US4743481A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Molding process for articles having an irregular shaped internal passage
Assignee: Flex Technologies Inc
•
Filing: 1986-11-26
•
Granted: 1988-05-10
•
Expires: 2006-11-26
Abstract
Abstract A process for making an article having an irregular internal passage utilizes a hollow polymer preform. The preform is filled with a relatively incompressible filler material such as a powder or a fluid, which supports the preform when it is placed in a mold, e.g. an injection mold. The filler enables the preform to withstand high molding pressures and prevents deflection and movement of the internal passage within the preform. The shell, a layer of a polymer material is then molded about the preform. After the final article has been formed, consisting of the preform and shell, the filler is removed for possible reuse.
Inventors
- 👤 James T. Quinlan
- 👤 James I. Seeley
- 👤 Christopher H. Corbett
- 👤 Thomas A. Marcincavage
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:53
CPC Classifications
F; F02; F02M; F02M35/00; F02M35/10; F02M35/10314; F02M35/10321; B; B29; B29C; B29C33/00; B29C33/12; B29C33/123; B29C33/44; B29C33/54; B29C45/00; B29C45/14; B29C45/14467; B29C45/14598; B29C45/14614; B29C45/14836; B29C70/00; B29C70/68; B29C70/72; B29D; B29D23/00; B29D23/001; B29D23/003; B29D23/006; F02M35/1034; F02M35/10347; B29C45/14336; B29C2045/1445; B29L; B29L2031/00; B29L2031/24; F05; F05C; F05C2225/00; F05C2225/08; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
85 words
A process for forming a complex article having a plurality of irregular internal passages, comprising the steps of: fabricating a plurality of polymer preforms each having an internal passage; assembling said preforms into a final configuration; placing said assembled preforms into a mold, and molding a layer of a polymer material about said assembled preforms in said mold to form a shell on the assembled preforms and form said complex article, with said preforms remaining as an integral part thereof and defining said internal passages.
Claim 2
Dependent Claim
85 words
A process for forming a complex article having a plurality of irregular internal passages, comprising the steps of: fabricating a plurality of polymer preforms each having an internal passage; assembling said preforms into a final configuration; placing said assembled preforms into a mold, and molding a layer of a polymer material about said assembled preforms in said mold to form a shell on the assembled preforms and form said complex article, with said preforms remaining as an integral part thereof and defining said internal passages.
Claim 3
Dependent Claim
19 words
A process according to claim 1, including injection molding said shell on the assembled preforms to form said article.
Claim 4
Dependent Claim
24 words
A process according to claim 1, including filling said preforms with a filler material before molding the layer of polymer material about said preforms.
Claim 5
Dependent Claim
15 words
A process according to claim 2, wherein the filler material is a relatively incompressible material.
Claim 6
Dependent Claim
13 words
A process according to claim 3, wherein said incompressible material is a powder.
Claim 7
Dependent Claim
13 words
A process according to claim 3, wherein said incompressible material is a liquid.
Claim 8
Dependent Claim
45 words
A process according to claim 3, including applying said incompressible material in such a manner to said preforms so that any pressure applied to said preforms during molding of the shell is substantially and equally distributed throughout said preform to prevent deformation of the preform.
Claim 9
Dependent Claim
22 words
A process according to claim 4, including removing said complex article from said mold and removing said incompressible material from said preforms.
Claim 10
Dependent Claim
28 words
A process according to claim 4, wherein said polymer molding material is a thermoplastic, and wherein said thermoplastic material has a high heat resistance temperature and low shrinkage.
Claim 11
Dependent Claim
32 words
A process according to claim 5, wherein said thermoplastic preforms have good heat resistance at a temperature of at least 250° F., and wherein said preform thermoplastic is a liquid crystal polymer.
Claim 12
Dependent Claim
91 words
A molded plastic article having a complex internal passage made by the steps comprising: forming a plurality of thermoplastic preforms having internal surfaces which when combined substantially match the complex internal passage of the article; loading said plurality of preforms in a predetermined pattern into a mold with said internal surfaces forming said complex internal passage; molding a plastic material on said preform; and forming said article having said preforms remaining as an integral part thereof whereby said internal surfaces of the preforms form said internal passage of the molded article.
Claim 13
Dependent Claim
91 words
A molded plastic article having a complex internal passage made by the steps comprising: forming a plurality of thermoplastic preforms having internal surfaces which when combined substantially match the complex internal passage of the article; loading said plurality of preforms in a predetermined pattern into a mold with said internal surfaces forming said complex internal passage; molding a plastic material on said preform; and forming said article having said preforms remaining as an integral part thereof whereby said internal surfaces of the preforms form said internal passage of the molded article.
Claim 14
Dependent Claim
25 words
A molded article according to claim 11 wherein an incompressible material is loaded into the preforms so that said preforms resist molding pressure during molding.
Claim 15
Dependent Claim
17 words
A molded article according to claim 12, wherein said incompressible material is a powder or a liquid.
Claim 16
Dependent Claim
19 words
A molded article according to claim 12, wherein said thermoplastic preform has a high heat resistance and low shrinkage.
Claim 17
Dependent Claim
26 words
A molded article according to claim 13, wherein said mold is an injection mold, and including injection molding of said plastic material into said injection mold.
Claim 18
Dependent Claim
17 words
A molded article according to claim 14, wherein said thermoplastic preform material is a liquid crystal polymer.
References Cited (Backward Citations)
US2569935A
Cited
US2995781A
Cited
US4289817A
Cited
US3719735A
Cited
US3929954A
Cited
FR2260433A2
Cited
US3991146A
Cited
US4239568A
Cited
US4314964A
Cited
US4352772A
Cited
US4515842A
Cited
US4464324A
Cited
US4424183A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-10 | 1991-11-09 | 1992-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-10 | 1995-11-09 | 1996-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-10 | 1999-11-09 | 2000-05-10 | $7700.00 | Window Closed / Lapsed |