Method for making a semiconductor device
Assignee: Sony Corp
•
Filing: 1996-01-25
•
Granted: 1997-02-11
•
Expires: 2016-01-25
Abstract
Abstract A method for making a microfine semiconductor device includes the step of forming a diffusion layer of a small depth to provide reduced junction leak current. Si ions are implanted at a dosage of from 1×10 15 to 1×10 16 cm -2 into an Si substrate held at a temperature not higher than -40° C. Then, impurity ion implantation into the Si substrate is conducted so as to form an impurity layer having a depth smaller than that of the amorphous layer. Consequently, it is possible to form an amorphous layer wherein elongation and an increase of dislocation loops at the interface between the amorphous layer and crystalline layer is suppressed. It is also possible to activate the impurity layer through annealing and still provide an impurity layer having a depth smaller than that of the amorphous layer.
Inventors
- 👤 Hideki Kimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:53
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/202; H10P30/204; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0218; H10D30/022; H10D30/0223; H10D30/0227; H10D30/60; H10D30/601; H10D62/00; H10D62/10; H10D62/13; H10D62/149; H10D62/151; H10D62/17; H10D62/351; H10D62/357; H10D62/364; H10D62/371; H10P30/208; H10P30/21; H10P30/225; H10P30/226; H10P30/28; Y; Y10; Y10S; Y10S438/00; Y10S438/909
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
115 words
A method for making a semiconductor device comprising the steps of: providing a silicon substrate; cooling the substrate to a temperature of -40° C. or less and implanting Si ions into a surface of the substrate at a dosage of from about 1×10 15 to 1×10 16 ions/cm 2 to preamorphize the surface of the silicon substrate to form an amorphous layer having a first depth dimension; implanting impurity ions in the preamorphized surface to form an impurity layer having a second depth dimension less than that of the amorphous layer; and thereafter, annealing the silicon substrate in an atmosphere comprising a halogen element after said impurity implantation step to activate the implanted impurity ions.
Claim 2
Independent Claim
115 words
A method for making a semiconductor device comprising the steps of: providing a silicon substrate; cooling the substrate to a temperature of -40° C. or less and implanting Si ions into a surface of the substrate at a dosage of from about 1×10 15 to 1×10 16 ions/cm 2 to preamorphize the surface of the silicon substrate to form an amorphous layer having a first depth dimension; implanting impurity ions in the preamorphized surface to form an impurity layer having a second depth dimension less than that of the amorphous layer; and thereafter, annealing the silicon substrate in an atmosphere comprising a halogen element after said impurity implantation step to activate the implanted impurity ions.
Claim 3
Independent Claim
129 words
A method for making a semiconductor device comprising the steps of: providing a silicon substrate; cooling the substrate to a temperature of about 0° C. or below and implanting ions selected from the group consisting of Ga ions, Ge ions, and As ions into the silicon substrate at a dosage of from about 3×10 14 to about 1×10 16 ions/cm 2 to preamorphize a surface of the silicon substrate to form an amorphous layer having a first depth dimension; implanting impurity ions into the surface of the substrate to form an impurity layer having a second depth dimension less than that of the amorphous layer; and thereafter, annealing the silicon substrate in an atmosphere comprising a halogen element after said impurity implantation step to activate the implanted impurity ions.
Claim 4
Independent Claim
129 words
A method for making a semiconductor device comprising the steps of: providing a silicon substrate; cooling the substrate to a temperature of about 0° C. or below and implanting ions selected from the group consisting of Ga ions, Ge ions, and As ions into the silicon substrate at a dosage of from about 3×10 14 to about 1×10 16 ions/cm 2 to preamorphize a surface of the silicon substrate to form an amorphous layer having a first depth dimension; implanting impurity ions into the surface of the substrate to form an impurity layer having a second depth dimension less than that of the amorphous layer; and thereafter, annealing the silicon substrate in an atmosphere comprising a halogen element after said impurity implantation step to activate the implanted impurity ions.
Claim 5
Dependent Claim
19 words
The method as defined in claim 1, wherein the silicon substrate is cooled during said impurity ion implantation step.
Claim 6
Dependent Claim
19 words
The method as defined in claim 2, wherein the silicon substrate is cooled during said impurity ion implantation step.
Claim 7
Dependent Claim
15 words
A method as defined in claim 1, wherein said atmosphere comprises NF 3 or HCl.
Claim 8
Dependent Claim
39 words
A method as defined in claim 1, wherein said annealing step is performed by heating the substrate to a temperature of from about 800° to about 900° C. for a period of from about 10 to about 60 minutes.
Claim 9
Dependent Claim
40 words
A method as defined in claim 1, wherein said annealing step is performed by rapidly heating the substrate to a temperature of from about 900° to about 1100° C. for a period of from about 1 to about 300 seconds.
Claim 10
Dependent Claim
26 words
A method as defined in claim 1, wherein the implantation of Si ions is performed using a mask comprising a gate electrode of an MOS transistor.
Claim 11
Dependent Claim
18 words
A method as defined in claim 8, wherein said mask further comprises sidewalls formed in said gate electrode.
Claim 12
Dependent Claim
32 words
A method as defined in claim 1, wherein said impurity layer is formed in a lightly-doped impurity layer comprising a first impurity type in an LDD structure defined in the silicon substrate.
Claim 13
Dependent Claim
38 words
A method as defined in claim 10, further comprising the step of forming a pocket layer under the lightly-doped impurity layer by introducing an impurity of an opposite type to said first impurity type in the silicon substrate.
Claim 14
Dependent Claim
15 words
A method as defined in claim 2, wherein said atmosphere comprises NF 3 or HCl.
Claim 15
Dependent Claim
39 words
A method as defined in claim 2, wherein said annealing step is performed by heating the substrate to a temperature of from about 800° to about 900° C. for a period of from about 10 to about 60 minutes.
Claim 16
Dependent Claim
40 words
A method as defined in claim 2, wherein said annealing step is performed by rapidly heating the substrate to a temperature of from about 900° to about 1100° C. for a period of from about 1 to about 300 seconds.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-11 | 2000-08-12 | 2001-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-11 | 2004-08-12 | 2005-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-11 | 2008-08-12 | 2009-02-11 | $7700.00 | Window Closed / Lapsed |