Abrasive grain containing alumina and zirconia
Assignee: 3M Co
•
Filing: 1995-11-06
•
Granted: 1996-09-03
•
Expires: 2015-11-06
Abstract
Abstract A method of preparing preferred abrasive grain includes: preparing a dispersion including alpha alumina oxide monohydrate and zirconia sol therein; converting the dispersion to base grit material; and sintering the base grit to form abrasive grains. The presence of the zirconia sol within the dispersion from which the base grits are formed provides an improved abrasive grain. The improved abrasive grain are useful in abrasive products.
Inventors
- 👤 Henry A. Larmie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:28
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C09; C09K; C09K3/00; C09K3/14; C09K3/1409; C09K3/1418; B; B24; B24D; B24D11/00; B24D3/00; B24D3/02; B24D3/04; B24D3/14; B24D5/00; B24D5/12; C04B35/111; C04B35/117; C04B35/119; C04B35/622
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
168 words
A method of preparing abrasive grain material; said method comprising the steps of: (a) preparing a dispersion of alumina hydrate and zirconia particles, wherein at least about 97% by weight of said zirconia particles are less than about 0.2 micrometer in size; (b) forming alumina base grits from said dispersion; and (c) sintering said alumina base grits to provide abrasive grain comprising about 70 to about 99.9 percent by weight alumina and at least about 0.1 percent by weight zirconia, based on the total weight of said abrasive grain, said alumina being present as one of alpha alumina, alumina reaction product, or a combination thereof, said zirconia being present as one of zirconia or zirconia and zirconia reaction product, with the proviso that said zirconia particles are present in said dispersion in an amount sufficient to increase densification of said abrasive grain of step (c) as compared to an abrasive grain made according to steps (a), (b), and (c) without the presence of zirconia in said abrasive grain.
Claim 2
Independent Claim
168 words
A method of preparing abrasive grain material; said method comprising the steps of: (a) preparing a dispersion of alumina hydrate and zirconia particles, wherein at least about 97% by weight of said zirconia particles are less than about 0.2 micrometer in size; (b) forming alumina base grits from said dispersion; and (c) sintering said alumina base grits to provide abrasive grain comprising about 70 to about 99.9 percent by weight alumina and at least about 0.1 percent by weight zirconia, based on the total weight of said abrasive grain, said alumina being present as one of alpha alumina, alumina reaction product, or a combination thereof, said zirconia being present as one of zirconia or zirconia and zirconia reaction product, with the proviso that said zirconia particles are present in said dispersion in an amount sufficient to increase densification of said abrasive grain of step (c) as compared to an abrasive grain made according to steps (a), (b), and (c) without the presence of zirconia in said abrasive grain.
Claim 3
Dependent Claim
32 words
A method according to claim 1 wherein said dispersion is aqueous dispersion, and further comprises the step of calcining said alumina base grits of step (b) before said sintering of step (c).
Claim 4
Dependent Claim
36 words
A method according to claim 2 wherein said dispersion contains a sufficient amount of said zirconia particles therein such that said abrasive grain of step (c) comprises between about 0.1% and about 30% by weight zirconia.
Claim 5
Dependent Claim
34 words
A method according to claim 2 wherein said dispersion comprises about 15 to about 40% by weight colloidal zirconia particles of which about 50% by weight are less than about 0.05 micrometer in size.
Claim 6
Dependent Claim
19 words
A method according to claim 2 wherein said aqueous dispersion comprises about 30 to about 80% by weight water.
Claim 7
Dependent Claim
15 words
A method according to claim 2 wherein said aqueous dispersion further comprises a nucleating material.
Claim 8
Dependent Claim
16 words
A method according to claim 2 wherein said aqueous dispersion further comprises a metal oxide precursor.
Claim 9
Dependent Claim
26 words
A method according to claim 2 including a step of impregnating said calcined alumina base grits with metal oxide precursor prior to said step of sintering.
Claim 10
Dependent Claim
164 words
A method according to claim 8 wherein said metal oxide precursor is a precursor of an oxide selected from the group consisting of yttria, magnesium oxide, and a rare earth oxide; wherein said metal oxide precursor is present in an amount sufficient to provide abrasive grain of step (c) with at least about 0.5% by weight of at least one metal oxide, said metal oxide being present as one of a metal oxide, metal oxide reaction product, or a combination thereof, (i) said rare earth oxide being selected from the group consisting of oxides of: praseodymium, samarium, ytterbium, neodymium, lanthanum, gadolinium, cerium, dysprosium, erbium, and mixtures thereof; and (ii) each of said yttria, magnesium oxide, and rare earth oxide, if present in said abrasive grain of step (c), being present up to about 10% by weight; and wherein said abrasive grain of step (c) comprises about 70 to about 95 percent by weight alumina and about 0.1 to about 15 percent by weight zirconia.
Claim 11
Dependent Claim
27 words
A method according to claim 9 wherein said yttria precursor is present in an amount sufficient to provide abrasive grain with about 0.5 to about 10% yttria.
Claim 12
Dependent Claim
60 words
A method according to claim 10 wherein said magnesium oxide precursor is present in an amount sufficient to provide said abrasive grain with about 0.5 to about 1.5% by weight magnesium oxide; and said rare earth oxide precursor is present in an amount sufficient to provide said abrasive grain with about 0.5 to about 5% by weight rare earth oxide.
Claim 13
Dependent Claim
60 words
A method according to claim 2 including a step of coating at least one of said alumina base grits and said calcined alumina base grits with a material selected from the group consisting of metal oxides, precursors thereof, and combinations thereof, prior to said step of sintering, said sintered abrasive grain comprising a sintered core and a metal oxide coating.
Claim 14
Dependent Claim
166 words
A method according to claim 2 wherein said dispersion further comprises a metal oxide precursor of an oxide selected from the group consisting of yttria, magnesium oxide, and a rare earth oxide; wherein said metal oxide precursor is present in an amount sufficient to provide abrasive grain of step (c) with at least about 0.5% by weight of at least one metal oxide, said metal oxide being present as one of a metal oxide, a metal oxide reaction product, or a combination thereof, (i) said rare earth oxide being selected from the group consisting of oxides of: praseodymium, samarium, ytterbium, neodymium, lanthanum, gadolinium, cerium, dysprosium, erbium, and mixtures thereof, and (ii) each of said yttria, magnesium oxide, and rare earth oxide, if present in said abrasive grain of step (c), being present up to about 10% by weight; and wherein said abrasive grain of step (c) comprises about 70 to about 95 percent by weight alumina and about 0.1 to about 15 percent by weight zirconia.
Claim 15
Dependent Claim
23 words
The method according to claim 1 wherein said abrasive grain of step (c) comprises about 70 to about 97 percent by weight alumina.
Claim 16
Dependent Claim
23 words
The method according to claim 1 wherein said abrasive grain of step (c) comprises about 70 to about 95 percent by weight alumina.
Claim 17
Dependent Claim
60 words
A sintered abrasive grain comprising alpha alumina, including alpha alumina domains comprised of alpha alumina crystallites, and about 0.05 to about 1 micrometer particles of zirconia, said particles of zirconia being substantially uniformly distributed throughout said abrasive grain, and a majority of said zirconia particles in said alpha alumina domains being randomly and uniformly distributed between said alpha alumina crystallites.
Claim 18
Dependent Claim
60 words
A sintered abrasive grain comprising alpha alumina, including alpha alumina domains comprised of alpha alumina crystallites, and about 0.05 to about 1 micrometer particles of zirconia, said particles of zirconia being substantially uniformly distributed throughout said abrasive grain, and a majority of said zirconia particles in said alpha alumina domains being randomly and uniformly distributed between said alpha alumina crystallites.
Claim 19
Dependent Claim
48 words
An abrasive grain according to claim 16 further comprising about 0.5 to about percent by weight yttria and about 0.3 to about 1.5 percent by weight magnesium oxide therein, said yttria being present as yttria reaction product, and said magnesium oxide being present as magnesium oxide reaction product.
Claim 20
Dependent Claim
140 words
An abrasive grain according to claim 16 comprising: (a) about 70 to about 95% by weight alumina; said alumina being present as one of said alpha alumina or said alpha alumina and an alumina reaction product; (b) about 0.1 to about 15% by weight zirconia, said zirconia present being as one of said zirconia particles or zirconia particles and a zirconia reaction product; (c) about 0.5 to about 1.5% by weight magnesium oxide, said magnesium oxide being present as a magnesium oxide reaction product; and (d) about 0.1 to about 5% by weight of rare earth oxide selected from the group consisting of oxides of: praseodymium, samarium, ytterbium, neodymium, lanthanum, gadolinium, cerium, dysprosium, erbium and mixtures thereof, said rare earth oxide being present as one of a rare earth oxide, a rare earth oxide reaction product, or a combination thereof.
Claim 21
Dependent Claim
25 words
An abrasive grain according to claim 18 including about 0.5 to about 10% by weight yttria, said yttria being present as a yttria reaction product.
Claim 22
Dependent Claim
24 words
An abrasive grain comprising a core and a surface coating of metal oxide thereon, said core being said abrasive grain according to claim 19.
Claim 23
Dependent Claim
25 words
An abrasive article including: (a) a binder; and (b) a plurality of abrasive grain according to claim 16 secured within said article by said binder.
Claim 24
Dependent Claim
15 words
An abrasive article according to claim 21 wherein said abrasive article is a grinding wheel.
Claim 25
Dependent Claim
15 words
An abrasive article according to claim 21 wherein said abrasive article is a cutoff wheel.
Claim 26
Dependent Claim
16 words
An abrasive article according to claim 21 wherein said abrasive article is a nonwoven abrasive product.
Claim 27
Dependent Claim
35 words
A coated abrasive article comprising: (a) a backing having a major surface; and (b) an abrasive layer comprising abrasive grain according to claim 21 secured to said major surface of said backing by a binder.
References Cited (Backward Citations)
US3454385A
Cited
US3891408A
Cited
US4126429A
Cited
US4331627A
Cited
US4314827A
Cited
US4518397A
Cited
US4333859A
Cited
US4457767A
Cited
US5204300A
Cited
EP0256182A1
Cited
US4744802A
Cited
EP0236507A1
Cited
US4770671A
Cited
US5259147A
Cited
US4829031A
Cited
US4960441A
Cited
US5164348A
Cited
EP0293163A2
Cited
EP0293164B1
Cited
US5185299A
Cited
US4881851A
Cited
EP0368837B1
Cited
EP0408771B1
Cited
US5215551A
Cited
US4952536A
Cited
US5002911A
Cited
US5194072A
Cited
US5076815A
Cited
US4997461A
Cited
EP0435677A2
Cited
EP0441640A2
Cited
WO1992001646A2
Cited
JPH0497942A
Cited
AT394850B
Cited
US5131926A
Cited
US5201916A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-03 | 2000-03-04 | 2000-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-03 | 2004-03-04 | 2004-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-03 | 2008-03-04 | 2008-09-03 | $7700.00 | Window Closed / Lapsed |