US5563100A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fabrication method of semiconductor device with refractory metal silicide formation by removing native oxide in hydrogen
Assignee: NEC Electronics Corp
•
Filing: 1994-12-16
•
Granted: 1996-10-08
•
Expires: 2014-12-16
Abstract
Abstract A fabrication method of a semiconductor device in which a refractory metal silicide film with a low sheet-resistance can be produced. First, a substructure made of Si-contained material is prepared, the surface of which is covered with a native SiO 2 film. The substructure is typically a single-crystal Si substrate or a polysilicon film. Next, the native SiO 3 film is reduced to be removed from the substructure in a hydrogen atmosphere whose pressure is from 1×10 -6 to 1×10 3 Torr. Then, a refractory metal film is formed on the surface of the substructure without exposing the substructure to the atmospheric pressure. The refractory metal film is in contact with the uncovered surface of the substructure. The refractory metal film is subjected to a heat-treatment process to react with the substructure, so that a refractory metal silicide film of a first phase is formed at the interface of the refractory metal film and the substructure. After the unreacted refractory metal film is removed from the substructure, the substructure is subjected to another heat-treatment process to transform in phase said refractory metal silicide film of said first phase to be that of a second phase lower in resistivity than that of said first phase.
Inventors
- 👤 Yoshihisa Matsubara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:00
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; Y; Y10; Y10S; Y10S148/00; Y10S148/017; Y10S438/00; Y10S438/934
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
167 words
A method of fabricating a semiconductor device, said method comprising the steps of: performing a first heat-treatment process on a Si-containing substructure located in a vacuum chamber to remove a native SiO 2 film from a surface of said substructure by reduction in a hydrogen atmosphere having a chamber pressure in the range of approximately 1×10 -6 to 1×10 -2 Torr such that said surface of said substructure is exposed without damage or doping from said hydrogen atmosphere; forming, in said vacuum chamber, a refractory metal film on said surface of said substructure without exposing said surface to the atmosphere to prevent formation of a second native oxide on said surface of said substructure; performing a second heat-treatment process on said refractory metal film to react said refractory metal film with said substructure to form a refractory metal silicide film at an interface of said refractory metal film and said surface of said substructure; and removing an unreacted portion of said refractory metal film from said substructure.
Claim 2
Independent Claim
167 words
A method of fabricating a semiconductor device, said method comprising the steps of: performing a first heat-treatment process on a Si-containing substructure located in a vacuum chamber to remove a native SiO 2 film from a surface of said substructure by reduction in a hydrogen atmosphere having a chamber pressure in the range of approximately 1×10 -6 to 1×10 -2 Torr such that said surface of said substructure is exposed without damage or doping from said hydrogen atmosphere; forming, in said vacuum chamber, a refractory metal film on said surface of said substructure without exposing said surface to the atmosphere to prevent formation of a second native oxide on said surface of said substructure; performing a second heat-treatment process on said refractory metal film to react said refractory metal film with said substructure to form a refractory metal silicide film at an interface of said refractory metal film and said surface of said substructure; and removing an unreacted portion of said refractory metal film from said substructure.
Claim 3
Dependent Claim
21 words
The method as claimed in claim 1, wherein said substructure is one of a single-crystal silicon substrate and a polysilicon film.
Claim 4
Dependent Claim
24 words
The method as claimed in claim 1, wherein said pressure range of said hydrogen atmosphere is from approximately 1×10 -3 to 1×10 -4 Torr.
Claim 5
Dependent Claim
21 words
The method as claimed in claim 1, wherein said refractory metal film has a melting point of 1500° C. or higher.
Claim 6
Dependent Claim
35 words
The method as claimed in claim 1, wherein said second heat treatment process is carried out at a temperature from approximately 600° to 700° C. in one of an inert atmosphere and a vacuum atmosphere.
Claim 7
Dependent Claim
24 words
The method as claimed in claim 5, wherein said second heat-treatment process is carried out in a period of approximately 10 to 60 seconds.
Claim 8
Dependent Claim
27 words
The method as claimed in claim 1, wherein said refractory metal film is a Ti film and said refractory metal silicide film is a TiSi 2 film.
Claim 9
Independent Claim
316 words
A method of fabricating a semiconductor device that includes at least one MOSFET, said method comprising the steps of: performing a first heat-treatment process on a substrate located in a vacuum chamber to remove a native SiO 2 film from a surface of a polysilicon film formed on a portion of said substrate and from a surface of a least one diffusion region formed in said substrate by reduction in a hydrogen atmosphere having a pressure in a range of 1×10 -6 to 1×10 -2 Torr such that said surface of said polysilicon film and said surface of said at least one diffusion region are exposed without damage or doping from said hydrogen atmosphere; forming, in said vacuum chamber, a refractory metal film on said surface of said polysilicon film and on said surface of said at least one diffusion region of said substrate without exposing said substrate to the atmosphere to prevent formation of a second native oxide on said surface of said polysilicon film and said surface of said at least one diffusion region; performing a second heat-treatment process on said substrate to produce refractory metal silicide films of a first structure at an interface of said refractory metal film and said surface of said polysilicon film and at an interface of said refractory metal film and said surface of said at least one diffusion region by a reaction between a refractory metal element contained in said refractory metal films and a Si element contained in said polysilicon film and in said at least one diffusion region; removing an unreacted portion of said refractory metal films from said substrate; and performing a third heat-treatment process on said substrate to transform said refractory metal silicide films of said first structure into refractory metal silicide films of a second structure having a lower resistivity than that of said refractory metal silicide films of said first structure.
Claim 10
Independent Claim
316 words
A method of fabricating a semiconductor device that includes at least one MOSFET, said method comprising the steps of: performing a first heat-treatment process on a substrate located in a vacuum chamber to remove a native SiO 2 film from a surface of a polysilicon film formed on a portion of said substrate and from a surface of a least one diffusion region formed in said substrate by reduction in a hydrogen atmosphere having a pressure in a range of 1×10 -6 to 1×10 -2 Torr such that said surface of said polysilicon film and said surface of said at least one diffusion region are exposed without damage or doping from said hydrogen atmosphere; forming, in said vacuum chamber, a refractory metal film on said surface of said polysilicon film and on said surface of said at least one diffusion region of said substrate without exposing said substrate to the atmosphere to prevent formation of a second native oxide on said surface of said polysilicon film and said surface of said at least one diffusion region; performing a second heat-treatment process on said substrate to produce refractory metal silicide films of a first structure at an interface of said refractory metal film and said surface of said polysilicon film and at an interface of said refractory metal film and said surface of said at least one diffusion region by a reaction between a refractory metal element contained in said refractory metal films and a Si element contained in said polysilicon film and in said at least one diffusion region; removing an unreacted portion of said refractory metal films from said substrate; and performing a third heat-treatment process on said substrate to transform said refractory metal silicide films of said first structure into refractory metal silicide films of a second structure having a lower resistivity than that of said refractory metal silicide films of said first structure.
Claim 11
Dependent Claim
24 words
The method as claimed in claim 8, wherein said pressure range of said hydrogen atmosphere is from approximately 1×10 -3 to 1×10 -4 Torr.
Claim 12
Dependent Claim
21 words
The method as claimed in claim 8, wherein said refractory metal film has a melting point of 1500° C. or higher.
Claim 13
Dependent Claim
34 words
The method as claimed in claim 8, wherein said second heat-treatment process is carried out at a temperature from approximately 600° to 700° C. in one of an inert atmosphere and a vacuum atmosphere.
Claim 14
Dependent Claim
24 words
The method as claimed in claim 11, wherein said second heat-treatment process is carried out in a period of approximately 10 to 60 seconds.
Claim 15
Dependent Claim
27 words
The method as claimed in claim 8, wherein said refractory metal film is a Ti film and said refractory metal silicide film is a TiSi 2 film.
Claim 16
Dependent Claim
27 words
The method as claimed in claim 1, further comprising the step of: performing a third heat-treatment process on said refractory metal silicide film to lower its resistivity.
Claim 17
Dependent Claim
26 words
The method as claimed in claim 14, wherein said third heat-treatment process lowers said resistivity without causing agglomeration or flow of said refractory metal silicide film.
Claim 18
Dependent Claim
44 words
The method as claimed in claim 8, further comprising the steps of: forming a gate insulator film on a portion of a single-crystal Si substrate; forming a polysilicon film on said gate insulator film; and forming at least one diffusion region in said substrate.
Claim 19
Dependent Claim
20 words
The method as claimed in claim 16, wherein said at least one diffusion region comprises a pair of source/drain regions.
Claim 20
Dependent Claim
29 words
The method as claimed in claim 16, wherein said third heat-treatment process transforms said refractory metal silicide films without causing agglomeration or flow of said refractory metal silicide films.
References Cited (Backward Citations)
US4940509A
Cited
US5338697A
Cited
JPH03263830A
Cited
US5089441A
Cited
JPH04226024A
Cited
US5023201A
Cited
US5316977A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-08 | 2000-04-08 | 2000-10-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-08 | 2004-04-08 | 2004-10-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-08 | 2008-04-08 | 2008-10-08 | $7700.00 | Window Closed / Lapsed |