin-film coating contacting said surface of the metal substrate disk.
Claim 6
Dependent Claim
92 words
A magnetic-recording disk as recited in claim 1 wherein the thin-film coating comprises an inner region contacting said surface of the metal substrate disk and composed of the metal constituent of the thin-film coating, comprises an intermediate region adjacent to the inner region and composed of a nitride, carbide, or boride of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and comprises an outer region adjacent to the intermediate region and having a material hardness that is less than the material hardness of the intermediate region of the thin-film coating.
Claim 7
Dependent Claim
24 words
A magnetic-recording disk as recited in claim 1 wherein the thickness of the thin-film coating is within the range of 0.5 to 5.0 microns.
Claim 8
Dependent Claim
28 words
A magnetic-recording disk as recited in claim 3 wherein the material hardness of the thin-film coating is softer at an outer surface thereof than below the outer surface.
Claim 9
Dependent Claim
19 words
A magnetic-recording disk as recited in claim 7 wherein the outer surface of the thin-film coating is abrasively textured.
Claim 10
Dependent Claim
114 words
A magnetic-recording disk comprising: a metal substrate disk; a thin-film coating on a surface of the metal substrate disk, wherein the material of the thin-film coating has a material hardness greater than that of the metal substrate disk and is selected from the group consisting of carbides and borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and wherein either an annular area of an outer surface of the thin-film coating is textured or an annular area of said surface of the metal substrate disk is textured; and a layer of magnetic-recording material that overlies the thin-film coating and replicates the texturing of the thin-film coating or the metal substrate disk.
Claim 11
Dependent Claim
114 words
A magnetic-recording disk comprising: a metal substrate disk; a thin-film coating on a surface of the metal substrate disk, wherein the material of the thin-film coating has a material hardness greater than that of the metal substrate disk and is selected from the group consisting of carbides and borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and wherein either an annular area of an outer surface of the thin-film coating is textured or an annular area of said surface of the metal substrate disk is textured; and a layer of magnetic-recording material that overlies the thin-film coating and replicates the texturing of the thin-film coating or the metal substrate disk.
Claim 12
Independent Claim
132 words
A method for manufacturing magnetic-recording media, including the steps of: providing a metal substrate disk; applying a thin-film coating to a surface of the metal substrate disk, wherein the thin-film coating has a material hardness greater than that of the metal substrate disk and is selected from the group consisting of nitrides, carbides and borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and wherein either an annular area of an outer surface of the thin-film coating is textured or an annular area of said surface of the metal substrate disk is textured; and applying a layer of magnetic-recording material composed of cobalt or a cobalt alloy and overlying the thin-film coating to form a magnetic-recording medium having an outer surface at least a portion of which is textured.
Claim 13
Independent Claim
132 words
A method for manufacturing magnetic-recording media, including the steps of: providing a metal substrate disk; applying a thin-film coating to a surface of the metal substrate disk, wherein the thin-film coating has a material hardness greater than that of the metal substrate disk and is selected from the group consisting of nitrides, carbides and borides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and wherein either an annular area of an outer surface of the thin-film coating is textured or an annular area of said surface of the metal substrate disk is textured; and applying a layer of magnetic-recording material composed of cobalt or a cobalt alloy and overlying the thin-film coating to form a magnetic-recording medium having an outer surface at least a portion of which is textured.
Claim 14
Dependent Claim
36 words
A method as recited in claim 10 further comprising a step of texturing an annular area of the metal substrate disk and thereafter applying the thin-film coating to replicate the texturing of the metal substrate disk.
Claim 15
Dependent Claim
24 words
A method as recited in claim 10 further comprising a step of texturing an annular area of the outer surface of the thin-film coating.
Claim 16
Dependent Claim
85 words
A method as recited in claim 10 wherein the step of applying a thin-film coating includes the steps of first applying a inner coating of the metal constituent of the thin-film coating to the outer surface of the metal substrate disk, and then applying an intermediate coating of a nitride, carbide, or boride of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten, and then applying an outer coating having a material hardness that is less than the material hardness of the intermediate coating.
Claim 17
Dependent Claim
43 words
A method as recited in claim 10 further comprising the step of applying an underlayer of material after applying the thin-film coating and before applying the layer of magnetic-recording material, wherein the underlayer causes the magnetic-recording material to crystallize in a desired orientation.
Claim 18
Dependent Claim
29 words
A method as recited in claim 10 wherein the step of applying the thin-film coating results in a thin-film coating thickness within the range of 0.5 to 5.0 microns.
Claim 19
Dependent Claim
63 words
A method as recited in claim 10 wherein the step of applying a thin-film coating includes the steps of first applying a inner coating of the metal constituent of the thin-film coating to said surface of the metal substrate disk, and then applying an intermediate coating of a nitride, carbide, or boride of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, or tungsten.
Claim 20
Dependent Claim
42 words
A method as recited in claim 12 wherein the thin-film coating includes an outer region having a material hardness at the outer surface thereof that is less than the material hardness of the thin-film coating in a region below the outer region.
Claim 21
Dependent Claim
22 words
A method as recited in claim 17 further comprising a step of texturing the outer surface of the thin-film coating by abrasion.
Claim 22
Dependent Claim
35 words
A method as recited in claim 17 wherein the hardness of the outer region is controlled by controlling the percent content of the reacted nitrogen, carbon, or boron constituent during deposition of the outer region.
References Cited (Backward Citations)
US3900592A
Cited
US4565772A
Cited
JPS59148129A
Cited
JPS59217225A
Cited
US4614705A
Cited
US4743491A
Cited
US4698251A
Cited
US4911967A
Cited
US4743481A
Cited
US4839207A
Cited
US4877666A
Cited
US5008176A
Cited
US4946730A
Cited
EP0369784A2
Cited
US4973496A
Cited
EP0447025A1
Cited
US5062021A
Cited
US5108781A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-02 | 2000-12-02 | 2001-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-02 | 2004-12-02 | 2005-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-02 | 2008-12-02 | 2009-06-03 | $7700.00 | Window Closed / Lapsed |