Method of forming a pattern of silylated planarizing photoresist
Assignee: Sharp Corp
•
Filing: 1995-05-09
•
Granted: 1996-08-13
•
Expires: 2015-05-09
Abstract
Abstract The invention provides an improved planarizing methodology for forming high-definition photolithographic masks of the type used in semiconductor integrated circuit manufacturing. A layer of planarizing photoresist is first applied to the surface topography of a semiconductor wafer substrate and shallow-penetrating radiation is then used to irradiate the surface of the photoresist. The radiation creates a blanket irradiated layer, adjacent the surface of the resist, consisting of an acid and resist in solution. The acid/resist solution readily absorbs and incorporates silicon. Next, the wafer is exposed to a silicon-containing compound, or softbaked in a silicon-containing environment, creating a silicon-enriched region adjacent the surface of the photoresist. An imaging resist is then applied to the resist, and a photolithographic mask is formed in the imaging resist. An etching step transfers the mask to the silicon-enriched region of the photoresist. The remaining areas of the silicon-enriched layer are exposed to an oxygen plasma which converts the silicon-enriched areas to silicon dioxide. The method of the invention produced high-definition mask lines and avoids the defect densities associated with conventional tri-layer processing using SOG.
Inventors
- 👤 Tatsuo Nakato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:50
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/075; G03F7/0752; G03F7/09; G03F7/094; G03F7/16; G03F7/168; Y; Y10; Y10T; Y10T428/00; Y10T428/31; Y10T428/31504; Y10T428/31652; Y10T428/31663; Y10T428/31667
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
190 words
A method of forming a mask pattern of silicon dioxide on the surface of a layer of photoresist, the method comprising the steps of: (a) forming a uniform, unpatterned, silicon-reactive region in a surface region of the photoresist by irradiating the surface of the photoresist with uniform, unpatterned, radiation that reaches the surface without passing through a mask and which penetrates not more than 3,000 Å below the surface of the photoresist; (b) softbaking the irradiated photoresist in a silicon-containing environment to convert said silicon-reactive region to a silicon e enriched region which extends below the surface of the photoresist to a depth determined by the penetration of the radiation in step (a); (c) applying a second photoresist layer over the softbaked irradiated photoresist from step (b); (d) forming a desired photolithographic pattern of imaging resist on the surface of the second photoresist layer (e) forming said photolithographic pattern in said siliconenriched region of the photoresist using the imaging resist as a mask; and (f) etching the resultant structure using an oxygen plasma to remove the imaging resist and convert the remaining portions of said silicon-enriched region to silicon dioxide.
Claim 2
Independent Claim
190 words
A method of forming a mask pattern of silicon dioxide on the surface of a layer of photoresist, the method comprising the steps of: (a) forming a uniform, unpatterned, silicon-reactive region in a surface region of the photoresist by irradiating the surface of the photoresist with uniform, unpatterned, radiation that reaches the surface without passing through a mask and which penetrates not more than 3,000 Å below the surface of the photoresist; (b) softbaking the irradiated photoresist in a silicon-containing environment to convert said silicon-reactive region to a silicon e enriched region which extends below the surface of the photoresist to a depth determined by the penetration of the radiation in step (a); (c) applying a second photoresist layer over the softbaked irradiated photoresist from step (b); (d) forming a desired photolithographic pattern of imaging resist on the surface of the second photoresist layer (e) forming said photolithographic pattern in said siliconenriched region of the photoresist using the imaging resist as a mask; and (f) etching the resultant structure using an oxygen plasma to remove the imaging resist and convert the remaining portions of said silicon-enriched region to silicon dioxide.
Claim 3
Dependent Claim
26 words
A method as in claim 1 in which the radiation used in step (a) has a wavelength in the range of approximately 200- to 320- nanometers.
Claim 4
Dependent Claim
211 words
A photolithography method for creating high-resolution patterns on a substrate, the method comprising the steps off: (a) applying a planarizing photoresist composition to the surface topography of the substrate; (b) forming a uniform, unpatterned, silicon-reactive region in a surface region of the planarizing photoresist by irradiating the surface of the photoresist with radiation that penetrates not more than 3,000 Å below the surface of the photoresist, wherein the radiation reaches the surface without passing through a mask to create a silicon-reactive surface layer in the planarizing photoresist extending over the substrate; (c) softbaking the irradiated planarizing photoresist in a silicon-containing environment to produce a silicon-enriched surface layer in the planarizing photoresist extending over the substrate; (d) coating the planarizing photoresist with a layer of imaging resist extending over the substrate; (e) forming a first photolithographic pattern in the imaging resist layer; (f) employing photolithographic techniques to etch the planarizing photoresist in selected areas defined by said first photolithographic pattern formed in the imaging resist to remove the silicon-enriched layer in said selected areas; and (g) exposing the remainder of the planarizing photoresist to an oxidizing agent to convert the silicon-enriched surface layer to SiO 2 , thereby producing a desired pattern of SiO 2 on the surface of the planarizing photoresist.
Claim 5
Dependent Claim
211 words
A photolithography method for creating high-resolution patterns on a substrate, the method comprising the steps off: (a) applying a planarizing photoresist composition to the surface topography of the substrate; (b) forming a uniform, unpatterned, silicon-reactive region in a surface region of the planarizing photoresist by irradiating the surface of the photoresist with radiation that penetrates not more than 3,000 Å below the surface of the photoresist, wherein the radiation reaches the surface without passing through a mask to create a silicon-reactive surface layer in the planarizing photoresist extending over the substrate; (c) softbaking the irradiated planarizing photoresist in a silicon-containing environment to produce a silicon-enriched surface layer in the planarizing photoresist extending over the substrate; (d) coating the planarizing photoresist with a layer of imaging resist extending over the substrate; (e) forming a first photolithographic pattern in the imaging resist layer; (f) employing photolithographic techniques to etch the planarizing photoresist in selected areas defined by said first photolithographic pattern formed in the imaging resist to remove the silicon-enriched layer in said selected areas; and (g) exposing the remainder of the planarizing photoresist to an oxidizing agent to convert the silicon-enriched surface layer to SiO 2 , thereby producing a desired pattern of SiO 2 on the surface of the planarizing photoresist.
Claim 6
Dependent Claim
30 words
A photolithography method as in claim 3 in which the planarizing photoresist composition includes one or more polymers selected from the group consisting of a novolac, polymethylmethacrylate, polydimethylglutarimide, and polyhydroxystyrene.
Claim 7
Dependent Claim
16 words
A photolithography method as in claim 3 in which step (g) also removes the imaging resist.
Claim 8
Dependent Claim
71 words
A photolithography method as in claim 3 in which step (g) includes etching the planarizing photoresist in said selected areas using an oxidizing plasma to convert the silicon-enriched surface layer to SiO 2 , permitting the SiO 2 to act as a mask for etching the planarizing photoresist, and causing the oxidizing plasma to etch the remaining planarizing photoresist in said selected areas to expose the surface topography of the substrate.
Claim 9
Dependent Claim
27 words
A photolithography method as in claim 3 in which the radiation used in step (b) has a wavelength in the range of approximately 200- to 320- nanometers.
Claim 10
Dependent Claim
32 words
A photolithography method as in claim 3 in which step (c) further includes softbaking the planarizing photoresist in the presence of a liquid or gaseous organosilane to produce said silicon-enriched surface layer.
Claim 11
Independent Claim
225 words
A method of forming a pattern of silylated planarizing resist extending over the surface topography of an integrated circuit substrate to serve as a photolithographic mask, the method comprising the steps of: (a) applying a first photoresist layer over the surface topography of the substrate; (b) irradiating the surface of the first photoresist layer with unpatterned radiation which reaches the surface without passing through a mask, the radiation having a wavelength which penetrates not more than 3,000 Å below the surface of the photoresist to produce a shallow, uniform surface layer of acid within the photoresist in a plane adjacent the surface of the photoresist; (c) exposing the irradiated first photoresist layer to a silicon-containing environment, whereby the silicon reacts with the acid in said shallow, uniform surface layer to produce a silicon-enriched surface layer within the first photoresist layer; (d) applying a second photoresist layer over said first photoresist layer; (e) forming a photolithographic pattern in the second photoresist layer; (f) using the second photoresist layer as a mask, removing said silicon-enriched surface layer within the first photoresist layer in the regions corresponding to said photolithographic pattern; and (g) exposing the resultant structure to an oxidizing agent to convert the unremoved regions of the silicon-enriched surface layer within the first photoresist layer to silicon dioxide, thereby reproducing said photolithographic pattern in the silicon dioxide.
Claim 12
Independent Claim
225 words
A method of forming a pattern of silylated planarizing resist extending over the surface topography of an integrated circuit substrate to serve as a photolithographic mask, the method comprising the steps of: (a) applying a first photoresist layer over the surface topography of the substrate; (b) irradiating the surface of the first photoresist layer with unpatterned radiation which reaches the surface without passing through a mask, the radiation having a wavelength which penetrates not more than 3,000 Å below the surface of the photoresist to produce a shallow, uniform surface layer of acid within the photoresist in a plane adjacent the surface of the photoresist; (c) exposing the irradiated first photoresist layer to a silicon-containing environment, whereby the silicon reacts with the acid in said shallow, uniform surface layer to produce a silicon-enriched surface layer within the first photoresist layer; (d) applying a second photoresist layer over said first photoresist layer; (e) forming a photolithographic pattern in the second photoresist layer; (f) using the second photoresist layer as a mask, removing said silicon-enriched surface layer within the first photoresist layer in the regions corresponding to said photolithographic pattern; and (g) exposing the resultant structure to an oxidizing agent to convert the unremoved regions of the silicon-enriched surface layer within the first photoresist layer to silicon dioxide, thereby reproducing said photolithographic pattern in the silicon dioxide.
Claim 13
Dependent Claim
32 words
A method as in claim 9 in which step (f) includes removing a majority of the first photoresist layer in the regions corresponding to said photolithographic pattern, including said silicon-enriched surface layer.
Claim 14
Dependent Claim
26 words
A method as in claim 9 in which the radiation used in step (b) has a wavelength in the range of approximately 200- to 320- nanometers.
Claim 15
Dependent Claim
33 words
A method as in claim 9 in which the first photoresist layer is a composition which includes one or more polymers selected from the group consisting of a novolac, polymethylmethacrylate, polydimethylglutarimide, and polyhydroxystyrene.
Claim 16
Dependent Claim
59 words
A method as in claim 9 in which step (g) includes etching the resultant structure using an oxygen plasma, with the silicon dioxide acting as a mask, to remove the second photoresist layer and to remove the remaining portions of the first photoresist layer, thereby exposing the topography of the substrate in the regions corresponding to said photolithographic pattern.
Claim 17
Dependent Claim
16 words
A method as in claim 9 in which step (g) also removes the second photoresist layer.
Claim 18
Dependent Claim
32 words
A method as in claim 9 in which step (c) further includes softbaking the first photoresist layer in the presence of a liquid or gaseous organosilane to produce said silicon-enriched surface layer.
References Cited (Backward Citations)
US4810601A
Cited
US4963463A
Cited
US4882008A
Cited
US5108875A
Cited
US4957588A
Cited
US5024876A
Cited
US5286607A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-08-13 | 2000-02-12 | 2000-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-08-13 | 2004-02-12 | 2004-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-08-13 | 2008-02-12 | 2008-08-13 | $7700.00 | Window Closed / Lapsed |