Blow-molded article made from thermoplastic resin composition
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1995-03-07
•
Granted: 1996-09-10
•
Expires: 2015-03-07
Abstract
Abstract A blow-molded article made from a polyphenylene ether/polyamide composition reinforced with glass fibers is provided. The article is excellent in mechanical properties and blow moldability. The composition comprises a mixture consisting of (A) 10-65 parts by weight of a polyphenylene ether and (B) 90-35 parts by weight of a polyamide and, on the basis of 100 parts by weight of said mixture, (C) 10-100 parts by weight of a glass fiber, (D) 1-35 parts by weight of a polyolefin and (E) 0.01-10 parts by weight of an unsaturated polar monomer compound having in its molecule both (a) carbon-carbon double bond or carbon-carbon triple bond and (b) carboxyl group, acid anhydride group, amino group, acid amide group, imide group, epoxy group, carboxylic acid ester group, isocyanate group, methylol group or hydroxyl group as a compatibilizing agent, amounts of (C), (D) and (E) being based on 100 parts by weight of [(A)+(B)].
Inventors
- 👤 Kenji Nagaoka
- 👤 Hiroshi Hagimori
- 👤 Kaoru Kitadono
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 05:28
CPC Classifications
C; C08; C08L; C08L71/00; C08L71/08; C08L71/10; C08L71/12; C08L71/123; C08F; C08F283/00; C08F283/04; C08F283/06; C08F283/08; C08L77/00; Y; Y10; Y10S; Y10S525/00; Y10S525/905
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
170 words
A blow-molded article made from a thermoplastic resin composition which comprises a mixture consisting of (A) 10-65 parts by weight of a polyphenylene ether and (B) 90-35 parts by weight of a polyamide, (C) 10-100 parts by weight of a glass fiber, (D) 3-20 parts by weight of a polyolefin and (E) 0.01-10 parts by weight of an unsaturated polar monomer compound having in its molecule simultaneously (a) carbon-carbon double bond or carbon-carbon triple bond and (b) carboxyl group, acid anhydride group, amino group, acid amide group, imide group, epoxy group, carboxylic acid ester group, isocyanate group, methylol group or hydroxyl group as a compatibilizing agent, said amounts of (C), (D) and (E) are respectively on the basis of 100 parts by weight of a mixture of (A) and (B), wherein said thermoplastic resin composition has a critical parison length of 450 to 550 mm when it is blow-molded using a 50 mm φ blow-molding machine at an extrusion rate of 170 g/minute and at a temperature of 270° C.
Claim 2
Dependent Claim
170 words
A blow-molded article made from a thermoplastic resin composition which comprises a mixture consisting of (A) 10-65 parts by weight of a polyphenylene ether and (B) 90-35 parts by weight of a polyamide, (C) 10-100 parts by weight of a glass fiber, (D) 3-20 parts by weight of a polyolefin and (E) 0.01-10 parts by weight of an unsaturated polar monomer compound having in its molecule simultaneously (a) carbon-carbon double bond or carbon-carbon triple bond and (b) carboxyl group, acid anhydride group, amino group, acid amide group, imide group, epoxy group, carboxylic acid ester group, isocyanate group, methylol group or hydroxyl group as a compatibilizing agent, said amounts of (C), (D) and (E) are respectively on the basis of 100 parts by weight of a mixture of (A) and (B), wherein said thermoplastic resin composition has a critical parison length of 450 to 550 mm when it is blow-molded using a 50 mm φ blow-molding machine at an extrusion rate of 170 g/minute and at a temperature of 270° C.
Claim 3
Dependent Claim
22 words
A blow-molded article according to claim 1 wherein the polyolefin (D) is a polyolefin which is not compatible with the polyphenylene ether.
Claim 4
Dependent Claim
23 words
A blow-molded article according to claim 1 wherein the polyolefin (D) is a copolymer of a modified or unmodified ethylene and an α-olefin.
Claim 5
Dependent Claim
22 words
A blow-molded article according to claim 1 wherein the polyolefin (D) is a copolymer of a modified or unmodified ethylene and butene-1.
Claim 6
Dependent Claim
34 words
A blow-molded article according to claim 1 wherein the amount of the glass fiber (C) is 15-80 parts by weight on the basis of 100 parts by weight of the mixture (A) and (B).
References Cited (Backward Citations)
JPS61204263A
Cited
US4873276A
Cited
JPS6335652A
Cited
JPS63101452A
Cited
US5112907A
Cited
US4957966A
Cited
US5175211A
Cited
US5086105A
Cited
US5147942A
Cited
US5084511A
Cited
JPH03177454A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-10 | 2000-03-11 | 2000-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-10 | 2004-03-11 | 2004-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-10 | 2008-03-11 | 2008-09-10 | $7700.00 | Window Closed / Lapsed |