Abstract
Abstract The present invention provides a method of manufacturing a T-shaped capacitor for a DRAM which uses one mask to define both the node contact hole and the bottom electrode. This novel one mask method uses an oxygen plasma treatment to enlarge a first opening (the node contact opening) in the resist layer to create a slightly larger second opening which defines the storage electrode. This method reduces the number of masking steps used and therefore reduces process costs and increases yields. The process comprises forming an insulation layer and a resist layer having a first opening over an active area. Next, the insulation layer is etched through the first opening forming a node contact hole extending partially through the insulation layer. The first opening is widened with an oxygen plasma etch to form a slightly larger second opening. Then, the insulation layer is etched through the second opening forming a storage electrode hole and the node contact hole is extended to expose the source. The resist layer is removed. A polysilicon layer is formed that completely fills the node contact hole and the storage electrode hole and covers the first insulation layer. The polysilicon layer covering the first insulation layer is removed thereby forming the T-shaped storage electrode. The first insulation layer is removed. A capacitor dielectric layer and a top electrode are formed over the T-shaped storage electrode thus completing the T-shaped capacitor.
Inventors
- 👤 Horng-Huei Tseng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:29
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/30; H10B12/31; H10B12/318
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
320 words
A method of fabricating a memory cell having a gate electrode formed on a substrate disposed between a source and a drain, comprising the sequential processes of: forming a barrier layer over a substrate surface and said gate electrode; forming a first insulation layer over first barrier layer; forming a resist layer over said first insulation layer, said resist layer having a first opening over said source; etching a first hole defined by said first opening said first insulation layer, said first hole extends partially through said first insulation layer, said first hole having a depth less than a thickness of said first insulation layer; laterally etching said resist layer with an oxygen plasma thereby enlarging said first opening in said resist layer to form a second opening over said source, said second opening being concentric with said first hole and having a larger area than said first hole; anisotropically etching said first insulation layer and said barrier layer using said etched resist layer as a mask and extending said first hole through said first insulation layer to expose said source, and etching said first insulation layer through said second opening thereby forming a second hole into said first insulation layer to a depth less than the thickness of said first insulation layer, said second hole being defined by sidewalls of said first insulation layer; removing said resist layer; forming a first polysilicon layer completely filling said extended first hole and said second hole and covering a top surface of said first insulation layer; etching back solid first polysilicon layer removing said first polysilicon layer covering the top surface of said first insulation layer, and removing said first insolation layer using said barrier layer as an etch stop thereby forming a T-shaped storage electrode; forming a dielectric layer and a top electrode over said storage electrode, and forming a top insulation layer over said substrate thereby completing said memory cell.
Claim 2
Independent Claim
320 words
A method of fabricating a memory cell having a gate electrode formed on a substrate disposed between a source and a drain, comprising the sequential processes of: forming a barrier layer over a substrate surface and said gate electrode; forming a first insulation layer over first barrier layer; forming a resist layer over said first insulation layer, said resist layer having a first opening over said source; etching a first hole defined by said first opening said first insulation layer, said first hole extends partially through said first insulation layer, said first hole having a depth less than a thickness of said first insulation layer; laterally etching said resist layer with an oxygen plasma thereby enlarging said first opening in said resist layer to form a second opening over said source, said second opening being concentric with said first hole and having a larger area than said first hole; anisotropically etching said first insulation layer and said barrier layer using said etched resist layer as a mask and extending said first hole through said first insulation layer to expose said source, and etching said first insulation layer through said second opening thereby forming a second hole into said first insulation layer to a depth less than the thickness of said first insulation layer, said second hole being defined by sidewalls of said first insulation layer; removing said resist layer; forming a first polysilicon layer completely filling said extended first hole and said second hole and covering a top surface of said first insulation layer; etching back solid first polysilicon layer removing said first polysilicon layer covering the top surface of said first insulation layer, and removing said first insolation layer using said barrier layer as an etch stop thereby forming a T-shaped storage electrode; forming a dielectric layer and a top electrode over said storage electrode, and forming a top insulation layer over said substrate thereby completing said memory cell.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein said barrier layer is formed of silicon nitride having a thickness in a range of between about 500 and 2000 Å.
Claim 4
Dependent Claim
28 words
The method of claim 1 wherein first insulation layer is composed of silicon oxide and has a thickness in a range of between about 5000 and 10,000 Å.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said first opening has an open dimension in range of between about 0.1 and 0.5 μm.
Claim 6
Dependent Claim
30 words
The method of claim 1 wherein said first hole that extends partially through said first insulation layer has a depth in a range of between about 3000 and 5000 Å.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said second opening has an open dimension in a range of between about 0.2 and 0.7 μm.
Claim 8
Dependent Claim
22 words
The method of claim 1 wherein said second hole has a depth in a range of between about 2500 and 5000 Å.
Claim 9
Dependent Claim
48 words
The method of claim 1 wherein said first polysilicon layer is formed of polycrystalline silicon being doped with conductive impurities with an impurity concentrations in range of between about 1E20 and 1E22 atoms/cm 3 and has a thickness in a range of between about 1500 and 4000 Å.
Claim 10
Dependent Claim
46 words
The method of claim 1 wherein said dielectric layer is formed of a layer of silicon oxide, a layer of silicon nitride, and a layer of silicon oxide (ONO) and said dielectric layer has a total thickness in a range between about 20 and 100 Å.
Claim 11
Dependent Claim
37 words
The method of claim 1 wherein said top electrode has a thickness in the range between about 1000 and 2000 Å and a dopant concentration in a range of between about 1E20 and 1E22 atoms/cm 3 .
Claim 12
Independent Claim
307 words
A method of manufacturing a T-shaped capacitor over a node in a substrate, comprising the steps of: forming a first insulation layer over a substrate surface; forming a resist layer over said first insulation layer, said resist layer having a first opening over said node; etching said first insulation layer through said first opening forming a node contact hole defined by said first opening in said first insulation layer, said node contact hole extending partially through said first insulation layer, said node contact hole having a depth less than a thickness of said first insulation layer; laterally etching said resist layer with an oxygen plasma thereby widening said first opening in said resist layer to form a second opening over said node, said second opening being concentric with said not contact hole and having a larger area than said node contact hole; anisotropically etching said first insulation layer using said etched resist layer as a mask and extending said node contact hole through said first insulation layer to expose said node, and etching said first insulation layer through said second opening thereby forming a storage electrode hole into said first insulation layer to a depth less than the thickness of said first insulation layer, said storage electrode hole being defined by sidewalls of said first insulation layer; removing said resist layer; forming a first polysilicon layer completely filling said extended node contact hole and said storage electrode hole and covering a top surface of said first insulation layer; etching back said first polysilicon layer on the top surface of said first insulation layer thereby exposing said first insulation layer; selectively etching said first insulation layer thereby forming a T-shaped storage electrode from remaining portions of said first polysilicon layer; and forming a dielectric layer and a top electrode over said storage electrode thereby completing said T-shaped capacitor.
Claim 13
Independent Claim
307 words
A method of manufacturing a T-shaped capacitor over a node in a substrate, comprising the steps of: forming a first insulation layer over a substrate surface; forming a resist layer over said first insulation layer, said resist layer having a first opening over said node; etching said first insulation layer through said first opening forming a node contact hole defined by said first opening in said first insulation layer, said node contact hole extending partially through said first insulation layer, said node contact hole having a depth less than a thickness of said first insulation layer; laterally etching said resist layer with an oxygen plasma thereby widening said first opening in said resist layer to form a second opening over said node, said second opening being concentric with said not contact hole and having a larger area than said node contact hole; anisotropically etching said first insulation layer using said etched resist layer as a mask and extending said node contact hole through said first insulation layer to expose said node, and etching said first insulation layer through said second opening thereby forming a storage electrode hole into said first insulation layer to a depth less than the thickness of said first insulation layer, said storage electrode hole being defined by sidewalls of said first insulation layer; removing said resist layer; forming a first polysilicon layer completely filling said extended node contact hole and said storage electrode hole and covering a top surface of said first insulation layer; etching back said first polysilicon layer on the top surface of said first insulation layer thereby exposing said first insulation layer; selectively etching said first insulation layer thereby forming a T-shaped storage electrode from remaining portions of said first polysilicon layer; and forming a dielectric layer and a top electrode over said storage electrode thereby completing said T-shaped capacitor.
Claim 14
Dependent Claim
31 words
The method of claim 11 wherein said substrate further includes spaced gate electrodes surrounding said node, and a barrier layer over said substrate surface, said barrier layer formed of silicon nitride.
Claim 15
Dependent Claim
28 words
The method of claim 11 wherein first insulation layer is composed of silicon oxide and has a thickness in a range of between about 5000 and 10,000 Å.
Claim 16
Dependent Claim
23 words
The method of claim 11 wherein said first opening has an open dimension in a range of between about 0.1 and 0.5 μm.
Claim 17
Dependent Claim
30 words
The method of claim 11 wherein said node contract hole that extends partially through said first insulation layer has a depth in range of between about 3000 and 5000 Å.
Claim 18
Dependent Claim
22 words
The method of claim 11 wherein said second opening has an open dimension in range of between about 0.2 and 0.7 μm.
Claim 19
Dependent Claim
23 words
The method of claim 11 wherein said storage electrode hole has a depth in a range of between about 2500 and 5000 Å.
Claim 20
Dependent Claim
48 words
The method of claim 11 wherein said first polysilicon layer is formed of polycrystalline silicon being doped with conducive impurities with an impurity concentrations in a range of between about 1E20 and 1E22 atoms/cm 3 and has a thickness in range of between about 1500 and 4000 Å.
Claim 21
Dependent Claim
47 words
The method of claim 11 when in said dielectric layer is formed of a layer of silicon oxide, a layer of silicon nitride, and a layer of silicon oxide (ONO), and said dielectric layer has a total thickness in a range between about 20 and 100 Å.
Claim 22
Dependent Claim
37 words
The method of claim 11 wherein said top electrode has a thickness in a range between about 1000 and 2000 Å and a dopant concentration in a range of between about 1E20 and 1E22 atoms/cm 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-22 | 2000-04-22 | 2000-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-22 | 2004-04-22 | 2004-10-22 | $3760.00 | Window Closed / Lapsed |