US5581876A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of adhering green tape to a metal support substrate with a bonding glass
Assignee: Sarnoff Corp
•
Filing: 1995-01-27
•
Granted: 1996-12-10
•
Expires: 2015-01-27
Abstract
Abstract In the manufacture of ceramic circuit boards having ceramic or metal support substrates, a bonding glass layer that is adherent both to the substrate material and to multilayer green tape compositions having circuitry printed thereon, is deposited and flowed onto the support substrate. The bonding glasses suitable for use with nickel plated metal substrates and green tape compositions containing forsterite-cordierite-type glasses are mixed oxides including calcium, zinc and boron as well as other oxides. These bonding glasses have a thermal coefficient of expansion that is larger than said metal substrate, and a flow temperature below that of said cordierite-type glasses.
Inventors
- 👤 Ashok N. Prabhu
- 👤 Barry J. Thaler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:16
CPC Classifications
C; C03; C03C; C03C8/00; C03C8/02; C03C8/04; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/05; H05K1/053; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C3/066; C03C3/068; C03C3/076; C03C3/097; C03C3/102; C03C3/108; H10; H10W; H10W40/00; H10W40/20; H10W40/25; H10W40/255; H10W70/00; H10W70/60; H10W70/67; H10W70/68; H10W70/6875; H10W99/00; H05K3/00; H05K3/0058; H10W90/00; H10W90/701; H10W90/751; H10W90/754; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49128; Y10T29/49155; Y10T29/49163; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/24926
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
141 words
A method of making a ceramic multilayer circuit board comprising a multilayer ceramic green tape stack made from forsterite-cordierite-type glasses having circuitry thereon and a ceramic or nickel plated metal support substrate comprising depositing a bonding glass on a surface of said support substrate, said bonding glass having a flow temperature and comprising an oxide mixture including calcium, zinc and boron oxides, patterning said bonding glass layer, aligning said coated support substrate with a multilayer green tape stack so that contact can be made between vias in said support substrate and the circuitry in said green tape stack, and firing the aligned coated substrate and green tape stack to a temperature above the flow temperature of the bonding glass so as to bond the resulting multilayer ceramic stack to said support substrate thereby limiting the shrinkage in the multilayer ceramic stack.
Claim 2
Independent Claim
141 words
A method of making a ceramic multilayer circuit board comprising a multilayer ceramic green tape stack made from forsterite-cordierite-type glasses having circuitry thereon and a ceramic or nickel plated metal support substrate comprising depositing a bonding glass on a surface of said support substrate, said bonding glass having a flow temperature and comprising an oxide mixture including calcium, zinc and boron oxides, patterning said bonding glass layer, aligning said coated support substrate with a multilayer green tape stack so that contact can be made between vias in said support substrate and the circuitry in said green tape stack, and firing the aligned coated substrate and green tape stack to a temperature above the flow temperature of the bonding glass so as to bond the resulting multilayer ceramic stack to said support substrate thereby limiting the shrinkage in the multilayer ceramic stack.
Claim 3
Dependent Claim
37 words
A method according to claim 1 wherein said support substrate having said bonding glass layer thereon is heated to a temperature above the flow temperature of the bonding glass prior to aligning with said green tape stack.
Claim 4
Dependent Claim
18 words
A method according to claim 1 wherein said support substrate is a nickel plated Kovar or Invar plate.
Claim 5
Dependent Claim
26 words
A method according to claim 1 wherein said support substrate is a nickel plated composite plate selected from the group consisting of Cu/Mo/Cu, Cu/Invar/Cu and Cu/Kovar/Cu.
Claim 6
Dependent Claim
18 words
A method according to claim 1 wherein said bonding glass is deposited on both surfaces of said substrate.
Claim 7
Dependent Claim
20 words
A method according to claim 5 wherein a green tape stack is aligned on both sides of said support substrate.
Claim 8
Dependent Claim
62 words
A method according to claim 1 wherein said bonding glass is a glass having the composition of from 20-45% by weight of barium oxide, from 5-15% by weight of calcium oxide, from 15-22% by weight of zinc oxide, from 15-25% by weight of silicon oxide, from 15-25% by weight of boron oxide and up to 2% by weight of additional metal oxides.
Claim 9
Dependent Claim
53 words
A method according to claim 7 wherein said bonding glass has the composition consisting essentially of 42.7% by weight of barium oxide, 6.25% by weight of calcium oxide, 13.6% by weight of zinc oxide, 16.7% by weight of silicon oxide, 19.5% by weight of boron oxide and minor amounts of additional metal oxides.
Claim 10
Dependent Claim
47 words
A method according to claim 7 wherein said bonding glass has the composition consisting essentially of 20.4% by weight of barium oxide, 14.9% by weight of calcium oxide, 21.6% by weight of zinc oxide, 25% by weight of silicon oxide, and 23.1% by weight of boron oxide.
Claim 11
Dependent Claim
22 words
A method according to claim 1 wherein up to about 30% by weight of bismuth oxide is added to said bonding glass.
Claim 12
Independent Claim
157 words
A method of making a ceramic multilayer circuit board comprising a multilayer ceramic green tape stack made from forsterite-cordierite-type glasses having circuitry thereon and a ceramic or nickel plated metal support substrate comprising depositing a bonding glass on a surface of said support substrate, said bonding glass having the composition of from 45-55% by weight of zinc oxide, from 30-40% by weight of boron oxide, from 3-7% by weight of calcium oxide and from 3-7% by weight of aluminum oxide, said bonding glass having a flow temperature, patterning said bonding glass layer, aligning said coated support substrate with a multilayer green tape stack so that contact can be made between vias in said support substrate and the circuitry in said green tape stack, and firing the aligned coated substrate and green tape stack to a temperature above the flow temperature of the bonding glass so as to bond the resulting multilayer ceramic structure to said support substrate.
Claim 13
Independent Claim
157 words
A method of making a ceramic multilayer circuit board comprising a multilayer ceramic green tape stack made from forsterite-cordierite-type glasses having circuitry thereon and a ceramic or nickel plated metal support substrate comprising depositing a bonding glass on a surface of said support substrate, said bonding glass having the composition of from 45-55% by weight of zinc oxide, from 30-40% by weight of boron oxide, from 3-7% by weight of calcium oxide and from 3-7% by weight of aluminum oxide, said bonding glass having a flow temperature, patterning said bonding glass layer, aligning said coated support substrate with a multilayer green tape stack so that contact can be made between vias in said support substrate and the circuitry in said green tape stack, and firing the aligned coated substrate and green tape stack to a temperature above the flow temperature of the bonding glass so as to bond the resulting multilayer ceramic structure to said support substrate.
Claim 14
Dependent Claim
41 words
A method according to claim 11 wherein said bonding glass has a composition consisting essentially of 50% by weight of zinc oxide, 39% by weight of boron oxide, 5% by weight of calcium oxide and 6% by weight of aluminum oxide.
References Cited (Backward Citations)
US4712161A
Cited
US4997698A
Cited
US4808460A
Cited
US5044074A
Cited
US5043222A
Cited
US5013360A
Cited
US5256469A
Cited
US5277724A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-12-10 | 2000-06-10 | 2000-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-12-10 | 2004-06-10 | 2004-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-12-10 | 2008-06-10 | 2008-12-10 | $7700.00 | Window Closed / Lapsed |