Implant surface preparation utilizing acid treatment
Assignee: Innovative Implants Inc
•
Filing: 1996-05-20
•
Granted: 1997-02-18
•
Expires: 2016-05-20
Abstract
Abstract The surface of a device that is surgically implantable in living bone is prepared. The device is made of titanium with a native oxide layer on the surface. The method of preparation comprises the steps of removing the native oxide layer from the surface of the device and performing further treatment of the surface substantially in the absence of unreacted oxygen.
Inventors
- 👤 Keith D. Beaty
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:32
CPC Classifications
A; A61; A61C; A61C8/00; A61C8/0012; A61C8/0013; A61C8/0015; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61F2/30771; A61L; A61L27/00; A61L27/02; A61L27/04; A61L27/06; A61L27/28; A61L27/30; A61L27/306; A61L27/50; B; B24; B24C; B24C1/00; B24C1/08; B24C11/00; C; C23; C23F; C23F1/00; C23F1/02; C23F1/10; C23F1/14; C23F1/16; C23F1/26; C23G; C23G1/00; C23G1/02; C23G1/10; C23G1/106; A61C8/0018; A61C8/0037; A61C2008/0046; A61F2/3094; A61F2002/30838; A61F2002/30904; A61F2002/30906; A61F2002/30925; A61F2310/00; A61F2310/00005; A61F2310/00011; A61F2310/00023; A61F2310/00389; A61F2310/00592; A61F2310/00598; A61F2310/00616; A61F2310/00796; A61F2310/0097; A61F2310/00976; A61L2400/00; A61L2400/18; A61L2430/00; A61L2430/02; A61L2430/12; Y; Y10; Y10S; Y10S623/00; Y10S623/901; Y10S623/92
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
81 words
A method of preparing the surface of a device that is surgically implantable in living bone and that is made of titanium having a native oxide layer on the surface thereof, said method comprising the steps of grit blasting the surface of said device to roughen the surface, etching the grit blasted surface with hydrofluoric acid to remove the native oxide layer, and etching the resulting surface with a mixture of sulfuric and hydrochloric acids to produce a uniformly roughened surface.
Claim 2
Independent Claim
81 words
A method of preparing the surface of a device that is surgically implantable in living bone and that is made of titanium having a native oxide layer on the surface thereof, said method comprising the steps of grit blasting the surface of said device to roughen the surface, etching the grit blasted surface with hydrofluoric acid to remove the native oxide layer, and etching the resulting surface with a mixture of sulfuric and hydrochloric acids to produce a uniformly roughened surface.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the ratio of sulfuric acid to hydrochloric acid in said aqueous solution is approximately 6 to 1.
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein said acid etching is carried out at room temperature.
Claim 5
Dependent Claim
29 words
The method of claim 1 wherein said hydrofluoric acid is in an aqueous solution that produces an etch rate of from about 200 to about 350 Angstroms per minute.
Claim 6
Dependent Claim
34 words
The method of claim 1 which includes the step of depositing on the acid-etched surface at least one material selected from the group consisting of bone minerals, hydroxyapatite, whitlockite, bone morphogenic proteins and medicaments.
Claim 7
Dependent Claim
13 words
The method of claim 5 wherein said deposited material is in particulate form.
Claim 8
Dependent Claim
18 words
The method of claim 5 wherein said depositing step is carried out substantially in the absence of oxygen.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein the grit used in said grit blasting is composed of titanium or a dilute alloy of titanium.
Claim 10
Dependent Claim
25 words
The method of claim 1 wherein the grit used in said grit blasting has a particle size of from about 10 to about 60 microns.
Claim 11
Dependent Claim
23 words
The method of claim 1 wherein said grit blasting is carrted out at a pressure of from about 50 to about 80 psi.
Claim 12
Independent Claim
121 words
A method of preparing the surface of a dental implant made of titanium having on the surface thereof a native oxide layer having a thickness between about 70 and about 150 Angstroms, said method comprising the steps of removing the native oxide layer from the surface of the implant by immersing the implant in hydrofluoric acid of sufficient strength to etch the native oxide layer at a rate of at least 100 Angstroms per minute, removing the implant from the hydrofluoric acid after removal of the native oxide layer, and before re-oxidation of the etched surface, immersing the implant in a mixture of sulfuric acid and hydrochloric acid for about 3 to about 10 minutes to produce a uniformly etched surface.
Claim 13
Independent Claim
121 words
A method of preparing the surface of a dental implant made of titanium having on the surface thereof a native oxide layer having a thickness between about 70 and about 150 Angstroms, said method comprising the steps of removing the native oxide layer from the surface of the implant by immersing the implant in hydrofluoric acid of sufficient strength to etch the native oxide layer at a rate of at least 100 Angstroms per minute, removing the implant from the hydrofluoric acid after removal of the native oxide layer, and before re-oxidation of the etched surface, immersing the implant in a mixture of sulfuric acid and hydrochloric acid for about 3 to about 10 minutes to produce a uniformly etched surface.
Claim 14
Dependent Claim
23 words
The method of claim 11 wherein the ratio of sulfuric acid to hydrochloric acid in said aqueous solution is approximately 6 to 1.
Claim 15
Dependent Claim
35 words
The method of claim 11 which further includes the step of depositing on the acid-etched surface at least one material selected from the group consisting of bone minerals, hydroxyapatite, whitlockite, bone morphogenic proteins and medicaments.
Claim 16
Dependent Claim
18 words
The method of claim 13 wherein said depositing step is carrted out substantially in the absence of oxygen.
Claim 17
Dependent Claim
24 words
The method of claim 11 which further includes the step of grit blasting the implant surface prior to removal of the native oxide layer.
References Cited (Backward Citations)
US3855638A
Cited
US4145764A
Cited
US4818559A
Cited
US5071351A
Cited
US4908030A
Cited
US4944754A
Cited
US4911953A
Cited
US4874434A
Cited
US5188800A
Cited
US5456723A
Cited
US5190795A
Cited
US5344425A
Cited
US5484286A
Cited
EP0606566A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-18 | 2000-08-19 | 2001-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-18 | 2004-08-19 | 2005-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-18 | 2008-08-19 | 2009-02-18 | $7700.00 | Window Closed / Lapsed |