High strength, fast absorbing, melt processable, gycolide-rich, poly(glycolide-co-p-dioxanone) copolymers
Assignee: Ethicon Inc
•
Filing: 1995-06-30
•
Granted: 1997-05-27
•
Expires: 2015-06-30
Abstract
Abstract Absorbable, segmented copolymers of aliphatic polyesters based on lactone monomers glycolide, and p-dioxanone are described. The segmented copolymers exhibit a broad range of properties, especially high strength and stiffness, and fast absorption rates and breaking strength retention (BSR) profiles, useful in a variety of medical devices. Most importantly, for suture applications where Vicryl®-like polyglcolide-polylactide sutures with excellent tensile properties, but shorter BSR profiles than Vicryl® are needed. The copolymers of the present invention have such properties, making them useful in plastic surgery where faster absorption times would lead to less tissue scarring.
Inventors
- 👤 Rao S. Bezwada
- 👤 Kevin Cooper
- 👤 Dennis D. Jamiolkowski
- 👤 Hugh D. Newman, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:21
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G63/82; C08G63/823; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/26; A61L17/00; A61L17/06; A61L17/10; A61L17/12; A61L31/00; A61L31/04; A61L31/06; C08G63/66; C08G63/664
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
75 words
An absorbable, biocompatible segmented copolymer comprising: a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide; and, a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone, wherein the polymer bas a weight average molecular weight of about 10,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 2
Dependent Claim
75 words
An absorbable, biocompatible segmented copolymer comprising: a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide; and, a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone, wherein the polymer bas a weight average molecular weight of about 10,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 3
Dependent Claim
40 words
The segmented copolymer of claim 1 wherein the copolymer has a molecular weight such that the inherent viscosity is from about 0.6 dL/g to about 3.0 dL/g as measured in HFIP at 25° C. at a concentration of 0.1 g/dL.
Claim 4
Dependent Claim
45 words
The segmented copolymer of claim 1 wherein the major component comprises about 30 mole percent to about 90 mole percent of repeating units of glycolide, and wherein the minor component comprises about 70 mole percent to about 10 mole percent of repeating units of p-dioxanone.
Claim 5
Dependent Claim
40 words
The segmented copolymer of claim 3 wherein the copolymer has a molecular weight such that the inherent viscosity is from about 0.6 dL/g to about 3.0 dL/g as measured in HFIP at 25° C. at a concentration of 0.1 g/dL.
Claim 6
Dependent Claim
45 words
The segmented copolymer of claim 1 wherein the repeating units of glycolide comprise about 30 mole percent to about 50 mole percent of the copolymer, and wherein the repeating units of p-dioxanone comprise about 50 mole percent to about 70 mole percent of the copolymer.
Claim 7
Dependent Claim
40 words
The segmented copolymer of claim 5 wherein the copolymer has a molecular weight such that the inherent viscosity is from about 0.6 dL/g to about 3.0 dL/g as measured in HFIP at 25° C. at a concentration of 0.1 g/dL.
Claim 8
Dependent Claim
88 words
An absorbable device for use in medical applications, the medical device comprising a segmented copolymer, said copolymer comprising: a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide; and, a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 20,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4 0 deciliters per gram.
Claim 9
Dependent Claim
88 words
An absorbable device for use in medical applications, the medical device comprising a segmented copolymer, said copolymer comprising: a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide; and, a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 20,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4 0 deciliters per gram.
Claim 10
Dependent Claim
87 words
An absorbable device for use in medical applications, the medical device comprising a segmented copolymer, said copolymer comprising: a major component comprising about 30 mole percent to about 90 mole percent of repeating units of glycolide, and, a minor component comprising about 70 mole percent to about 10 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 20,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 11
Dependent Claim
87 words
An absorbable device for use in medical applications, the medical device comprising a segmented copolymer, said copolymer comprising: a major component comprising about 30 mole percent to about 90 mole percent of repeating units of glycolide, and, a minor component comprising about 70 mole percent to about 10 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 20,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 12
Dependent Claim
79 words
An absorbable device for use in medical applications, the medical device comprising a segmented copolymer, said copolymer comprising: about 30 mole percent to about 50 mole percent of repeating units of glycolide; and, about 70 mole percent to about 50 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 20,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 13
Dependent Claim
79 words
An absorbable device for use in medical applications, the medical device comprising a segmented copolymer, said copolymer comprising: about 30 mole percent to about 50 mole percent of repeating units of glycolide; and, about 70 mole percent to about 50 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 20,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 14
Dependent Claim
89 words
A process for producing a segmented copolymer of p-dioxanone and glycolide, said process comprising heating a mixture of p-dioxanone monomer, p-dioxanone homopolymer, and glycolide monomer, to a sufficient temperature, said temperature ranging between about 100° C. and about 220° C., for a period of time to effectively produce a segmented copolymer comprising a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide and a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone.
Claim 15
Dependent Claim
89 words
A process for producing a segmented copolymer of p-dioxanone and glycolide, said process comprising heating a mixture of p-dioxanone monomer, p-dioxanone homopolymer, and glycolide monomer, to a sufficient temperature, said temperature ranging between about 100° C. and about 220° C., for a period of time to effectively produce a segmented copolymer comprising a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide and a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone.
Claim 16
Dependent Claim
138 words
A process for producing a segmented copolymer comprising the steps of: a) polymerizing p-dioxanone in the presence of a catalytically effective amount of catalyst and an initiator at a sufficient temperature of about 100° C. and about 130° C. and for a sufficient period of time to yield a first mixture of p-dioxanone monomer and p-dioxanone homopolymer; and b) adding glycolide to the first mixture to form a second mixture; and, c) polymerizing the second mixture at a sufficient temperature of about 180° C. to about 220° C. and for a sufficient amount of time to form a segmented copolymer comprising a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide and a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone.
Claim 17
Dependent Claim
138 words
A process for producing a segmented copolymer comprising the steps of: a) polymerizing p-dioxanone in the presence of a catalytically effective amount of catalyst and an initiator at a sufficient temperature of about 100° C. and about 130° C. and for a sufficient period of time to yield a first mixture of p-dioxanone monomer and p-dioxanone homopolymer; and b) adding glycolide to the first mixture to form a second mixture; and, c) polymerizing the second mixture at a sufficient temperature of about 180° C. to about 220° C. and for a sufficient amount of time to form a segmented copolymer comprising a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide and a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone.
Claim 18
Dependent Claim
61 words
The process of claim 11 for producing a segmented copolymer wherein the temperature for the initial polymerization is about 100° C. to about 130° C. and the time is about 5 to about 6 hours and the temperature for the second polymerization is about 180° C. to about 220° C., and the time is about 1 hour to about 4 hours.
Claim 19
Dependent Claim
35 words
The process of claim 12 wherein the amount of catalyst utilized is from about 10,000/1 to about 100,000/1, based on the molar ratio of monomer to catalyst, and wherein the catalyst is preferably tin based.
Claim 20
Dependent Claim
11 words
The process of claim 13 wherein the catalyst is stannous octoate.
Claim 21
Dependent Claim
45 words
The process of claim 12 wherein the amount of catalyst used comprises from about 100/1 to about 5,000/1, based on the molar ratio of monomer to initiator, and wherein the initiator is selected from the group consisting of alkanol, glycol, hydroxyacid, amine, and combinations thereof.
Claim 22
Dependent Claim
33 words
The process of claim 12 wherein the lactone monomer added in step (b) is glycolide and the temperature of the polymerization of the second mixture is about 180° C. to about 220° C.
Claim 23
Dependent Claim
39 words
The process of claim 16 wherein the segmented copolymer has a molecular weight such that the inherent viscosity is about 0.6 dL/g to about 3.0 dL/g as measured in HFIP at 25° C. at a concentration of 0.1 g/dL.
Claim 24
Dependent Claim
79 words
The process of claim 11 wherein the segmented copolymer comprises: a major component comprising about 30 mole percent to about 90 mole percent of repeating units of glycolide and, a minor component comprising about 70 mole percent to about 10 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 10,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram.
Claim 25
Dependent Claim
39 words
The process of claim 11 wherein the segmented copolymer comprises: about 30 mole percent to about 50 mole percent of repeating units of glycolide and, about 70 mole percent to about 50 mole percent of repeating units of p-dioxanone.
Claim 26
Dependent Claim
177 words
A process for manufacturing an absorbable, biocompatible segmented copolymer comprising a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide; and, a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 10,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram, wherein said segmented copolymer comprises the product of the process comprising the steps of: a) polymerizing p-dioxanone in the presence of a catalytically effective amount of catalyst and an initiator at a sufficient temperature of about 100° C. to about 130° C. and for a sufficient period of time to yield a first mixture of p-dioxanone monomer and p-dioxanone homopolymer; and b) adding glycolide to the first mixture to form a second mixture; and, c) polymerizing the second mixture at a sufficient temperature of about 180° C. to about 220° C. and for a sufficient amount of time.
Claim 27
Dependent Claim
177 words
A process for manufacturing an absorbable, biocompatible segmented copolymer comprising a major component comprising about 30 mole percent to about 95 mole percent of repeating units of glycolide; and, a minor component comprising about 70 mole percent to about 5 mole percent of repeating units of p-dioxanone, wherein the polymer has a weight average molecular weight of about 10,000 grams to about 300,000 grams per mole and an inherent viscosity of about 0.5 to about 4.0 deciliters per gram, wherein said segmented copolymer comprises the product of the process comprising the steps of: a) polymerizing p-dioxanone in the presence of a catalytically effective amount of catalyst and an initiator at a sufficient temperature of about 100° C. to about 130° C. and for a sufficient period of time to yield a first mixture of p-dioxanone monomer and p-dioxanone homopolymer; and b) adding glycolide to the first mixture to form a second mixture; and, c) polymerizing the second mixture at a sufficient temperature of about 180° C. to about 220° C. and for a sufficient amount of time.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-26 | 2000-11-25 | 2001-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-26 | 2004-11-25 | 2005-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-26 | 2008-11-25 | 2009-05-27 | $7700.00 | Window Closed / Lapsed |