Process for thickening selective gate oxide regions
Assignee: Texas Instruments Inc
•
Filing: 1994-10-28
•
Granted: 1997-01-21
•
Expires: 2014-10-28
Abstract
Abstract One embodiment of the present invention is a method of simultaneously forming high-voltage (12) and low-voltage (10) devices on a single substrate (14), the method comprising: forming a thin oxide layer (18) on the substrate, the thin oxide layer having a desired thickness for a gate oxide for the low-voltage device; selectively forming a gate structure (30) for the high-voltage device, the thin oxide is situated between the gate structure and the substrate; and selectively thickening the thin oxide under the gate structure while keeping the thin oxide layer utilized for the low-voltage device at the desired thickness.
Inventors
- 👤 Howard L. Tigelaar
- 👤 Bert R. Riemenschneider
- 👤 Richard A. Chapman
- 👤 Andrew T. Appel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:46
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D84/0123; H10D84/0126; H10D84/0144; H10D84/0165; H10D84/0181; H10D84/02; H10D84/03; H10D84/038; H10D64/01346; Y; Y10; Y10S; Y10S438/00; Y10S438/911; Y10S438/981
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
204 words
A method of simultaneously forming a first transistor and a second transistor on a single substrate for an electrical device structure, said method comprising: providing a substrate, said substrate having a first region for said first transistor and a second region for said second transistor; forming an oxide layer on said substrate, said oxide layer having a first thickness; forming a conductive layer on said oxide layer, said conductive layer covering said oxide layer and said substrate in said first region and said second region; removing portions of said conductive layer in said first region to form a gate structure for said first transistor and so as to leave said conductive layer remaining in said second region; after forming said gate structure for said first transistor, thickening said oxide layer under the entire width of said gate structure for said first transistor to a second thickness while leaving said oxide layer in said second region at said first thickness; and removing portions of said conductive layer in said second region so as to form a gate structure for said second transistor, said oxide layer having a thickness of said first thickness is disposed between said gate structure for said second transistor and said substrate.
Claim 2
Independent Claim
204 words
A method of simultaneously forming a first transistor and a second transistor on a single substrate for an electrical device structure, said method comprising: providing a substrate, said substrate having a first region for said first transistor and a second region for said second transistor; forming an oxide layer on said substrate, said oxide layer having a first thickness; forming a conductive layer on said oxide layer, said conductive layer covering said oxide layer and said substrate in said first region and said second region; removing portions of said conductive layer in said first region to form a gate structure for said first transistor and so as to leave said conductive layer remaining in said second region; after forming said gate structure for said first transistor, thickening said oxide layer under the entire width of said gate structure for said first transistor to a second thickness while leaving said oxide layer in said second region at said first thickness; and removing portions of said conductive layer in said second region so as to form a gate structure for said second transistor, said oxide layer having a thickness of said first thickness is disposed between said gate structure for said second transistor and said substrate.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein a blocking layer is formed on said conductive layer.
Claim 4
Dependent Claim
49 words
The method of claim 2 wherein said blocking layer is formed prior to said step of said removing portions of said conductive layer in said second region, and portions of said blocking layer are removed during said step of removing portions of said conductive layer in said second region.
Claim 5
Dependent Claim
27 words
The method of claim 2 wherein said blocking layer is comprised of a material selected from the group of: silicon nitrides, titanium nitrides, or any combination thereof.
Claim 6
Dependent Claim
17 words
The method of claim 2 wherein said blocking layer is comprised of Si 2 N 4 .
Claim 7
Dependent Claim
13 words
The method of claim 2 wherein said blocking layer is comprised of TiN.
Claim 8
Dependent Claim
33 words
The method of claim 1 wherein said step of thickening said oxide layer is performed by subjecting said electrical device structure to a dry oxidizing atmosphere at between 800° C. and 1000° C.
Claim 9
Dependent Claim
34 words
The method of claim 7 wherein said step of subjecting said electrical device structure to a dry oxidizing atmosphere is performed by subjecting said electrical device to said atmosphere for 30 to 50 minutes.
Claim 10
Dependent Claim
32 words
The method of claim 8 wherein said oxide layer will have a thickness of between 80 and 100Å for said gate structure for said first transistor that is approximately 0.6 μm wide.
Claim 11
Dependent Claim
32 words
The method of claim 8 wherein said oxide layer will have a thickness of between 50 and 70Å for said gate structure for said first transistor that is approximately 0.35 μm wide.
Claim 12
Dependent Claim
32 words
The method of claim 1 wherein said step of thickening said oxide layer is performed by subjecting said electrical device structure to a steam atmosphere at between 800° C. and 1000° C.
Claim 13
Dependent Claim
36 words
The method of claim 11 wherein said step of subjecting said electrical device structure to a wet oxidizing atmosphere is performed by subjecting said electrical device to said wet oxidizing atmosphere for 10 to 50 minutes.
Claim 14
Dependent Claim
32 words
The method of claim 12 wherein said oxide layer will have a thickness of between 80 and 100Å for said gate structure for said first transistor that is approximately 0.6 μm wide.
Claim 15
Dependent Claim
32 words
The method of claim 12 wherein said oxide layer will have a thickness of between 50 and 70Å for said gate structure for said first transistor that is approximately 0.35 μm wide.
References Cited (Backward Citations)
US4313256A
Cited
US4516313A
Cited
EP0244367A2
Cited
JPH02187063A
Cited
JPH02230775A
Cited
US5057449A
Cited
US5208175A
Cited
US5314834A
Cited
US5371026A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-21 | 2000-07-22 | 2001-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-21 | 2004-07-22 | 2005-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-21 | 2008-07-22 | 2009-01-21 | $7700.00 | Window Closed / Lapsed |