Method of forming a thin film magnetic structure having ferromagnetic and antiferromagnetic layers
Assignee: Western Digital Technologies Inc
•
Filing: 1996-08-14
•
Granted: 1997-03-18
•
Expires: 2016-08-14
Abstract
Abstract A method of forming a magnetic structure having layers with different magnetization orientations provided by a common magnetic bias layer includes the steps of depositing an antiferromagnetic layer between first and second ferromagnetic layers. During the deposition of the first and second ferromagnetic layers, magnetization fields of different orientations are employed separately to induce different directions of magnetization in the first and second layers. The different directions of magnetization in the first and second layers are sustained, through the process of exchange coupling, by the interposed antiferromagnetic layer which serves as the bias layer. A magnetic structure thus fabricated, can be used as a read transducer capable of generating differential signals with common mode noise rejection, and can be used as a magnetic pole for a magnetic head with reduced Barkhausen noise.
Inventors
- 👤 Minshen Tan
- 👤 Hua-Ching Tong
- 👤 Francis H. Liu
- 👤 Swie-In Tan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:15
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/35; C23C14/351; B; B82; B82Y; B82Y25/00; B82Y40/00; G; G01; G01R; G01R33/00; G01R33/02; G01R33/06; G01R33/09; G01R33/093; G11; G11B; G11B5/00; G11B5/127; G11B5/31; G11B5/3109; G11B5/3113; G11B5/33; G11B5/39; G11B5/3903; G11B5/3906; G11B5/3945; G11B5/3948; H; H01; H01F; H01F10/00; H01F10/32; H01F10/3218; H01F10/324; H01F10/3254; H01F41/00; H01F41/14; H01F41/30; H01F41/302; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
95 words
A method of forming a thin film magnetic structure, comprising the steps of: providing a substrate; depositing a first layer of ferromagnetic material on said substrate in the presence of a magnetic field oriented in a first direction; depositing a layer of antiferromagnetic material on said first layer of ferromagnetic material; and depositing a second layer of ferromagnetic material on saidlayer of antiferromagnetic material in the presence of a magnetic field oriented in a second direction, said first layer of ferromagnetic material being spaced from said second layer of ferromagnetic material by said antiferromagnetic material.
Claim 2
Independent Claim
95 words
A method of forming a thin film magnetic structure, comprising the steps of: providing a substrate; depositing a first layer of ferromagnetic material on said substrate in the presence of a magnetic field oriented in a first direction; depositing a layer of antiferromagnetic material on said first layer of ferromagnetic material; and depositing a second layer of ferromagnetic material on saidlayer of antiferromagnetic material in the presence of a magnetic field oriented in a second direction, said first layer of ferromagnetic material being spaced from said second layer of ferromagnetic material by said antiferromagnetic material.
Claim 3
Dependent Claim
24 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said layer of antiferromagnetic material is electrically insulating.
Claim 4
Dependent Claim
41 words
The method of forming a thin film magnetic structure as set forth in claim 2 wherein said layer of electrically insulating antiferromagnetic material is formed of a material selected from the group of NiC--O, Ni--O and Fe 2 O 3 .
Claim 5
Dependent Claim
28 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said first and second magnetic field directions are antiparallel to each other.
Claim 6
Dependent Claim
28 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said first and second magnetic field directions are perpendicular to each other.
Claim 7
Dependent Claim
32 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said steps of depositing comprise the step of sputtering or the step of ion beam deposition.
Claim 8
Dependent Claim
32 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said first and second layers of ferromagnetic material are formed of Permalloy, NiFeCo, FeCo or Co.
Claim 9
Dependent Claim
29 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said layer of antiferromagnetic material is formed of ferrous manganese or nickel manganese.
Claim 10
Dependent Claim
32 words
The method of forming a thin film magnetic structure as set forth in claim 1 wherein said steps of depositing said layers are performed below the blocking temperature of said ferromagnetic material.
Claim 11
Independent Claim
107 words
A method of forming a thin film magnetic structure comprising the steps of: providing a substrate; applying a first magnetic field oriented in a first direction to said structure; depositing a first layer of ferromagnetic material on said substrate; depositing a layer of antiferromagnetic material on said first layer of ferromagnetic material; applying a second magnetic field oriented in a second direction to said structure; depositing a second layer of ferromagnetic material on said layer of antiferromagnetic material, such that said first layer of ferromagnetic material is spaced from said second layer of ferromagnetic material by said layer of antiferromagnetic material; and terminating said second magnetic field.
Claim 12
Independent Claim
107 words
A method of forming a thin film magnetic structure comprising the steps of: providing a substrate; applying a first magnetic field oriented in a first direction to said structure; depositing a first layer of ferromagnetic material on said substrate; depositing a layer of antiferromagnetic material on said first layer of ferromagnetic material; applying a second magnetic field oriented in a second direction to said structure; depositing a second layer of ferromagnetic material on said layer of antiferromagnetic material, such that said first layer of ferromagnetic material is spaced from said second layer of ferromagnetic material by said layer of antiferromagnetic material; and terminating said second magnetic field.
Claim 13
Dependent Claim
35 words
The method of forming a thin film magnetic structure as set forth in claim 10 wherein said steps of depositing said ferromagnetic layers are performed at temperatures below the blocking temperature of said ferromagnetic material.
Claim 14
Dependent Claim
41 words
The method of forming a thin film magnetic structure as set forth in claim 11 wherein said layer of antiferromagnetic material is formed from a material selected from the group comprising NiCo--O, Ni--O, Fe 2 O 3 , FeMn and NiMn.
Claim 15
Dependent Claim
26 words
The method of forming a thin film magnetic structure as set forth in claim 10 wherein said first and second directions are antiparallel to each other.
Claim 16
Dependent Claim
26 words
The method of forming a thin film magnetic structure as set forth in claim 10 wherein said first and second directions are perpendicular to each other.
Claim 17
Dependent Claim
24 words
The method of forming a thin film magnetic structure as set forth in claim 10 wherein said antiferromagnetic material comprises ferrous manganeseor nickel manganese.
Claim 18
Independent Claim
234 words
A method of forming a thin film magnetic structure having different magnetization orientations provided by a common magnetic bias layer, comprising the steps of: providing a substrate; depositing a first layer of ferromagnetic material on said substrate in the presence of a first magnetic field oriented in a first direction, said first magnetic field inducing a first direction of uniaxial anisotropy in said first layer; depositing on said first layer a layer of antiferromagnetic material having first and second major surfaces, said first major surface being in contact with said first layer of ferromagnetic material; and depositing on said layer of antiferromagnetic material a second layer of ferromagnetic material in the presence of a second magnetic field oriented in a second direction, said second layer of ferromagnetic material being in contact with said second major surface of said antiferromagnetic layer, said second magnetic field inducing a second direction of uniaxial anisotropy in said second layer, said first and second layers of ferromagnetic material being spaced from each other by said layer of antiferromagnetic material; wherein said first and second directions of uniaxial anisotropy mutually exchange-couple with said first and second major surfaces of said layer of antiferromagnetic material, such that said layer of antiferromagnetic material constitutes said common magnetic bias layer for providing different magnetization orientations as said first and second directions of uniaxial anisotropy in said first and second layers of ferromagnetic material.
Claim 19
Independent Claim
234 words
A method of forming a thin film magnetic structure having different magnetization orientations provided by a common magnetic bias layer, comprising the steps of: providing a substrate; depositing a first layer of ferromagnetic material on said substrate in the presence of a first magnetic field oriented in a first direction, said first magnetic field inducing a first direction of uniaxial anisotropy in said first layer; depositing on said first layer a layer of antiferromagnetic material having first and second major surfaces, said first major surface being in contact with said first layer of ferromagnetic material; and depositing on said layer of antiferromagnetic material a second layer of ferromagnetic material in the presence of a second magnetic field oriented in a second direction, said second layer of ferromagnetic material being in contact with said second major surface of said antiferromagnetic layer, said second magnetic field inducing a second direction of uniaxial anisotropy in said second layer, said first and second layers of ferromagnetic material being spaced from each other by said layer of antiferromagnetic material; wherein said first and second directions of uniaxial anisotropy mutually exchange-couple with said first and second major surfaces of said layer of antiferromagnetic material, such that said layer of antiferromagnetic material constitutes said common magnetic bias layer for providing different magnetization orientations as said first and second directions of uniaxial anisotropy in said first and second layers of ferromagnetic material.
Claim 20
Dependent Claim
29 words
The method of forming a thin film magnetic structure as set forth in claim 16 wherein said first and second directions are angularly oriented with respect to each other.
Claim 21
Dependent Claim
26 words
The method of forming a thin film magnetic structure as set forth in claim 16 wherein said first and second directions are antiparallel to each other.
Claim 22
Dependent Claim
49 words
The method of forming a thin film magnetic structure as set forth in claim 16 wherein said first and second layers comprise Permalloy and said layer of antiferromagnetic material is formed from a material selected from the group comprising NiCo--O, Ni--O, Fe 2 O 3 , FeMn and NiMn.
Claim 23
Dependent Claim
54 words
The method of forming a thin film magnetic structure as set forth in claim 19 where said layer of antiferromagnetic material is deposited to a thickness of between 200 to 250 Angstroms, and each of said first and second layers of ferromagnetic material is deposited to a thickness of between 100 to 200 Angstroms.
Claim 24
Dependent Claim
30 words
The method of forming a thin film magnetic structure as set forth in claim 16 wherein said steps of depositing comprise the step of sputtering or the ion beam deposition.
Claim 25
Dependent Claim
32 words
The method of forming a thin film magnetic structure as set forth in claim 16 wherein said steps of depositing said layers are performed below the blocking temperature of said ferromagnetic material.
Claim 26
Dependent Claim
34 words
The method of forming a thin film magnetic structure as set forth in claim 16, including the step of patterning electrical lead layers in contact with said first and second layers of ferromagnetic material.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-03-17 | 2000-09-16 | 2001-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-03-17 | 2004-09-16 | 2005-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-03-17 | 2008-09-16 | 2009-03-18 | $7700.00 | Window Closed / Lapsed |