Method for forming an electrode and/or wiring layer by reducing copper oxide or silver oxide
Assignee: Toshiba Corp
•
Filing: 1995-03-17
•
Granted: 1996-10-01
•
Expires: 2015-03-17
Abstract
Abstract The present invention provides a method of manufacturing a semiconductor device, including the steps of forming a metal oxide film made of a metal oxide having a decrease in standard free energy smaller than a decrease in standard free energy of hydrogen oxide or of carbon oxide, on an insulating film formed on a semiconductor substrate, forming a metal oxide film pattern by subjecting a treatment to the metal oxide film, and converting said metal oxide pattern into at least one of an electrode and a wiring made of a metal which is a main component constituting the metal oxide, by reducing the metal oxide film pattern at a temperature of 80 DEG to 500 DEG C.
Inventors
- 👤 Mie Matsuo
- 👤 Haruo Okano
- 👤 Nobuo Hayasaka
- 👤 Kyoichi Suguro
- 👤 Hideshi Miyajima
- 👤 Jun-ichi Wada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:51
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10W20/032; H10W20/033; H10W20/037; H10W20/071; H10W20/093; H10W20/094; H10W20/40; H10W20/41; H10W20/425; H10W20/435
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
158 words
A method of forming an electrode and/or wiring pattern, comprising the steps of: forming a metal oxide film comprising a metal on an insulating film, said insulating film having a groove formed on the surface thereof, and formed on a semiconductor substrate, wherein the metal oxide of said metal oxide film, upon reduction with a reducing agent, in the reduction of the last step infra, generates at least one member selected from the group consisting of H 2 O, CO and CO 2 as the oxidized product; forming a metal oxide film pattern by subjecting said metal oxide film to a treatment; and converting said metal oxide pattern into at least one of an electrode and a wiring pattern made of the metal which constitutes said metal oxide, by reducing said metal oxide film pattern at a temperature of 80° to 500° C., wherein said at least one of the electrode and the wiring pattern fills said groove.
Claim 2
Independent Claim
158 words
A method of forming an electrode and/or wiring pattern, comprising the steps of: forming a metal oxide film comprising a metal on an insulating film, said insulating film having a groove formed on the surface thereof, and formed on a semiconductor substrate, wherein the metal oxide of said metal oxide film, upon reduction with a reducing agent, in the reduction of the last step infra, generates at least one member selected from the group consisting of H 2 O, CO and CO 2 as the oxidized product; forming a metal oxide film pattern by subjecting said metal oxide film to a treatment; and converting said metal oxide pattern into at least one of an electrode and a wiring pattern made of the metal which constitutes said metal oxide, by reducing said metal oxide film pattern at a temperature of 80° to 500° C., wherein said at least one of the electrode and the wiring pattern fills said groove.
Claim 3
Dependent Claim
34 words
The method according to claim 1, wherein said at least one of the electrode and said wiring pattern is constituted of at least one metal selected from the group consisting of Cu and Ag.
Claim 4
Dependent Claim
25 words
The method according to claim 1, wherein reduction of said metal oxide film pattern is performed in a gaseous atmosphere containing hydrogen or carbon monoxide.
Claim 5
Dependent Claim
13 words
The method according to claim 1, wherein said treatment is Chemical Mechanical Polishing.
Claim 6
Dependent Claim
16 words
The method according to claim 1, wherein said metal oxide film is formed by collimated sputtering.
Claim 7
Dependent Claim
27 words
The method according to claim 1 wherein the formation of said metal oxide film on said semiconductor substrate is performed by sputtering while rotating said semiconductor substrate.
Claim 8
Dependent Claim
50 words
The method according to claim 1, wherein said semiconductor substrate is swung such that an axis perpendicular to a surface of said semiconductor substrate is more than -90° and less than 90° with respect to the incident direction of particles in a sputtering step which forms the metal oxide film.
Claim 9
Independent Claim
116 words
A method of forming an electrode and/or wiring pattern, comprising the steps of: forming a groove in an insulating film which is formed on a semiconductor substrate; forming a metal layer on said insulating film such that said groove is filled with the metal of said metal layer; forming a metal oxide layer by oxidizing the metal layer to the extent that at least the top-portion of the metal layer in said groove is converted to metal oxide; removing the metal oxide film remaining on the portion of said insulating film other than said groove; and forming at least one of said electrode and said wiring pattern, made of the metal, by reducing the metal oxide.
Claim 10
Independent Claim
116 words
A method of forming an electrode and/or wiring pattern, comprising the steps of: forming a groove in an insulating film which is formed on a semiconductor substrate; forming a metal layer on said insulating film such that said groove is filled with the metal of said metal layer; forming a metal oxide layer by oxidizing the metal layer to the extent that at least the top-portion of the metal layer in said groove is converted to metal oxide; removing the metal oxide film remaining on the portion of said insulating film other than said groove; and forming at least one of said electrode and said wiring pattern, made of the metal, by reducing the metal oxide.
Claim 11
Dependent Claim
14 words
The method according to claim 8, wherein said metal layer contains Cu or Ag.
Claim 12
Dependent Claim
20 words
The method according to claim 9, wherein a barrier layer is interposed between said insulating film and said metal layer.
Claim 13
Dependent Claim
60 words
The method according to claim 10, wherein said barrier-layer is a first layer made of at least one metal selected from the group consisting of Ti, Nb, W, Mo, Cr, V, Ta, Zr, and Hf, or a laminated layer of said first layer and a second layer made of a nitride of at least one metal selected from said group.
Claim 14
Dependent Claim
29 words
The method according to claim 11, which further comprises: interposing an oxide film of a metal which constitutes said metal layer between said barrier layer and said metal layer.
Claim 15
Dependent Claim
27 words
The method according to claim 9, wherein reduction of said metal oxide is performed by applying a heat treatment at a temperature of 80° to 500° C.
Claim 16
Dependent Claim
24 words
The method according to claim 9, wherein said reduction of said metal oxide is performed in a gaseous atmosphere containing hydrogen or carbon monoxide.
Claim 17
Dependent Claim
27 words
The method according to claim 8, wherein a film remaining on a portion of said insulating film other than said groove is removed by Chemical Mechanical Polishing.
Claim 18
Independent Claim
113 words
A method of forming an electrode and/or wiring pattern, comprising the steps of: forming a metal oxide film comprising a metal selected from the group consisting of Cu, Ag, Ni and Pd, on an insulating film, whose surface has a groove therein which defines at least one of said electrode and wiring pattern, which is formed on a semiconductor substrate; forming a metal oxide film pattern by subjecting said metal oxide film to a treatment; and converting said metal oxide pattern into at least one of said electrode and said wiring pattern in said groove made of a metal, by reducing said metal oxide film pattern at a temperature of 80° to 500°.
Claim 19
Independent Claim
113 words
A method of forming an electrode and/or wiring pattern, comprising the steps of: forming a metal oxide film comprising a metal selected from the group consisting of Cu, Ag, Ni and Pd, on an insulating film, whose surface has a groove therein which defines at least one of said electrode and wiring pattern, which is formed on a semiconductor substrate; forming a metal oxide film pattern by subjecting said metal oxide film to a treatment; and converting said metal oxide pattern into at least one of said electrode and said wiring pattern in said groove made of a metal, by reducing said metal oxide film pattern at a temperature of 80° to 500°.
Claim 20
Dependent Claim
30 words
The method according to claim 16, wherein the structure of said insulating film on said semiconductor substrate forms a capacitor, and said electrode is formed on the capacitor insulating film.
Claim 21
Dependent Claim
25 words
The method according to claim 16, wherein reduction of said metal oxide film pattern is performed in a gaseous atmosphere containing hydrogen or carbon monoxide.
Claim 22
Dependent Claim
13 words
The method according to claim 16, wherein said treatment is Chemical Mechanical Polishing.
Claim 23
Dependent Claim
16 words
The method according to claim 16, wherein said metal oxide film is formed by collimated sputtering.
Claim 24
Dependent Claim
27 words
The method of claim 16, wherein formation of said metal oxide film on said semiconductor substrate is performed by sputtering while said semiconductor substrate is being rotated.
Claim 25
Dependent Claim
50 words
The method according to claim 16, wherein said semiconductor substrate is swung such that an axis perpendicular to a surface of said semiconductor substrate is more than -90° and less than 90° with respect to the incident direction of particles in a sputtering step which forms the metal oxide film.
Claim 26
Dependent Claim
31 words
The method according to claim 16, wherein a metal film is formed below the metal oxide film to reduce the metal oxide and to oxidize a metal of the metal film.
Claim 27
Dependent Claim
27 words
The method according to claim 23, wherein the steps of the method form a capacitor and said oxidized metal film is an insulating film of the capacitor.
Claim 28
Dependent Claim
32 words
The method according to claim 1, wherein a metal film is formed below the metal oxide film to reduce the metal oxide film and to oxidize the metal of said metal film.
Claim 29
Dependent Claim
23 words
The method according to claim 25, wherein the processing of claim 25 forms a capacitor whose insulating film is said oxidized metal film.
References Cited (Backward Citations)
US4039698A
Cited
US4557036A
Cited
US4511601A
Cited
JPH05145067A
Cited
JPH05145068A
Cited
US5290358A
Cited
US5387315A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-01 | 2000-04-01 | 2000-10-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-01 | 2004-04-01 | 2004-10-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-01 | 2008-04-01 | 2008-10-01 | $7700.00 | Window Closed / Lapsed |