Aluminum containing iron-base alloys useful as electrical resistance heating elements
Assignee: Philip Morris USA Inc
•
Filing: 1994-12-29
•
Granted: 1997-01-21
•
Expires: 2014-12-29
Abstract
Abstract The invention relates generally to aluminum containing iron-base alloys useful as electrical resistance heating elements. The aluminum containing iron-base alloys have a disordered body centered cubic structure and improved room temperature ductility, electrical resistivity, cyclic fatigue resistance, high temperature oxidation resistance, low and high temperature strength, and/or resistance to high temperature sagging. The alloy has an entirely ferritic microstructure which is free of austenite and includes, in weight %, 4 to 9.5% Al, 0.2-2.0% Ti, 0.5-2% Mo, 0.1 to 0.8% Zr, 0.01-0.5% C, balance Fe.
Inventors
- 👤 Vinod K. Sikka
- 👤 Seetharama C. Deevi
- 👤 Grier S. Fleischhauer
- 👤 Mohammad R. Hajaligol
- 👤 A. Clifton Lilly, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 19:27
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C38/00; C22C38/06; B; B22; B22F; B22F2998/00; B22F2998/10; B22F2999/00
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
60 words
An iron-based alloy useful as an electrical resistance heating element and having a disordered body centered cubic structure, the alloy having improved room temperature ductility, resistance to cyclic oxidation, thermal fatigue resistance, electrical resistivity and high temperature sag resistance, and comprising, in weight %, 4 to 9.5% Al, 0.5-2.0% Ti, 0.5-2% Mo, 0.1 to 0.8% Zr, 0.01-0.5% C, balance Fe.
Claim 2
Dependent Claim
60 words
An iron-based alloy useful as an electrical resistance heating element and having a disordered body centered cubic structure, the alloy having improved room temperature ductility, resistance to cyclic oxidation, thermal fatigue resistance, electrical resistivity and high temperature sag resistance, and comprising, in weight %, 4 to 9.5% Al, 0.5-2.0% Ti, 0.5-2% Mo, 0.1 to 0.8% Zr, 0.01-0.5% C, balance Fe.
Claim 3
Dependent Claim
11 words
The iron-based alloy of claim 1, wherein the alloy is Ni-free.
Claim 4
Dependent Claim
15 words
The iron-based alloy of claim 1, wherein the alloy has a microstructure which is austenite-free.
Claim 5
Dependent Claim
14 words
The iron-based alloy of claim 1, wherein the alloy has an entirely ferritic microstructure.
Claim 6
Dependent Claim
14 words
The iron-based alloy of claim 1, wherein the alloy is free of ceramic particles.
Claim 7
Dependent Claim
23 words
The iron-based alloy of claim 1, wherein the alloy includes ≦2% Si, ≦30% Ni, ≦0.5% Y, ≦0.1% B, ≦1% Nb and ≦1% Ta.
Claim 8
Dependent Claim
24 words
The iron-based alloy of claim 1, wherein the alloy consists essentially of 8.0-9.0% Al, 0.75-1.5% Ti, 0.75-1.5% Mo, 0.15-0.75% Zr, 0.05-0.35% C, balance Fe.
Claim 9
Dependent Claim
28 words
The iron-based alloy of claim 1, wherein the alloy consists essentially of 8.0-9.0% Al, 0.75-1.25% Ti, 0.75-1.25% Mo, 0.2 to 0.6% Zr, 0.03-0.09% C, 0.01-0.1% Y, balance Fe.
Claim 10
Dependent Claim
31 words
The iron-based alloy of claim 1, wherein the alloy consists essentially of 8.0-9.0% Al, 0.75-1.25% Ti, 0.75-1.25% Mo, 0.1-0.3% Zr, 0.01-0.1% C, 0.25-0.75% Nb, 0.25-0.75% Ta and 0.01-0.1% Y, balance Fe.
Claim 11
Dependent Claim
27 words
The iron-based alloy of claim 1, wherein the alloy consists essentially of 8.0-9.0% Al, 0.75-1.25% Ti, 0.75-1.25% Mo, 0.5-0.75% Zr, 0.05-0.15% C and 0.01-0.2% Si, balance Fe.
Claim 12
Dependent Claim
27 words
The iron-based alloy of claim 1, wherein the alloy consists essentially of 8.0-9.0% Al, 0.05-0.15% Si, 0.75-1.25% Ti, 0.75-1.25% Mo, 0.1-0.3% Zr and 0.2-0.4% C, balance Fe.
Claim 13
Dependent Claim
23 words
The iron-based alloy of claim 1, wherein the alloy comprises an electrical resistance heating element having a room temperature resistivity of 80-400 μΩ·cm.
Claim 14
Dependent Claim
17 words
The iron-based alloy of claim 1, wherein the alloy exhibits room temperature ductility of at least 3%.
Claim 15
Dependent Claim
35 words
The iron-based alloy of claim 1, wherein the alloy heats to 900° C. in less than 1 second when a voltage up to 10 volts and up to 6 amps is passed through the alloy.
Claim 16
Dependent Claim
27 words
The iron-based alloy of claim 1, wherein the alloy exhibits a weight gain of less than 4% when heated in air to 1000° C. for three hours.
Claim 17
Dependent Claim
26 words
The iron-based alloy of claim 1, wherein the alloy has a resistance of 0.05 to 7 ohms throughout a heating cycle between ambient and 900° C.
Claim 18
Dependent Claim
26 words
The iron-based alloy of claim 1, wherein the alloy has a resistivity of 80 to 200 Ω·cm throughout a heating cycle between ambient and 900° C.
Claim 19
Dependent Claim
20 words
The iron-based alloy of claim 1, wherein the alloy exhibits a room temperature reduction in area of at least 14%.
Claim 20
Dependent Claim
18 words
The iron-based alloy of claim 1, wherein the alloy exhibits a room temperature elongation of at least 15%.
Claim 21
Dependent Claim
20 words
The iron-based alloy of claim 1, wherein the alloy exhibits a room temperature yield strength of at least 50 ksi.
Claim 22
Dependent Claim
20 words
The iron-based alloy of claim 1, wherein the alloy exhibits a room temperature tensile strength of at least 80 ksi.
Claim 23
Dependent Claim
23 words
The iron-based alloy of claim 1, wherein the alloy exhibits a high temperature reduction in area at 800° C. of at least 30%.
Claim 24
Dependent Claim
21 words
The iron-based alloy of claim 1, wherein the alloy exhibits a high temperature elongation at 800° C. of at least 30%.
Claim 25
Dependent Claim
23 words
The iron-based alloy of claim 1, wherein the alloy exhibits a high temperature yield strength at 800° C. of at least 7 ksi.
Claim 26
Dependent Claim
23 words
The iron-based alloy of claim 1, wherein the alloy exhibits a high temperature tensile strength at 800° C. of at least 10 ksi.
Claim 27
Dependent Claim
37 words
The iron-based alloy of claim 1, wherein the alloy exhibits thermal fatigue resistance of over 10,000 cycles without breaking when heated from room temperature to 1000° C. for 0.5 to 5 seconds in each of the cycles.
Claim 28
Dependent Claim
11 words
The iron-based alloy of claim 1, wherein the alloy is Cr-free.
Claim 29
Dependent Claim
13 words
The iron-based alloy of claim 1, wherein the alloy is Mn-free and/or Si-free.
References Cited (Backward Citations)
US1550508A
Cited
US1990650A
Cited
US2300336A
Cited
US2768915A
Cited
US3026197A
Cited
US3676109A
Cited
US4391634A
Cited
US4961903A
Cited
US5032190A
Cited
US5173254A
Cited
US5084109A
Cited
US5158744A
Cited
EP0495123A1
Cited
EP0495121A1
Cited
US5320802A
Cited
US5238645A
Cited
US5439640A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-21 | 2000-07-22 | 2001-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-21 | 2004-07-22 | 2005-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-21 | 2008-07-22 | 2009-01-21 | $7700.00 | Window Closed / Lapsed |