Abstract
Abstract The present invention relates to a method for chemically treating structures fabricated from titanium based alloy compositions which compositions inherently possess positive open circuit corrosion potentials and reduced rates of corrosion properties. The method comprises contacting said fabricated structures with an aqueous pickling solution of hydrofluoric and sulfuric acids at a temperature of at least ambient temperature. This contact is continued for a time sufficient to remove any deleterious oxide layers adhered to the surfaces of the alloy compositions of the fabricated structures.
Inventors
- 👤 Olen L. Riggs, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:48
CPC Classifications
C; C23; C23G; C23G1/00; C23G1/02; C23G1/10; C23G1/106; C23F; C23F1/00; C23F1/10; C23F1/14; C23F1/16; C23F1/26
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
170 words
A method for treating a structure fabricated from a titanium base alloy composition consisting essentially of about 0.25 to about 1.5 weight percent of iron and about 0.1 to about 1.5 weight percent of copper, based on the weight of the composition, the balance being substantially all titanium apart from incidental impurities and where said titanium base alloy composition further is characterized by inherent properties of positive open circuit corrosion potentials and substantially reduced rates of corrosion, said method comprising: providing an aqueous pickling solution comprising at least about 5 g/l of hydrofluoric acid and at least about 25 g/l of sulfuric acid; contacting said aqueous solution with said fabricated structure; and maintaining said aqueous solution, while in contact with said fabricated structure, at a temperature of at least about ambient temperature and continuing said contact at said temperature for a period ranging up to about 24 hours whereby upon discontinuing said contact, said inherent properties of the titanium base alloy composition from which the structure is fabricated are retained.
Claim 2
Independent Claim
170 words
A method for treating a structure fabricated from a titanium base alloy composition consisting essentially of about 0.25 to about 1.5 weight percent of iron and about 0.1 to about 1.5 weight percent of copper, based on the weight of the composition, the balance being substantially all titanium apart from incidental impurities and where said titanium base alloy composition further is characterized by inherent properties of positive open circuit corrosion potentials and substantially reduced rates of corrosion, said method comprising: providing an aqueous pickling solution comprising at least about 5 g/l of hydrofluoric acid and at least about 25 g/l of sulfuric acid; contacting said aqueous solution with said fabricated structure; and maintaining said aqueous solution, while in contact with said fabricated structure, at a temperature of at least about ambient temperature and continuing said contact at said temperature for a period ranging up to about 24 hours whereby upon discontinuing said contact, said inherent properties of the titanium base alloy composition from which the structure is fabricated are retained.
Claim 3
Dependent Claim
32 words
The method of claim 1 wherein said aqueous pickling solution comprises from about 5 to about 200 g/l of hydrofluoric acid and from about 25 to about 250 g/l of sulfuric acid.
Claim 4
Dependent Claim
52 words
The method of claim 1 wherein said aqueous pickling solution is maintained, while in contact with said fabricated structure, at a temperature of from about ambient temperature to about 150° C. and wherein said contact is continued at said temperature for a period of from about 0.5 minutes to about 24 hours.
Claim 5
Dependent Claim
43 words
The method of claim 3 wherein said aqueous solution is maintained at a temperature of from about 100° C. to about 125° C. and wherein said contact is continued at said temperature for a period of from about 0.5 to about 5.0 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-16 | 1993-04-17 | 1993-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-16 | 1997-04-17 | 1997-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-16 | 2001-04-17 | 2001-10-17 | $7700.00 | Window Closed / Lapsed |