Method for doping strained heterojunction semiconductor devices and structure
Assignee: NXP USA Inc
•
Filing: 1995-02-02
•
Granted: 1996-10-15
•
Expires: 2015-02-02
Abstract
Abstract A method for doping a strained heterojunction semiconductor device includes heating a substrate (16) having a strained mono-crystalline semiconductor region (22) to a temperature above room temperature. While the substrate (16) is heated, dopants are ion implanted into the strained mono-crystalline semiconductor region (22) to minimize implant related damage. Thereafter the substrate (16) is heated under non-steady state conditions for a time sufficient to activate the implanted dopant and anneal implant related damage while minimizing relaxation of the strained heterojunction.
Inventors
- 👤 N. David Theodore
- 👤 Donald Y. C. Lie
- 👤 T. C. Smith
- 👤 John W. Steele
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:14
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/21; H10D; H10D10/00; H10D10/01; H10D10/021; H10D62/00; H10D62/80; H10D62/83; H10D62/834; H10P30/202; H10P30/204; H10P30/224; H10P30/28; Y; Y10; Y10S; Y10S438/00; Y10S438/938
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
121 words
A method for doping strained heterojunction semiconductor devices comprising the steps of: exposing a substrate to a first temperature above room temperature, the substrate including a first layer and a strained mono-crystalline semiconductor layer formed on the first layer, wherein the strained mono-crystalline semiconductor layer forms a strained heterojunction with the first layer; implanting a dopant into the strained mono-crystalline semiconductor layer while the substrate is exposed to the first temperature; and thereafter exposing the substrate to a second temperature to activate the dopant and to anneal implant damage, wherein the substrate is exposed to the second temperature for a time sufficient to activate the dopant and to anneal the implant damage while maintaining the strained heterojunction in a strained condition.
Claim 2
Independent Claim
121 words
A method for doping strained heterojunction semiconductor devices comprising the steps of: exposing a substrate to a first temperature above room temperature, the substrate including a first layer and a strained mono-crystalline semiconductor layer formed on the first layer, wherein the strained mono-crystalline semiconductor layer forms a strained heterojunction with the first layer; implanting a dopant into the strained mono-crystalline semiconductor layer while the substrate is exposed to the first temperature; and thereafter exposing the substrate to a second temperature to activate the dopant and to anneal implant damage, wherein the substrate is exposed to the second temperature for a time sufficient to activate the dopant and to anneal the implant damage while maintaining the strained heterojunction in a strained condition.
Claim 3
Dependent Claim
90 words
The method of claim 1 wherein the step of exposing the substrate to the first temperature includes exposing a substrate having a silicon layer and a IV-IV mono-crystalline semiconductor alloy layer formed on the silicon layer, wherein the IV-IV mono-crystalline semiconductor alloy layer is formed on the silicon layer at a third temperature, and wherein the step of exposing the substrate to the second temperature includes exposing the substrate to a second temperature that is less than 400° C. above the third temperature for a time less than 500 seconds.
Claim 4
Dependent Claim
90 words
The method of claim 1 wherein the step of exposing the substrate to the first temperature includes exposing a substrate having a silicon layer and a Si 1-x Ge x layer formed on the silicon layer, wherein the Si 1-x Ge x layer is formed on the silicon layer at a third temperature, and wherein the step of exposing the substrate to the second temperature includes exposing the substrate to a second temperature that is less than 400° C. above the third temperature for a time less than 500 seconds.
Claim 5
Dependent Claim
90 words
The method of claim 3 wherein the step of exposing the substrate to the first temperature includes exposing a substrate having a silicon layer and a Si 1-x Ge x layer formed on the silicon layer, wherein the Si 1-x Ge x layer is formed on the silicon layer at a third temperature, and wherein the step of exposing the substrate to the second temperature includes exposing the substrate to a second temperature that is less than 300° C. above the third temperature for a time less than 60 seconds.
Claim 6
Dependent Claim
119 words
The method of claim 1 wherein the step of exposing the substrate to the first temperature includes exposing a substrate having an n-type silicon layer and a p-type Si 1-x Ge x layer formed on the n-type silicon layer, the n-type silicon layer forming a collector region, and the p-type Si 1-x Ge x layer forming a base region, and wherein the step of implanting the dopant includes selectively implanting an n-type dopant into the p-type Si 1-x Ge x layer to form a collector contact region, and wherein the method further includes the step of forming an n-type polycrystalline semiconductor layer on the p-type Si 1-x Ge x layer, the n-type polycrystalline semiconductor layer forming an emitter region.
Claim 7
Dependent Claim
16 words
The method of claim 1 wherein the step of implanting the dopant includes ion implanting phosphorous.
Claim 8
Dependent Claim
33 words
The method of claim 6 wherein the step of exposing the substrate to the first temperature includes exposing the substrate to a temperature in a range from approximately 40° C. to 300° C.
Claim 9
Dependent Claim
105 words
A process for doping a IV-IV strained heterojunction semiconductor device including the steps of: placing a semiconductor substrate into a ion implanter, the semiconductor substrate including a strained heterojunction structure, heating the semiconductor substrate to a first temperature in a range from approximately 40° C. to 300° C.; implanting a dopant into the strained heterojunction structure to form an implanted region while the semiconductor substrate is exposed to the first temperature to minimize implantation damage effects; and annealing the semiconductor substrate at a second temperature for a time to activate the dopant and to anneal implant damage while minimizing relaxation of the strained heterojunction structure.
Claim 10
Dependent Claim
105 words
A process for doping a IV-IV strained heterojunction semiconductor device including the steps of: placing a semiconductor substrate into a ion implanter, the semiconductor substrate including a strained heterojunction structure, heating the semiconductor substrate to a first temperature in a range from approximately 40° C. to 300° C.; implanting a dopant into the strained heterojunction structure to form an implanted region while the semiconductor substrate is exposed to the first temperature to minimize implantation damage effects; and annealing the semiconductor substrate at a second temperature for a time to activate the dopant and to anneal implant damage while minimizing relaxation of the strained heterojunction structure.
Claim 11
Dependent Claim
53 words
The process according to claim 8 wherein the step of placing the semiconductor substrate into the ion implanter includes placing a substrate comprising a silicon layer and a Si 1-x Ge x layer formed on the silicon layer, wherein the Si 1-x Ge x layer forms a strained heterojunction with the silicon layer.
Claim 12
Dependent Claim
117 words
The process according to claim 9 wherein the step of placing the semiconductor substrate into the ion implanter includes placing a substrate comprising an n-type silicon layer and a p-type Si 1-x Ge x layer over the n-type silicon layer, the n-type silicon layer forming a collector region and the p-type Si 1-x Ge x layer forming a base region, and wherein the step of implanting the dopant includes selectively implanting phosphorous into the Si 1-x Ge x layer to form a collector contact region, and wherein the process further comprises the step of forming an n-type polysilicon layer over a portion of the Si 1-x Ge x layer, the n-type polysilicon layer forming an emitter region.
Claim 13
Dependent Claim
63 words
The process according to claim 10 wherein the step of heating the semiconductor substrate to the first temperature includes exposing the semiconductor substrate to a temperature in a range from approximately 60° C. to 100° C., and wherein the step of implanting phosphorous includes implanting phosphorous at an implant dosage in a range from approximately 8.0×10 13 to 2.0×10 14 ions/cm 2 .
Claim 14
Dependent Claim
44 words
The process according to claim 10 wherein the step of annealing the semiconductor substrate includes annealing the semiconductor substrate in an RTA system at a temperature in a range from 650° C. to 850° C. for less than 60 seconds in a non-reactive ambient.
Claim 15
Dependent Claim
26 words
The process according to claim 8 further comprising the step of forming a screen oxide on the semiconductor substrate before the step of implanting the dopant.
Claim 16
Dependent Claim
36 words
The process according to claim 8 wherein the step of placing the semiconductor substrate into the ion implanter includes placing a semiconductor substrate comprising a silicon layer and a carbon-doped silicon layer over the silicon layer.
Claim 17
Dependent Claim
37 words
The process according to claim 8 wherein the step of placing the semiconductor substrate into the ion implanter includes placing a semiconductor substrate comprising a silicon layer and a germanium/carbon doped silicon layer over the silicon layer.
Claim 18
Dependent Claim
130 words
A strained heterojunction bipolar structure having an ion implanted region comprising: a semiconductor substrate including a first layer having a first conductivity type, a strained mono-crystalline semiconductor layer having a second conductivity type formed on the first layer, wherein the strained mono-crystalline semiconductor layer forms a strained heterojunction with the first layer; an ion implanted collector contact region of the first conductivity type selectively formed in the strained mono-crystalline semiconductor layer and the first layer such that the strained heterojunction structure is maintained in a strained condition; and a polycrystalline semiconductor layer of the first conductivity type formed on the strained mono-crystalline semiconductor layer, wherein the first layer forms a collector region, the strained mono-crystalline semiconductor layer forms a base region, and the polycrystalline semiconductor layer forms an emitter region.
Claim 19
Dependent Claim
130 words
A strained heterojunction bipolar structure having an ion implanted region comprising: a semiconductor substrate including a first layer having a first conductivity type, a strained mono-crystalline semiconductor layer having a second conductivity type formed on the first layer, wherein the strained mono-crystalline semiconductor layer forms a strained heterojunction with the first layer; an ion implanted collector contact region of the first conductivity type selectively formed in the strained mono-crystalline semiconductor layer and the first layer such that the strained heterojunction structure is maintained in a strained condition; and a polycrystalline semiconductor layer of the first conductivity type formed on the strained mono-crystalline semiconductor layer, wherein the first layer forms a collector region, the strained mono-crystalline semiconductor layer forms a base region, and the polycrystalline semiconductor layer forms an emitter region.
Claim 20
Dependent Claim
23 words
The structure of claim 16 wherein the first layer comprises silicon and the strained mono-crystalline semiconductor layer comprises Si 1-x Ge x .
Claim 21
Dependent Claim
15 words
The structure of claim 17 wherein X is in a range from 0.01 to 0.50.
Claim 22
Dependent Claim
12 words
The structure of claim 17 wherein the polycrystalline semiconductor layer comprises polysilicon.
Claim 23
Dependent Claim
98 words
The structure of claim 17 wherein the first conductivity type is n-type and the second conductivity type is p-type, and wherein the strained mono-crystalline semiconductor layer is doped with boron in a range from 1.0×10 18 to 5.0×10 19 atoms/cm 3 , and wherein the strained mono-crystalline semiconductor layer has a thickness in a range from 0.25 to 0.35 microns, and wherein the first layer is doped with an n-type dopant at a concentration in range from 1.0 to 3.0×10 16 atoms/cm 3 , and wherein the first layer has a thickness on an order of 1.5 microns.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-15 | 2000-04-15 | 2000-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-15 | 2004-04-15 | 2004-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-15 | 2008-04-15 | 2008-10-15 | $7700.00 | Window Closed / Lapsed |