Method of making graded refractive index polymeric optical fibers and optical fibers made by the method
Assignee: UNION CHEMICAL LABORATORIES/INDUSTRIAL TECHNOLOGY RESEARCH INSTITUTE
•
Filing: 1994-09-07
•
Granted: 1996-09-10
•
Expires: 2014-09-07
Abstract
Abstract A continuous manufacturing method is provided by extruding a composite optical fiber from two polymeric solutions containing two different monomers having different refractive indices, and then allowing the monomers to diffuse in a diffusion region such that the two monomers are diffused into each other before the optical fiber is hardened.
Inventors
- 👤 Bang C. Ho
- 👤 Jian-Hong Chen
- 👤 Shu-Yin Yang
- 👤 Yih-Her Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:03
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/02033; G02B6/02038; B; B29; B29C; B29C48/00; B29C48/03; B29C48/05; B29C48/15; B29C48/154; B29C48/25; B29C48/30; B29C48/32; B29C48/34; B29D; B29D11/00; B29D11/00663; B29D11/00682; C; C08; C08F; C08F265/00; C08F265/04; C08F265/06
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
230 words
A method of producing a composite optical fiber of polymeric materials having a continuous refractive index distribution from the center of the fiber to the outer layer of the fiber comprising the steps of: providing a first mixture of a first polymer and at least one first monomer that is a solvent for said first polymer, providing a second mixture of a second polymer and at least one second monomer that is a solvent for said second polymer, said at least one second monomer being different from said at least a one first monomer, flowing said first and said second mixtures through a concentric die equipped with an orifice such that a composite optical fiber having an inner layer and an outer layer formed by said first and said second mixtures, respectively, having an interface there in-between is obtained, passing said composite optical fiber through a diffusion apparatus for a sufficient length of time such that a sufficient amount of said first and said second monomers diffuses across said interface into said outer layer and said inner layer, respectively, and passing said composite optical fiber through a hardening fixture such that said composite optical fiber is hardened by a radiation energy or an oxidation/reduction process without removing an outermost layer of said fiber, wherein said composite optical fiber formed has a diameter between about 0.1 mm to about 5 mm.
Claim 2
Independent Claim
230 words
A method of producing a composite optical fiber of polymeric materials having a continuous refractive index distribution from the center of the fiber to the outer layer of the fiber comprising the steps of: providing a first mixture of a first polymer and at least one first monomer that is a solvent for said first polymer, providing a second mixture of a second polymer and at least one second monomer that is a solvent for said second polymer, said at least one second monomer being different from said at least a one first monomer, flowing said first and said second mixtures through a concentric die equipped with an orifice such that a composite optical fiber having an inner layer and an outer layer formed by said first and said second mixtures, respectively, having an interface there in-between is obtained, passing said composite optical fiber through a diffusion apparatus for a sufficient length of time such that a sufficient amount of said first and said second monomers diffuses across said interface into said outer layer and said inner layer, respectively, and passing said composite optical fiber through a hardening fixture such that said composite optical fiber is hardened by a radiation energy or an oxidation/reduction process without removing an outermost layer of said fiber, wherein said composite optical fiber formed has a diameter between about 0.1 mm to about 5 mm.
Claim 3
Dependent Claim
72 words
A method according to claim 1, wherein said first and said second polymer are selected from a group consisting of polymethyl methacrylate and a copolymer formed of methyl methacrylate and a monomer selected from the group consisting of ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, t-butyl methacrylate, cyclohexyl methacrylate, fluoro-alkyl methacrylate, 2-hydroxy methyl methacrylate, 2-phenoxyethyl methacrylate, glyceryl methacrylate, benzyl methacrylate, phenyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate, fluoro-alkyl acrylate and acrylic acid.
Claim 4
Dependent Claim
61 words
A method according to claim 1, wherein said at least one first monomer and said at least one second monomer are selected from the group consisting of methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, t-butyl methacrylate, cyclohexyl methacrylate, phenyl methacrylate, benzyl methacrylate, fluoro-alkyl methacrylate, 2-hydroxy methyl methacrylate, 2-phenoxyethyl methacrylate, glaryl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate and fluoro-alkyl acrylate.
Claim 5
Dependent Claim
34 words
A method according to claim 1, wherein at least one of said first reactant mixture and said second reactant mixture is heated to a predetermined temperature to facilitate the formation of said reactant mixture.
Claim 6
Dependent Claim
24 words
A method according to claim 1, wherein at least one of said first reactant mixture and said second reactant mixture further comprises a catalyst.
Claim 7
Independent Claim
231 words
A method of producing a composite optical fiber of polymeric materials having a continuous refractive index distribution from the center of the fiber to the outer layer of the fiber comprising the steps of: providing a first mixture of a first polymer and at least one first monomer that is a solvent for said first polymer, providing a second mixture of a second polymer and at least one second monomer that is a solvent for said second polymer, said at least one second monomer being different from said at least one first monomer, flowing said first and said second mixtures through a concentric die equipped with an orifice such that a composite optical fiber having an inner layer and an outer layer formed by said first and said second mixtures, respectively, having an interface there in-between is obtained, passing said composite optical fiber through a diffusion apparatus for a sufficient length of time such that a sufficient amount of said first and said second monomers diffuses across said interface into said outer layer and said inner layer, respectively, and passing said composite optical fiber through a hardening fixture such that said composite optical fiber is hardened by a radiation energy or an oxidation/reduction process without removing an outermost layer of said fiber, wherein the volume ratio between said inner layer and said outer layer is between about 1:1 and about 1:100.
Claim 8
Independent Claim
231 words
A method of producing a composite optical fiber of polymeric materials having a continuous refractive index distribution from the center of the fiber to the outer layer of the fiber comprising the steps of: providing a first mixture of a first polymer and at least one first monomer that is a solvent for said first polymer, providing a second mixture of a second polymer and at least one second monomer that is a solvent for said second polymer, said at least one second monomer being different from said at least one first monomer, flowing said first and said second mixtures through a concentric die equipped with an orifice such that a composite optical fiber having an inner layer and an outer layer formed by said first and said second mixtures, respectively, having an interface there in-between is obtained, passing said composite optical fiber through a diffusion apparatus for a sufficient length of time such that a sufficient amount of said first and said second monomers diffuses across said interface into said outer layer and said inner layer, respectively, and passing said composite optical fiber through a hardening fixture such that said composite optical fiber is hardened by a radiation energy or an oxidation/reduction process without removing an outermost layer of said fiber, wherein the volume ratio between said inner layer and said outer layer is between about 1:1 and about 1:100.
Claim 9
Dependent Claim
25 words
A method to claim 6, wherein the volume ratio between said inner layer and said outer layer is preferably between about 1:1 and about 1:10.
Claim 10
Dependent Claim
27 words
A method according to claim 6, wherein the volume ratio between said inner layer and said outer layer is more preferably between about 1:1 and about 1:5.
Claim 11
Dependent Claim
26 words
A method according to claim 1, wherein the refractive index of said first polymer is higher or equal to the refractive index of said second polymer.
Claim 12
Independent Claim
264 words
A method of producing a composite optical fiber of polymeric materials having a continuous refractive index distribution from the center of the fiber to the outer layer of the fiber comprising the steps of: providing a first mixture of a first polymer and at least one first monomer that is a solvent for said first polymer, providing a second mixture of a second polymer and at least one second monomer that is a solvent for said second polymer, said at least one second monomer being different from said at least one first monomer, flowing said first and said second mixtures through a concentric die equipped with an orifice such that a composite optical fiber having an inner layer and an outer layer formed by said first and said second mixtures, respectively, having an interface there in-between is obtained, passing said composite optical fiber through a diffusion apparatus for a sufficient length of time such that a sufficient amount of said first and said second monomers diffuses across said interface into said outer layer and said inner layer, respectively, and passing said composite optical fiber through a hardening fixture such that said composite optical fiber is hardened by a radiation energy or an oxidation/reduction process without removing an outermost layer of said fiber, wherein the total weight or said at least one first monomer sand said at least one second monomer is between about 10 to about 80 percent of the total weight of said optical fiber, and more preferably between about 40 to about 70 percent of the total weight of said optical fiber.
Claim 13
Independent Claim
264 words
A method of producing a composite optical fiber of polymeric materials having a continuous refractive index distribution from the center of the fiber to the outer layer of the fiber comprising the steps of: providing a first mixture of a first polymer and at least one first monomer that is a solvent for said first polymer, providing a second mixture of a second polymer and at least one second monomer that is a solvent for said second polymer, said at least one second monomer being different from said at least one first monomer, flowing said first and said second mixtures through a concentric die equipped with an orifice such that a composite optical fiber having an inner layer and an outer layer formed by said first and said second mixtures, respectively, having an interface there in-between is obtained, passing said composite optical fiber through a diffusion apparatus for a sufficient length of time such that a sufficient amount of said first and said second monomers diffuses across said interface into said outer layer and said inner layer, respectively, and passing said composite optical fiber through a hardening fixture such that said composite optical fiber is hardened by a radiation energy or an oxidation/reduction process without removing an outermost layer of said fiber, wherein the total weight or said at least one first monomer sand said at least one second monomer is between about 10 to about 80 percent of the total weight of said optical fiber, and more preferably between about 40 to about 70 percent of the total weight of said optical fiber.
Claim 14
Dependent Claim
22 words
A method according to claim 1, wherein said optical fiber may be elongated to obtain a desirable diameter before the hardening step.
Claim 15
Dependent Claim
131 words
A composite optical fiber of polymeric materials comprising: a core formed by the polymerization of a first polymer dissolved in at least one first monomer solvent, a surface layer formed by the polymerization of a second polymer dissolved in at least one second monomer solvent, and an interface between said core and said surface layer across which a sufficient amount of said at least one first monomer being diffused into said surface layer and a sufficient amount of said at least one second monomer being diffused into said core to cause the formation of a continuous distribution of refractive index from a center of said core to the outermost layer of said surface layer of the fiber, wherein said fiber has a diameter between about 0.1 mm to about 5 mm.
Claim 16
Dependent Claim
131 words
A composite optical fiber of polymeric materials comprising: a core formed by the polymerization of a first polymer dissolved in at least one first monomer solvent, a surface layer formed by the polymerization of a second polymer dissolved in at least one second monomer solvent, and an interface between said core and said surface layer across which a sufficient amount of said at least one first monomer being diffused into said surface layer and a sufficient amount of said at least one second monomer being diffused into said core to cause the formation of a continuous distribution of refractive index from a center of said core to the outermost layer of said surface layer of the fiber, wherein said fiber has a diameter between about 0.1 mm to about 5 mm.
Claim 17
Dependent Claim
74 words
A composite optical fiber according to claim 12, wherein said first and said second polymer are selected from a group consisting of polymethyl methacrylate and a copolymer formed of methyl methacrylate and a monomer selected from the group consisting of ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, t-butyl methacrylate, cyclohexyl methacrylate, fluoro-alkyl methacrylates 2-hydroxy methyl methacrylate, 2-phenoxyethyl methacrylate, glyceryl methacrylate, benzyl methacrylate, phenyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate, fluoro-alkyl acrylate and acrylic acid.
Claim 18
Dependent Claim
65 words
A composite optical fiber according to claim 12, wherein said at least one first monomer solvent and said at least one second monomer solvent are selected from the group consisting of methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, t-butyl methacrylate, cyclohexyl methacrylate, phenyl methacrylate, benzyl methacrylate, fluoro-alkyl methacrylate, 2-hydroxy methyl methacrylate, 2-phenoxyethyl methacrylate, glaryl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate and fluoro-alkyl acrylate.
Claim 19
Dependent Claim
28 words
A composite optical fiber according to claim 12, wherein at least one of the polymerization process for said core and said surface layer is assisted by a catalyst.
Claim 20
Dependent Claim
135 words
A composite optical fiber of polymeric materials comprising: a core formed by the polymerization of a first polymer dissolved in at least one first monomer solvent, a surface layer formed by the polymerization of a second polymer dissolved in at least one second monomer solvent, and an interface between said core and said surface layer across which a sufficient amount of said at least one first monomer being diffused into said surface layer and a sufficient amount of said at least one second monomer being diffused into said core to cause the formation of a continuous distribution of refractive index from a center of said core to the outermost layer of said surface layer of the fiber, wherein the volume ratio between said core and said surface layer is between about 1:1 and about 1:100.
Claim 21
Dependent Claim
135 words
A composite optical fiber of polymeric materials comprising: a core formed by the polymerization of a first polymer dissolved in at least one first monomer solvent, a surface layer formed by the polymerization of a second polymer dissolved in at least one second monomer solvent, and an interface between said core and said surface layer across which a sufficient amount of said at least one first monomer being diffused into said surface layer and a sufficient amount of said at least one second monomer being diffused into said core to cause the formation of a continuous distribution of refractive index from a center of said core to the outermost layer of said surface layer of the fiber, wherein the volume ratio between said core and said surface layer is between about 1:1 and about 1:100.
Claim 22
Dependent Claim
27 words
A composite optical fiber according to claim 16, wherein the volume ratio between said core and said surface layer is preferably between about 1:1 and about 1:10.
Claim 23
Dependent Claim
26 words
A composite optical fiber according to claim 16, wherein the volume ratio between said core and surface layer is more preferably between 1:1 and about 1:5.
References Cited (Backward Citations)
JPS525857A
Cited
US4125644A
Cited
JPS5430301A
Cited
JPS5637521A
Cited
JPS5729682A
Cited
US4861835A
Cited
US4807964A
Cited
JPH01189602A
Cited
JPH01254704A
Cited
JPH0216505A
Cited
JPH0233104A
Cited
US5378776A
Cited
US5235660A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-10 | 2000-03-11 | 2000-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-10 | 2004-03-11 | 2004-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-10 | 2008-03-11 | 2008-09-10 | $7700.00 | Window Closed / Lapsed |