US5565383A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for selective formation of silicide films without formation on vertical gate sidewalls using collimated sputtering
Assignee: Renesas Electronics Corp
•
Filing: 1996-01-16
•
Granted: 1996-10-15
•
Expires: 2016-01-16
Abstract
Abstract In a method for forming silicide films on a silicon substrate being formed thereon with a gate surrounded by gate side walls and being formed therein with diffusion regions, the silicide film being formed on a predetermined region of the silicon substrate at least except for an extremely thin film on the gate side walls. The method comprises the following steps. The silicon substrate is subjected to a collimated sputtering of metal atoms with use of a meshed mask on the silicon substrate surface to deposit a metal film on an entire surface of the silicon substrate, except for an extremely thin film on the vertical walls. The deposited metal film is further subjected to a heat treatment to react the metal film with the diffusion regions to thereby selectively form a metal silicide film at least on the diffusion regions, except for an extremely thin film on the vertical walls.
Inventors
- 👤 Isami Sakai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:12
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D30/00; H10D30/01; H10D30/021; H10D30/0212; H10D30/0223; H10D30/0227
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
154 words
A method of forming a silicide film on a silicon substrate being formed thereon with a gate surrounded by vertical gate side walls and being formed therein with diffusion regions, said silicide film being formed on a region of said silicon substrate, said vertical gate side walls being substantially free from a formation of said silicide film thereon, wherein said method comprises the steps of: subjecting said silicon substrate to a collimated sputtering of metal atoms with use of a meshed mask on said silicon substrate surface to deposit a metal film on an entire surface of said silicon substrate, substantially no metal film being deposited on said vertical walls; and subjecting said deposited metal film to a heat treatment to react said metal film with said diffusion regions to thereby selectively form a metal silicide film at least on said diffusion regions, substantially no metal silicide film being formed on said vertical walls.
Claim 2
Independent Claim
154 words
A method of forming a silicide film on a silicon substrate being formed thereon with a gate surrounded by vertical gate side walls and being formed therein with diffusion regions, said silicide film being formed on a region of said silicon substrate, said vertical gate side walls being substantially free from a formation of said silicide film thereon, wherein said method comprises the steps of: subjecting said silicon substrate to a collimated sputtering of metal atoms with use of a meshed mask on said silicon substrate surface to deposit a metal film on an entire surface of said silicon substrate, substantially no metal film being deposited on said vertical walls; and subjecting said deposited metal film to a heat treatment to react said metal film with said diffusion regions to thereby selectively form a metal silicide film at least on said diffusion regions, substantially no metal silicide film being formed on said vertical walls.
Claim 3
Dependent Claim
17 words
The method as claimed in claim 1, wherein said metal film is made of a refractory metal.
Claim 4
Dependent Claim
24 words
The method as claimed in claim 2, wherein said refractory metal is selected from the group consisting of titanium, molybdenum, and tungsten and cobalt.
Claim 5
Dependent Claim
38 words
The method as claimed in claim 1, further comprising the step of removing unreacted metal film substantially after said heat treatment step by a wet etching to leave said metal silicide film substantially only on said silicon substrate.
Claim 6
Dependent Claim
22 words
The method as claimed in claim 4, wherein said wet etching uses a mixture liquid of aqueous ammonia with aqueous hydrogen peroxide.
Claim 7
Independent Claim
16 words
The method as claimed in clam 1, wherein said gate comprises an impurity doped polysilicon film.
Claim 8
Dependent Claim
27 words
The method as claimed in claim 1, wherein said gate comprises a lamination of an impurity doped polysilicon film and a metal film overlying said polysilicon film.
References Cited (Backward Citations)
JPS5799775A
Cited
JPS59161023A
Cited
US4660276A
Cited
US5070038A
Cited
US5401675A
Cited
US5262354A
Cited
US5300813A
Cited
US5426330A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-15 | 2000-04-15 | 2000-10-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-15 | 2004-04-15 | 2004-10-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-15 | 2008-04-15 | 2008-10-15 | $7700.00 | Window Closed / Lapsed |