Nanocrystalline layer thin film capacitors
Assignee: Research Foundation of the State University of New York
•
Filing: 1994-06-22
•
Granted: 1996-12-24
•
Expires: 2014-06-22
Abstract
Abstract The invention relates to a method for forming a high capacitance thin film capacitor comprising forming layers of dielectric material in amorphous, nanocrystalline and polycrystalline configuration and arranging the resulting layers between upper and lower electrodes. The invention further comprises dielectric articles such as capacitors formed in accordance with the method of the invention and includes their use in an electronic circuit.
Inventors
- 👤 Wayne A. Anderson
- 👤 Quanxi Jia
- 👤 Junsin Yi
- 👤 Lin-Huang Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:57
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/20; H10; H10D; H10D1/00; H10D1/60; H10D1/68; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
61 words
A method for preparing a dielectric article comprising forming a dielectric material into film layers arranged in opposing juxtaposition, a first layer comprising said dielectric material in amorphous configuration, a second film layer comprising said dielectric material in polycrystalline configuration and a third layer comprising said dielectric material in nanocrystalline configuration, and arranging said opposing layers between upper and lower electrodes.
Claim 2
Independent Claim
61 words
A method for preparing a dielectric article comprising forming a dielectric material into film layers arranged in opposing juxtaposition, a first layer comprising said dielectric material in amorphous configuration, a second film layer comprising said dielectric material in polycrystalline configuration and a third layer comprising said dielectric material in nanocrystalline configuration, and arranging said opposing layers between upper and lower electrodes.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein said dielectric article is arranged in a semiconductor substrate structure.
Claim 4
Dependent Claim
66 words
The method of claim 2 wherein a layer of said dielectric material is formed on said semiconductor substrate structure; another layer is formed on said layer formed on said semiconductor substrate structure; a further layer is formed on said another layer; an upper electrode is arranged in electrical communication with said further layer; and a lower electrode is arranged in electrical communication with said semiconductor substrate.
Claim 5
Dependent Claim
62 words
The method of claim 3 wherein said a layer is formed on at least one of said electrodes which is arranged in electrical communication with said semiconductor substrate structure; another layer is formed on said layer formed on said electrode; a further layer is formed on said another layer and an upper electrode is arranged in electrical communication with said further layer.
Claim 6
Dependent Claim
22 words
The method of claim 4 wherein said a layer is a nanocrystalline layer formed by crystallizing an amorphous layer on said electrode.
Claim 7
Dependent Claim
22 words
The method of claim 3 wherein said a layer is a nanocrystalline layer formed by crystallizing an amorphous layer on said substrate.
Claim 8
Dependent Claim
26 words
The method of claim 2 wherein said semiconductor substrate structure comprises a material selected from the group consisting of Si, SiC, GaAs, CdS, ZnO and ZnS.
Claim 9
Dependent Claim
26 words
The method of claim 1 wherein said polycrystalline layer of said dielectric material is formed on a surface of said nanocrystalline layer of said dielectric material.
Claim 10
Dependent Claim
26 words
The method of claim 1 wherein said amorphous layer of said dielectric material is formed on a surface of said polycrystalline layer of said dielectric material.
Claim 11
Dependent Claim
25 words
The method of claim 1 wherein said nanocrystalline layer of said dielectric material is formed through nanocrystallization of said amorphous layer of said dielectric material.
Claim 12
Dependent Claim
53 words
The method of claim 1 wherein said dielectric material is selected from the group consisting of BaTiO 3 , SrTiO 3 , KNO 3 , LiNbO 3 , Bi 4 Ti 3 O 12 , PbTiO 3 , PbZrO 3 , LaTiO 3 , PbMgO 3 , PbNbO 3 and LaZrO 3 .
Claim 13
Dependent Claim
17 words
The method of claim 11 wherein at least one film layer is formed by rf magnetron sputtering.
Claim 14
Dependent Claim
30 words
The method of claim 1 wherein at least one of said electrodes comprises a material selected from the group consisting of aluminum, copper, gold, silver, platinum, lead, ruthenium and palladium.
Claim 15
Dependent Claim
37 words
The method of claim 1 wherein at least one dielectric film layer is formed by a method selected from the group consisting of rf magnetron sputtering, vacuum evaporation, laser ablation, metal-organic chemical vapor deposition and E-beam evaporation.
Claim 16
Dependent Claim
23 words
The method of claim 14 wherein said polycrystalline film layer is formed at a temperature from about 540° Centigrade to about 1,000° Centigrade.
Claim 17
Dependent Claim
19 words
The method of claim 1 wherein said polycrystalline film layer is formed at a temperature above about 540° Centigrade.
Claim 18
Dependent Claim
19 words
The method of claim 1 wherein said amorphous film layer is formed at a temperature below about 350° Centigrade.
Claim 19
Dependent Claim
22 words
The method of claim 17 wherein said amorphous film is formed at a temperature from about room temperature to about 350° Centigrade.
Claim 20
Dependent Claim
19 words
The method of claim 1 wherein said nanocrystalline film layer is formed at a temperature above about 540° Centigrade.
Claim 21
Dependent Claim
23 words
The method of claim 19 wherein said nanocrystalline film layer is formed at a temperature from about 350° Centigrade to about 700° Centigrade.
Claim 22
Dependent Claim
23 words
The method of claim 1 wherein said polycrystalline film layer is formed to a thickness of from about 400 to about 10,000 angstroms.
Claim 23
Dependent Claim
23 words
The method of claim 21 wherein said polycrystalline film layer is formed to a thickness of from about 1,500 to about 3,500 angstroms.
Claim 24
Dependent Claim
23 words
The method of claim 1 wherein said amorphous film layer is formed to a thickness of from about 100 to about 2,000 angstroms.
Claim 25
Dependent Claim
23 words
The method of claim 23 wherein said amorphous film layer is formed to a thickness of from about 150 to about 600 angstroms.
Claim 26
Dependent Claim
21 words
The method of claim 1 wherein said nanocrystalline layer is formed by changing temperature conditions during deposition of said dielectric material.
Claim 27
Dependent Claim
41 words
The method of claim 25 wherein said polycrystalline layer is formed by deposition of a dielectric at a temperature above about 540° Centigrade and the temperature is lowered during deposition so as to deposit a nanocrystalline layer on the polycrystalline layer.
Claim 28
Dependent Claim
51 words
The method of claim 25 wherein said amorphous layer is formed by deposition of a dielectric at a temperature below about 400° Centigrade, the temperature is raised and the amorphous layer is crystallized so as to form a nanocrystalline layer, and a polycrystalline layer is thereafter deposited on the nanocrystalline layer.
Claim 29
Dependent Claim
17 words
The method of claim 1 comprising a further amorphous layer in opposing juxtaposition to said polycrystalline layer.
Claim 30
Dependent Claim
17 words
The method of claim 1 comprising a further nanocrystalline layer in opposing juxtaposition to said polycrystalline layer.
Claim 31
Dependent Claim
17 words
The method of claim 1 comprising a further polycrystalline layer in opposing juxtaposition to said nanocrystalline layer.
Claim 32
Dependent Claim
56 words
A high performance capacitor comprising film layers of a dielectric material arranged in opposing juxtaposition, one said layer comprising said dielectric in amorphous configuration, another of said layers comprising said dielectric material in nanocrystalline configuration and a further layer comprising said dielectric material in polycrystalline configuration, said opposing layers being arranged between upper and lower electrodes.
Claim 33
Dependent Claim
56 words
A high performance capacitor comprising film layers of a dielectric material arranged in opposing juxtaposition, one said layer comprising said dielectric in amorphous configuration, another of said layers comprising said dielectric material in nanocrystalline configuration and a further layer comprising said dielectric material in polycrystalline configuration, said opposing layers being arranged between upper and lower electrodes.
Claim 34
Dependent Claim
10 words
A capacitor of claim 31 comprising a semiconductor substrate structure.
Claim 35
Dependent Claim
50 words
A capacitor of claim 32 wherein a first layer engages a semiconductor substrate; another layer engages said first layer; a further layer engages said another layer; an upper electrode is arranged in communication with said further layer; and a lower electrode is arranged in electrical communication with said semiconductor substrate.
Claim 36
Dependent Claim
49 words
A capacitor of claim 32 wherein a first layer engages an electrode which is arranged in electrical communication with said semiconductor substrate structure; another layer engages said first layer; a further layer engages said another layer, and an upper electrode is arranged in electrical communication with said further layer.
Claim 37
Dependent Claim
26 words
A capacitor of claim 32 wherein said semiconductor substrate structure comprises a material selected from the group consisting of Si, SiC, GaAs, CdS, ZnO and ZnS.
Claim 38
Dependent Claim
53 words
A capacitor of claim 31 wherein said dielectric material is selected from the group consisting of BaTiO 3 , SrTiO 3 , KNO 3 , LiNbO 3 , Bi 4 Ti 3 O 12 , PbTiO 3 , PbZrO 3 , LaTiO 3 , PbMgO 3 , PbNbO 3 and LaZrO 3 .
Claim 39
Dependent Claim
28 words
A capacitor of claim 31 wherein at least one electrode comprises a material selected from the group consisting of aluminum, copper, gold, silver, platinum, lead, ruthenium and palladium.
Claim 40
Dependent Claim
37 words
A capacitor of claim 31 wherein at least one dielectric film layer is formed by a method selected from the group consisting of rf magnetron sputtering, vacuum evaporation, laser ablation, metal-organic chemical vapor deposition and E-beam evaporation.
Claim 41
Dependent Claim
18 words
A capacitor of claim 31 wherein said polycrystalline film is from about 400 to about 10,000 angstroms thick.
Claim 42
Dependent Claim
18 words
A capacitor of claim 31 wherein said amorphous film is from about 100 to about 2,000 angstroms thick.
Claim 43
Dependent Claim
18 words
A capacitor of claim 31 wherein said nanocrystalline film is from about 100 to about 2,000 angstroms thick.
Claim 44
Dependent Claim
21 words
A capacitor of claim 41 wherein said nanocrystalline layer is formed by nanocrystallization of an amorphous layer of the dielectric material.
Claim 45
Dependent Claim
17 words
A capacitor of claim 31 comprising a further amorphous layer in opposing juxtaposition to said polycrystalline layer.
References Cited (Backward Citations)
US4803591A
Cited
US4437139A
Cited
US4734340A
Cited
US4873610A
Cited
US4931897A
Cited
US5173835A
Cited
US5192871A
Cited
US5390072A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-12-24 | 2000-06-24 | 2000-12-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-12-24 | 2004-06-24 | 2004-12-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-12-24 | 2008-06-24 | 2008-12-24 | $7700.00 | Window Closed / Lapsed |