Method for improving wear resistance of polymeric bioimplantable components
Assignee: Johnson and Johnson Professional Inc
•
Filing: 1995-04-03
•
Granted: 1996-11-26
•
Expires: 2015-04-03
Abstract
Abstract Wear resistance and oxidation resistance of bioimplantable polymeric parts is improved by packaging the parts within flexible, gas impermeable containers while subjecting the containers and the parts to a relatively high vacuum force. The containers are heat sealed while subjected to the vacuum force such that, upon sealing, hydrostatic pressure is exerted on the part. Following sealing of the packages, the packages and their contents are irradiated to an extent sufficient to sterilize the parts and to promote crosslinking within the part. Alternatively, the same property enhancements can be imparted to polymeric parts by packaging the part within rigid or flexible containers, minimizing the oxygen content within the containers, pressurizing the containers with an inert gas, or with a mixture of hydrogen and an inert gas, to greater than 1.5 atmospheres, and irradiating the part and the container.
Inventors
- 👤 John V. Hamilton
- 👤 Mark A. Manasas
- 👤 Timothy M. Flynn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:33
CPC Classifications
A; A61; A61L; A61L2/00; A61L2/02; A61L2/08; A61L2/081; A61L2/082; A61L2/087; A61L27/00; A61L27/14; A61L27/16; B; B65; B65B; B65B55/00; B65B55/02; B65B55/04; B65B55/08; B65B55/12; B65B55/16; C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; A61L2103/00; A61L2103/15; B65B31/00; B65B31/04; C08L2207/00; C08L2207/06; C08L2207/068
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
126 words
A method for improving the wear resistance of a polymeric manufactured part, comprising the steps of: providing one or more manufactured polymeric parts; placing the parts in one or more gas impermeable, flexible packaging containers wherein each container has at least one heat sealable opening therein; subjecting the packaging container and the polymeric parts to a vacuum force; heat sealing the flexible packaging container while subjected to the vacuum force such that upon sealing of the packaging container hydrostatic pressure is exerted on the part; and irradiating the heat sealed packages and the parts for a period of time sufficient to sterilize the parts and to promote crosslinking within the polymer that forms the part; the part being characterized by improved resistance to wear and oxidation.
Claim 2
Independent Claim
126 words
A method for improving the wear resistance of a polymeric manufactured part, comprising the steps of: providing one or more manufactured polymeric parts; placing the parts in one or more gas impermeable, flexible packaging containers wherein each container has at least one heat sealable opening therein; subjecting the packaging container and the polymeric parts to a vacuum force; heat sealing the flexible packaging container while subjected to the vacuum force such that upon sealing of the packaging container hydrostatic pressure is exerted on the part; and irradiating the heat sealed packages and the parts for a period of time sufficient to sterilize the parts and to promote crosslinking within the polymer that forms the part; the part being characterized by improved resistance to wear and oxidation.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein the vacuum force is sufficient to remove all or substantially all of the oxygen from within the packaging container and the environment adjacent to the packaging container.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the vacuum force is in the range of about 500-1013 mbar.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein the hydrostatic pressure executed on the part is in the range of about 7 to 14.7 psi.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein any gas contained within the flexible packaging container is characterized by a reduced number of moles of hydrogen.
Claim 7
Dependent Claim
22 words
The method of claim 5 wherein the gas within the flexible packaging container has less than about 2.2×10 -5 moles/g of hydrogen.
Claim 8
Dependent Claim
20 words
The method of claim 1 wherein the step of irradiating is carried out using gamma, x-ray, or election beam radiation.
Claim 9
Dependent Claim
23 words
The method of claim 7 wherein the step of irradiating is carried out until a dose of about 20-60 KGy has been achieved.
Claim 10
Dependent Claim
35 words
The method of claim 1 wherein, following the step of irradiating, the part is characterized by a gel content in the range of about 75 to 100% as determined by Method C of ASTM D2765-90.
Claim 11
Dependent Claim
28 words
The method of claim 1 wherein the flexible packaging container is manufactured of a metal foil that is surrounded by one or more layers of a polymer film.
Claim 12
Dependent Claim
36 words
The method of claim 1 wherein the polymeric part is made from a polymer selected from the group consisting of low density polyethylene, high density polyethylene, ultrahigh molecular weight polyethylene, polypropylene, polyester, nylon, polyurethane, and poly(methylmethacrylate).
Claim 13
Dependent Claim
28 words
The method of claim 1 wherein the polymeric part is made from an ultrahigh molecular weight polyethylene having a number average molecular weight greater than about 1.0 million.
Claim 14
Dependent Claim
16 words
The method of claim 12 wherein the polymeric part is manufactured by a compression molding process.
Claim 15
Dependent Claim
16 words
The method of claim 12 wherein the polymeric part is manufactured by a RAM extrusion process.
Claim 16
Dependent Claim
49 words
The method of claim 1 wherein, following the step of irradiating, the method further comprises the step of aging the polymeric parts within a hydrogen enriched atmosphere of the packaging container for a period of time sufficient to enable hydrogen atoms to recombine with free radicals within the polymer.
Claim 17
Independent Claim
21 words
The method of claims 15 wherein the hydrogen rich atmosphere within the container has approximately 30% to 100% hydrogen by volume.
Claim 18
Dependent Claim
16 words
The method of claim 15 wherein the polymeric parts are aged for at least 48 hours.
Claim 19
Independent Claim
106 words
A method for improving the wear resistance of a polymeric manufactured part, comprising the steps of: providing one or more manufactured polymeric parts; placing the parts in one or more sealable, gas impermeable packaging containers; removing all or substantially all of the oxygen from within the packaging container; pressurizing the packaging containers with an inert gas at a pressure greater than about 1.5 to 4.0 atmospheres; irradiating the pressurized containers and the polymeric parts for a period of time sufficient to sterilize the parts and to promote crosslinking within the polymer that forms the part; the part being characterized by improved resistance to wear and oxidation.
Claim 20
Independent Claim
106 words
A method for improving the wear resistance of a polymeric manufactured part, comprising the steps of: providing one or more manufactured polymeric parts; placing the parts in one or more sealable, gas impermeable packaging containers; removing all or substantially all of the oxygen from within the packaging container; pressurizing the packaging containers with an inert gas at a pressure greater than about 1.5 to 4.0 atmospheres; irradiating the pressurized containers and the polymeric parts for a period of time sufficient to sterilize the parts and to promote crosslinking within the polymer that forms the part; the part being characterized by improved resistance to wear and oxidation.
Claim 21
Dependent Claim
27 words
The method of claim 18 wherein the step of minimizing the oxygen concentration within the packaging container is effected by flushing the container with an inert gas.
Claim 22
Dependent Claim
26 words
The method of claim 18 wherein the step of minimizing the oxygen concentration within packaging containers is effected by applying a vacuum force to the container.
Claim 23
Dependent Claim
20 words
The method of claim 18 wherein the inert gas is selected from the group consisting of argon, helium, and nitrogen.
Claim 24
Dependent Claim
11 words
The method of claim 18 wherein the packaging container is rigid.
Claim 25
Dependent Claim
11 words
The method of claim 18 wherein the packaging container is flexible.
Claim 26
Dependent Claim
20 words
The method of claim 18 wherein the step of irradiating is carried out using gamma, x-ray, or electron beam radiation.
Claim 27
Dependent Claim
23 words
The method of claim 24 wherein the step of irradiating is carried out until a dose of about 20-60 KGy has been achieved.
Claim 28
Independent Claim
138 words
A method for improving the wear resistance of a polymeric manufactured part, comprising the steps of: providing one or more manufactured polymeric parts; placing the parts in one or more sealable, gas impermeable packaging containers; removing all or substantially all of the oxygen from within the packaging container; pressurizing the packaging containers with a mixture of hydrogen gas and an inert gas at a pressure greater than about 1.5 atmospheres; irradiating the pressurized containers and the polymeric parts for a period of time sufficient to sterilize the parts and to promote crosslinking within the polymer that forms the part; aging the part within the atmosphere of the irradiated packaging container for a period of time sufficient for hydrogen atoms to recombine with free radicals within the part; the part being characterized by improved resistance to wear and oxidation.
Claim 29
Independent Claim
138 words
A method for improving the wear resistance of a polymeric manufactured part, comprising the steps of: providing one or more manufactured polymeric parts; placing the parts in one or more sealable, gas impermeable packaging containers; removing all or substantially all of the oxygen from within the packaging container; pressurizing the packaging containers with a mixture of hydrogen gas and an inert gas at a pressure greater than about 1.5 atmospheres; irradiating the pressurized containers and the polymeric parts for a period of time sufficient to sterilize the parts and to promote crosslinking within the polymer that forms the part; aging the part within the atmosphere of the irradiated packaging container for a period of time sufficient for hydrogen atoms to recombine with free radicals within the part; the part being characterized by improved resistance to wear and oxidation.
Claim 30
Dependent Claim
54 words
The method of claim 26 wherein the mixture of hydrogen gas and an inert gas is characterized by a minimum of about 2.2×10 -3 moles of hydrogen gas per gram of polymeric material within the packaging container and a volumetric concentration of hydrogen within the container in the range of about 30% to 95%.
Claim 31
Dependent Claim
20 words
The method of claim 26 wherein the part is aged within the packaging container for at least about 48 hours.
Claim 32
Dependent Claim
27 words
The method of claim 26 wherein the step of minimizing the oxygen concentration within the packaging container is effected by flushing the container with an inert gas.
Claim 33
Dependent Claim
26 words
The method of claim 26 wherein the step of minimizing the oxygen concentration within packaging containers is effected by applying a vacuum force to the container.
Claim 34
Dependent Claim
20 words
The method of claim 26 wherein the inert gas is selected from the group consisting of argon, helium, and nitrogen.
Claim 35
Dependent Claim
11 words
The method of claim 26 wherein the packaging container is rigid.
Claim 36
Dependent Claim
11 words
The method of claim 26 wherein the packaging container is flexible.
Claim 37
Dependent Claim
20 words
The method of claim 26 wherein the step of irradiating is carried out using gamma, x-ray, or electron beam radiation.
Claim 38
Dependent Claim
23 words
The method of claim 34 wherein the step of irradiating is carried out until a dose of about 20-60 KGy has been achieved.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-11-26 | 2000-05-27 | 2000-11-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-11-26 | 2004-05-27 | 2004-11-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-11-26 | 2008-05-27 | 2008-11-26 | $7700.00 | Window Closed / Lapsed |