Rapid process for producing a chalcopyrite semiconductor on a substrate
Assignee: Saint Gobain Glass France SAS
•
Filing: 1993-09-07
•
Granted: 1996-11-26
•
Expires: 2013-09-07
Abstract
Abstract To produce a polycrystalline, single-phase compound semiconductor layer of the chalcopyrite type ABC 2 , it is proposed to deposit, on a substrate, a layer structure which comprises a plurality of layers and which contains the components in elemental form, as an interelemental compound or as an alloy, the component C being present in stoichiometric excess. In a rapid annealing process with a heating rate of at least 10° C./s to a processing temperature of at least 350° C., the layer structure is converted into the compound semiconductor ABC 2 even after a few seconds, the gas exchange being limited by encapsulation of the layer structure, with the result that an evaporation of the most volatile components is prevented. Highly efficient solar cells can be produced from the semiconductor.
Inventors
- 👤 Franz Karg
- 👤 Volker Probst
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:42
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/10; H10F77/12; H10F77/126; H10F10/00; H10F10/10; H10F10/16; H10F10/167; H10F71/00; H10F71/128; H10P; H10P14/00; H10P14/20; H10P14/203; H10P14/29; H10P14/2901; H10P14/2922; H10P14/32; H10P14/3202; H10P14/3241; H10P14/34; H10P14/3402; H10P14/3436; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/541; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S438/00; Y10S438/971
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
191 words
A process for producing a chalcopyrite semiconductor of the type ABC 2 , where A is copper, B is indium or gallium, and C is sulfur or selenium, on a substrate, comprising the steps of: producing a layer structure on the substrate by applying the components A, B, and C in elemental form and/or as a binary interelemental compound B 2 C 3 , the component C being present in an excess which forms up to twice a stoichiometrically exact proportion of component; rapidly heating the substrate with the layer structure to a processing temperature, which is greater than or equal to 350° C., at a heating rate of at least 10° C./s; and keeping the substrate at the processing temperature for a time interval dt in the range of 10 seconds to 1 hour to perform annealing; providing an encapsulation as a covering above the layer structure at a spacing of less than 5 mm, which encapsulation maintains, throughout the entire annealing process, a partial pressure for the component C which is above the partial pressure of the component C which would develop above a stoichiometrically exact ABC 2 semiconductor.
Claim 2
Dependent Claim
191 words
A process for producing a chalcopyrite semiconductor of the type ABC 2 , where A is copper, B is indium or gallium, and C is sulfur or selenium, on a substrate, comprising the steps of: producing a layer structure on the substrate by applying the components A, B, and C in elemental form and/or as a binary interelemental compound B 2 C 3 , the component C being present in an excess which forms up to twice a stoichiometrically exact proportion of component; rapidly heating the substrate with the layer structure to a processing temperature, which is greater than or equal to 350° C., at a heating rate of at least 10° C./s; and keeping the substrate at the processing temperature for a time interval dt in the range of 10 seconds to 1 hour to perform annealing; providing an encapsulation as a covering above the layer structure at a spacing of less than 5 mm, which encapsulation maintains, throughout the entire annealing process, a partial pressure for the component C which is above the partial pressure of the component C which would develop above a stoichiometrically exact ABC 2 semiconductor.
Claim 3
Dependent Claim
25 words
The process as claimed in claim 1, wherein the substrate with the layer structure is kept in a closed container for the purpose of encapsulation.
Claim 4
Dependent Claim
25 words
The process as claimed in claim 2, wherein the closed container is a graphite container and the heating is carried out with a heating lamp.
Claim 5
Dependent Claim
24 words
The process as claimed in claim 1, wherein the component A is applied in elemental form as a first layer of the layer structure.
Claim 6
Dependent Claim
26 words
The process as claimed in claim 1, wherein the heating rate is high enough for the processing temperature to be reached in less than 10 seconds.
Claim 7
Dependent Claim
16 words
The process as claimed in claim 1, wherein the processing temperature is at least 500° C.
Claim 8
Dependent Claim
25 words
The process as claimed in claim 1, wherein the annealing is carried out at a total gas pressure of between 1 hpa and 1000 hpa.
Claim 9
Dependent Claim
46 words
The process as claimed in claim 1, wherein the components A, B, and C are deposited in a molar ratio of 1:m:2n for the layer structure, where m is in the range of 0.9 to 1.3 and n is in the range of 1.0 to 1.8.
Claim 10
Dependent Claim
44 words
The process as claimed in claim 1, wherein the components A and B are applied to the substrate in an amount of at least approximately 2 μmol/cm 2 and the component C is applied in an amount of at least 4.8 μmol/cm 2 .
Claim 11
Dependent Claim
41 words
The process as claimed in claim 1, wherein at least one of the components B and C is replaced by an element of a corresponding main group of the periodic system in proportions of 0 percent to 25 percent (atomic percent).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-11-26 | 2000-05-27 | 2000-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-11-26 | 2004-05-27 | 2004-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-11-26 | 2008-05-27 | 2008-11-26 | $7700.00 | Window Closed / Lapsed |