Method for producing flexible circuit boards
Assignee: Nippon Graphite Industries Ltd
•
Filing: 1995-11-07
•
Granted: 1997-02-18
•
Expires: 2015-11-07
Abstract
Abstract An adhesive is applied onto a flexible resistive film 1 and dried to form an adhesive layer 2. A metal foil 3 is contacted onto the layer 2, which is subjected to a heat and pressing treatment. The foil 3 is polished. An ultraviolet light curable ink is applied on the foil 3 and dried to form a first layer 4. A negative film is placed on or over the layer 4 and ultraviolet light is irradiated thereto through the film so that the layer 4 is cured. Uncured portions of the layer 4 is removed so that cured portions thereof remain and the foil 3 is exposed between the remaining cured portions. The metal foil 3 is subjected to an etching treatment to remove exposed portions of the foil 3 so that unexposed portions of the foil 3 remain and form conductors 3A. The cured portions of the layer 4 is removed from the conductors 3A. A metal plating film 5 is formed on each conductor 3A to form each electrical conductive circuit 9. An ultraviolet light curable ink is applied on the layer 2 and dried to form a second layer 7. Ultraviolet light is irradiated to the layer 7 through the film 1 so that the layer 7 is cured in gaps 6 between the circuits 9. Uncured portions of the layer 7 is removed so that the circuits 9 are exposed and cured portions of the layer 7 remain in the gaps 6. The cured portions of the layer 7 is subjected to a heat treatment. The resulting flexible circuit board comprises the film 1, the adhesive layer 2, the circuits 9 and cured films 8 filling the gaps 6.
Inventors
- 👤 Katsuhiro Murata
- 👤 Mitsumasa Shibata
- 👤 Toru Hatakeyama
- 👤 Tadaaki Isono
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:25
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/36; H05K3/361; H05K1/00; H05K1/02; H05K1/03; H05K1/0393; H05K2201/00; H05K2201/09; H05K2201/09818; H05K2201/09881; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/0723; H05K3/24; H05K3/244; H05K3/30; H05K3/32; H05K3/321; H05K3/323; H05K3/34; H05K3/3465; H05K3/3473; H05K3/38; H05K3/386; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
352 words
A process for producing a flexible circuit board comprising the steps of: (A) applying an adhesive onto a flexible resistive film and drying the adhesive to form an adhesive layer; (B) contacting a metal foil onto said adhesive layer, which is subjected to a heat and pressing treatment so that said flexible resistive film and said metal foil are adhered to each other; (C) polishing a surface of said metal foil to obtain a polished surface, onto which an ultraviolet light curable ink is applied and dried to form a first layer composed of said ultraviolet light curable ink; (D) placing a negative film with a predetermined pattern on or over said first layer and irradiating ultraviolet light to said first layer through said negative film so that said first layer is cured according to said predetermined pattern; (E) removing uncured portions of said first layer in the stage (D) so that cured portions of said first layer remains according to said predetermined pattern and said metal foil is exposed between said remaining cured portions; (F) subjecting said metal foil to an etching treatment to remove the exposed portions of said metal foil between said cured portions so that unexposed portions of said metal foil under said cured portions remain to form conductors; (G) removing said cured portions of said first layer from said conductors of metal foil; (H) forming a metal plating film on each conductor to form each electrical conductive circuit comprising said conductor and said metal plating film covering a surface of said conductor; (I) applying an ultraviolet light curable ink on said adhesive layer and drying said ink to form a second layer composed of said ink; (J) irradiating ultraviolet light to said second layer through said flexible resistive film so that said second layer is cured by the ultraviolet light in gaps between said electrical conductive circuits; (K) removing uncured portions of said second layer so that said electrical conductive circuits are exposed and cured portions of said second layer remains in said gaps; (L) subjecting said cured portions of said second layer to a heat treatment.
Claim 2
Dependent Claim
352 words
A process for producing a flexible circuit board comprising the steps of: (A) applying an adhesive onto a flexible resistive film and drying the adhesive to form an adhesive layer; (B) contacting a metal foil onto said adhesive layer, which is subjected to a heat and pressing treatment so that said flexible resistive film and said metal foil are adhered to each other; (C) polishing a surface of said metal foil to obtain a polished surface, onto which an ultraviolet light curable ink is applied and dried to form a first layer composed of said ultraviolet light curable ink; (D) placing a negative film with a predetermined pattern on or over said first layer and irradiating ultraviolet light to said first layer through said negative film so that said first layer is cured according to said predetermined pattern; (E) removing uncured portions of said first layer in the stage (D) so that cured portions of said first layer remains according to said predetermined pattern and said metal foil is exposed between said remaining cured portions; (F) subjecting said metal foil to an etching treatment to remove the exposed portions of said metal foil between said cured portions so that unexposed portions of said metal foil under said cured portions remain to form conductors; (G) removing said cured portions of said first layer from said conductors of metal foil; (H) forming a metal plating film on each conductor to form each electrical conductive circuit comprising said conductor and said metal plating film covering a surface of said conductor; (I) applying an ultraviolet light curable ink on said adhesive layer and drying said ink to form a second layer composed of said ink; (J) irradiating ultraviolet light to said second layer through said flexible resistive film so that said second layer is cured by the ultraviolet light in gaps between said electrical conductive circuits; (K) removing uncured portions of said second layer so that said electrical conductive circuits are exposed and cured portions of said second layer remains in said gaps; (L) subjecting said cured portions of said second layer to a heat treatment.
Claim 3
Dependent Claim
116 words
The process for producing a flexible circuit board as claimed in claim 1, wherein, in the stage (I), said ultraviolet light curable ink is a negative type photoetching resist ink comprising one or more photosensitive polymer selected from a group consisting of a photosensitive acrylic polymer and a photosensitive epoxy polymer, as its main component, an apparent specific gravity of said ultraviolet light curable ink is 0.9 to 2.0, a viscosity thereof is 0.1 to 1000 poise, a thickness of an applied layer of said ultraviolet light curable ink is 10 to 80 μm and said ultraviolet light curable ink is dried in a temperature of 20° to 80° C. for 10 minutes to 12 hours.
Claim 4
Dependent Claim
45 words
The process for producing a flexible circuit board as claimed in claim 2, wherein, in the stage (L), said cured portions of said second layer are subjected to a heat treatment in a temperature of 100° to 150° C. for 10 minutes to 3 hours.
Claim 5
Dependent Claim
51 words
The process for producing a flexible circuit board as claimed in claim 1, wherein, in the stage (A), said flexible resistive film is made of one or more resin selected from a group consisting of a polyester resin, a polyimide resin, a polyetherimide resin, a polycarbonate resin and an aramide resin.
Claim 6
Dependent Claim
101 words
The process for producing a flexible circuit board as claimed in claim 4, wherein said adhesive layer is formed of an epoxy adhesive and a thickness of an applied layer of said adhesive before drying is 5.0 to 30.0 μm in the stage (A), and a thickness of said metal foil is 4 to 70 μm, said heat and pressing treatment is carried out in a temperature of 100° C. to 150° C. and in a pressure of 1 to 5 kg/cm and said adhesive layer is aftercured in a temperature of 80° to 180° C. for 1 to 24 hours.
Claim 7
Dependent Claim
81 words
The process for producing a flexible circuit board as claimed in claim 4, wherein, in the stage (C), said ultraviolet light curable ink is a photoetching resist ink comprising a photosensitive acrylic polymer or a photosensitive epoxy polymer as its main component, an apparent specific gravity of said ultraviolet light curable ink is 0.9 to 2.0, a viscosity thereof is 0.1 to 1000 poise, and a thickness of an applied layer of the ink before drying is 5 to 20 μm.
Claim 8
Dependent Claim
134 words
The process for producing a flexible circuit board as claimed in claim 4, wherein said cured portions of said first layer are removed from said conductors of said metal foil by washing said cured portions with a weak alkaline solution and exposed surfaces of said conductors are subjected to a surface activating treatment by using an acidic solution in the stage (G), and said metal plating film comprises one or more metal plating film selected from a group consisting of a solder plating film, a tin plating film, a nickel plating film and a gold plating film, a thickness of said metal plating film is 0.5 to 15 μm and said flexible resistive film is dried in a temperature of 40° to 100° C. after forming said metal plating film in the stage (H).
References Cited (Backward Citations)
US3301730A
Cited
US4608274A
Cited
US4497975A
Cited
US4584039A
Cited
US4797508A
Cited
US4853277A
Cited
JPH01152736A
Cited
JPH01152737A
Cited
US5084124A
Cited
US5369881A
Cited
US5334421A
Cited
US5331117A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-18 | 2000-08-19 | 2001-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-18 | 2004-08-19 | 2005-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-18 | 2008-08-19 | 2009-02-18 | $7700.00 | Window Closed / Lapsed |