Method for making metal interconnection with chlorine plasma etch
Assignee: Kawasaki Microelectronics Inc
•
Filing: 1995-12-08
•
Granted: 1997-05-06
•
Expires: 2015-12-08
Abstract
Abstract A metal interconnection is prepared by forming an underlying metal film of high melting point metal such as Ti and/or high melting point metal compound such as TiN layers above a semiconductor substrate, plasma etching the surface of the underlying metal film in a gas atmosphere containing chloride, and forming an interconnecting metal film such as Al, Cu, Au and Ag on the underlying metal film. Alternatively, a metal interconnection is prepared by forming an insulating film above a semiconductor substrate, forming connection holes in the insulating film, forming an underlying metal film such as TiN on the insulating film and the bottom and side wall of the connection holes by a CVD process under controlled conditions, and forming an interconnecting metal film such as Al on the underlying metal film. The TiN film has (111) preferential orientation and the aluminum film has (111) preferential orientation, smooth surface and effective coverage. The thus fabricated metal interconnection has improved reliability including electromigration immunity when used in semiconductor devices and finding advantageous use in miniaturized semiconductor devices.
Inventors
- 👤 Hiroshi Shinriki
- 👤 Takeshi Kaizuka
- 👤 Nobuyuki Takeyasu
- 👤 Tomohiro Ohta
- 👤 Eiichi Kondoh
- 👤 Hiroshi Yamamoto
- 👤 Tomoharu Katagiri
- 👤 Tadashi Nakano
- 👤 Yumiko Kawano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 04:10
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/033; H10W20/035; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10W20/036; H10W20/047; H10W20/048; H10W20/054; H10W20/056; H10W20/40; H10W20/41; H10W20/425
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
127 words
A method for forming a metal interconnection for use in a semiconductor device, said device comprising a semiconductor substrate, said method comprising the steps of: forming an insulating film having at least one connection hole the semiconductor substrate; forming an underlying metal film containing a refractory metal or a refractory metal compound on the insulating film and in the a least one connection hole; plasma etching a surface portion of the thickness of the underlying metal film in a gas atmosphere containing chlorine, the etched underlying metal film remaining on the insulating film; and forming an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the etched underlying metal film in the at least one connection hole.
Claim 2
Independent Claim
127 words
A method for forming a metal interconnection for use in a semiconductor device, said device comprising a semiconductor substrate, said method comprising the steps of: forming an insulating film having at least one connection hole the semiconductor substrate; forming an underlying metal film containing a refractory metal or a refractory metal compound on the insulating film and in the a least one connection hole; plasma etching a surface portion of the thickness of the underlying metal film in a gas atmosphere containing chlorine, the etched underlying metal film remaining on the insulating film; and forming an interconnecting metal film containing predominantly a component selected from the group consisting of Al, Cu, Au and Ag on the etched underlying metal film in the at least one connection hole.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein said interconnecting metal film is a metal film composed mainly of aluminum.
Claim 4
Dependent Claim
57 words
The method of claim 1, wherein the step of forming said underlying metal film is performed such that the uppermost portion of said underlying metal film is composed mainly of is at least one member selected from the group consisting of Ti, Ta, Nb, TiN, VN, W 2 N, VC, W 2 C, and Mo 2 N.
Claim 5
Dependent Claim
21 words
The method of claim 3, wherein an uppermost portion of said underlying metal film is composed mainly of Ti or TiN.
Claim 6
Dependent Claim
16 words
The method of claim 1, wherein said gas atmosphere contains BCl 3 or Cl 2 .
Claim 7
Dependent Claim
34 words
The method of claim 1, wherein the step of forming said interconnecting metal film includes depositing a film composed mainly of Al by a CVD process using an organic aluminum compound as a reactant.
Claim 8
Dependent Claim
12 words
The method of claim 6 wherein said organic aluminum compound is dimethylaluminumhydride.
Claim 9
Dependent Claim
60 words
The method of claim 7 wherein the step of forming said interconnecting metal film is a CVD process including heating the gas containing dimethylaluminumhydride in a concentration of X (mol %) at a temperature T (°C.) in the range: 100≦T≦210-3.3X, feeding the reactant gas toward the surface of said underlying metal film, and depositing the film composed mainly of Al.
Claim 10
Dependent Claim
46 words
The method of claim 6, wherein the step of forming said interconnecting metal film includes depositing the film composed mainly of Al by a CVD process using reactant gas containing dimethylaluminumhydride (DMAH) as the organic aluminum compound and cyclopentadienylcopper triethylphosphine (CpCuTEP) as an organic copper compound.
Claim 11
Dependent Claim
39 words
The method of claim 9, wherein the ratio defined by partial pressures of the organic copper compound and the organic aluminum compound in the reactant gas, as (CpCuTEP partial pressure)/(DMAH partial pressure+CpCuTEP partial pressure), is from 0.001 to 0.2.
Claim 12
Dependent Claim
41 words
The method of claim 1, wherein the step of forming said interconnecting metal film includes depositing a film composed mainly of Al by a sputtering process while maintaining the substrate at a temperature of not lower than at about 350° C.
Claim 13
Dependent Claim
22 words
The method of claim 1, wherein the step of forming said underlying metal film includes depositing a film by a CVD process.
Claim 14
Dependent Claim
28 words
The method of claim 12, wherein the step of forming said underlying metal film includes depositing a film composed mainly of TiN by a low pressure CVD process.
Claim 15
Dependent Claim
43 words
The method of claim 1, wherein the step of forming said underlying metal film includes: depositing a first metal film on the insulating film and in the at least one connection hole, and depositing a second metal film on the first metal film.
Claim 16
Dependent Claim
57 words
The method of claim 14, wherein said first metal film is composed mainly of a metal selected from the group consisting of Ti, Ta, and Nb, and said second metal film is composed mainly of a metal compound selected from the group consisting of TiN, VN, W 2 N, VC, W 2 C, and Mo 2 N.
Claim 17
Dependent Claim
26 words
The method of claim 15, wherein said metal of said first metal film is Ti and said metal compound of said second metal film is TiN.
Claim 18
Dependent Claim
28 words
The method of claim 16, wherein the step of depositing said second metal film composed mainly of said metal compound includes depositing the film by a CVD process.
Claim 19
Dependent Claim
24 words
The method of claim 17, wherein the CVD process is a low pressure CVD process using titanium halide and a nitriding substance as reactants.
Claim 20
Dependent Claim
54 words
The method of claim 18, wherein the titanium halide is TICl 4 , the nitriding substance is selected from the group consisting of NH 3 , hydrazine, and alkylhydrazines, and the partial pressure ratio of the nitriding substance to the titanium halide in the low pressure CVD gas atmosphere is from 11:1 to 28:1.
Claim 21
Dependent Claim
30 words
The method of claim 19, wherein the partial pressure ratio of the nitriding substance to the titanium halide in the low pressure CVD gas atmosphere is from 20:1 to 28:1.
Claim 22
Dependent Claim
43 words
The method of claim 1, wherein the step of forming the underlying metal film provides the underlying metal film selectively on said insulating film and in the at least one connection hole in a region where the metal interconnection is to be formed.
Claim 23
Dependent Claim
27 words
The method of claim 21, wherein the step of forming the interconnecting metal film includes selectively depositing the interconnecting metal film only on the underlying metal film.
Claim 24
Dependent Claim
34 words
The method of claim 22, wherein the step of forming said interconnecting metal film includes depositing a film composed mainly of Al by a CVD process using an organic aluminum compound as a reactant.
References Cited (Backward Citations)
US4944836A
Cited
JPS62105422A
Cited
US4960732A
Cited
US4948623A
Cited
US4963423A
Cited
US4994410A
Cited
US4897709A
Cited
JPH02170419A
Cited
US4923717A
Cited
US5179042A
Cited
JPH04225223A
Cited
JPH0430421A
Cited
US5008217A
Cited
US5270254A
Cited
US5486492A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-05 | 2000-11-04 | 2001-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-05 | 2004-11-04 | 2005-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-05 | 2008-11-04 | 2009-05-06 | $7700.00 | Window Closed / Lapsed |