Process for preparing a non-conductive substrate for electroplating
Assignee: MacDermid Acumen Inc
•
Filing: 1995-02-10
•
Granted: 1996-07-16
•
Expires: 2015-02-10
Abstract
Abstract The modification of carbon particles is disclosed for achieving enhanced plating upon a non-conductive surface which has been previously treated with said modified carbon particles. The invention is particularly useful in plating through holes of printed circuit boards.
Inventors
- 👤 Donald Ferrier
- 👤 Rosa Martinez
- 👤 Eric Yakobson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 00:06
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/54; H; H05; H05K; H05K3/00; H05K3/40; H05K3/42; H05K3/423; H05K3/424; H05K2201/00; H05K2201/03; H05K2201/032; H05K2201/0323; H05K3/425; H05K3/427
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
148 words
A process for electroplating a conductive metal layer onto the surface of a non-conductive material comprising the following steps: (a) contacting said non-conductive surface with a liquid carbon dispersion comprising: (1) carbon particles which have been contacted with an aqueous metal containing bath such that metallic species are either adsorbed or reduced onto the surface of said carbon particles, said carbon particles having an average particle diameter of less than 3.0 microns in said dispersion; (2) a dispersant; (3) a liquid dispersing medium; (b) separating substantially all of the dispersing medium from said carbon particles, where said particles are deposited on said non-conductive surface in a substantially continuous layer; and (c) electroplating a conductive metal layer over the deposited carbon layer and said non-conductive surface; and wherein said metal containing bath comprises a metal selected from the group consisting of colloidal metallic species, metal ions, and combinations thereof.
Claim 2
Dependent Claim
148 words
A process for electroplating a conductive metal layer onto the surface of a non-conductive material comprising the following steps: (a) contacting said non-conductive surface with a liquid carbon dispersion comprising: (1) carbon particles which have been contacted with an aqueous metal containing bath such that metallic species are either adsorbed or reduced onto the surface of said carbon particles, said carbon particles having an average particle diameter of less than 3.0 microns in said dispersion; (2) a dispersant; (3) a liquid dispersing medium; (b) separating substantially all of the dispersing medium from said carbon particles, where said particles are deposited on said non-conductive surface in a substantially continuous layer; and (c) electroplating a conductive metal layer over the deposited carbon layer and said non-conductive surface; and wherein said metal containing bath comprises a metal selected from the group consisting of colloidal metallic species, metal ions, and combinations thereof.
Claim 3
Dependent Claim
27 words
A process according to claim 1 wherein the metallic species are selected from the group consisting of palladium, gold, silver, platinum, nickel, copper, cobalt and mixtures thereof.
Claim 4
Dependent Claim
13 words
A process according to claim 2 wherein the bath is a plating activator.
Claim 5
Dependent Claim
27 words
A process according to claim 2 wherein the bath is selected from the group consisting of metal ions in solution and colloidal metallic species in aqueous dispersion.
Claim 6
Dependent Claim
43 words
A process according to claim 3 wherein the bath is selected from the group consisting of ionic palladium containing activators, colloidal palladium activators, colloidal palladium-tin activators, ionic gold containing activators, ionic copper containing activators, ionic rhodium containing activators and ionic ruthenium containing activators.
Claim 7
Dependent Claim
42 words
A process according to any one of claims 1 through 5 wherein the plating requires less time to achieve substantially complete coverage of the non-conductive surface as compared to plating with carbon which has not been contacted with the metal containing bath.
Claim 8
Dependent Claim
41 words
A process according to any one of claims 1 through 5 wherein the process plates larger areas of non-conductive surface under otherwise similar conditions as compared to a process utilizing carbon which has not been contacted with the metal containing bath.
Claim 9
Dependent Claim
31 words
A process according to any one of claims 1 through 5 wherein the carbon particles are selected from the group consisting of carbon black, graphite, intermediate carbon structures and mixtures thereof.
Claim 10
Dependent Claim
117 words
A process for electroplating a conductive metal layer onto the surface of a non-conductive material comprising the following steps: (a) contacting said non-conductive surface with a liquid carbon dispersion comprising: (1) carbon particles which have been contacted with a specie selected from the group consisting of dyes, indicators and mixtures thereof, said carbon particles having an average particle diameter of less than 3.0 microns in said dispersion; (2) a dispersant; (3) a liquid dispersing medium; (b) separating substantially all of the dispersing medium from said carbon particles, where said particles are deposited on said non-conductive surface in a substantially continuous layer; and (c) electroplating a conductive metal layer over the deposited carbon layer and said non-conductive surface.
Claim 11
Dependent Claim
117 words
A process for electroplating a conductive metal layer onto the surface of a non-conductive material comprising the following steps: (a) contacting said non-conductive surface with a liquid carbon dispersion comprising: (1) carbon particles which have been contacted with a specie selected from the group consisting of dyes, indicators and mixtures thereof, said carbon particles having an average particle diameter of less than 3.0 microns in said dispersion; (2) a dispersant; (3) a liquid dispersing medium; (b) separating substantially all of the dispersing medium from said carbon particles, where said particles are deposited on said non-conductive surface in a substantially continuous layer; and (c) electroplating a conductive metal layer over the deposited carbon layer and said non-conductive surface.
Claim 12
Dependent Claim
28 words
A process according to claim 9 wherein the specie is selected from the group consisting of methylene blue, methyl red, janus green B, xylene cyanole and mixtures thereof.
Claim 13
Dependent Claim
18 words
A process according to claim 9 wherein the specie contains an aromatic structure and at least one nitrogen.
Claim 14
Dependent Claim
44 words
A process according to any one of claims 9 through 11 wherein the plating requires less time to achieve substantially complete coverage of the non-conductive surface as compared to plating with carbon which has not been contacted with the specie indicated in claim 9.
Claim 15
Dependent Claim
43 words
A process according to any one of claims 9 through 12 wherein the process plates larger areas of non-conductive surface under otherwise similar conditions as compared to a process utilizing carbon which has not been contacted with the specie indicated in claim 9.
Claim 16
Dependent Claim
31 words
A process according to any one of claims 9 through 11 wherein the carbon particles are selected from the group consisting of carbon black, graphite intermediate carbon structures and mixtures thereof.
Claim 17
Dependent Claim
107 words
A process for electroplating a conductive metal layer onto the surface of a non-conductive material comprising the following steps: (a) contacting said non-conductive surface with a liquid carbon dispersion comprising: (1) carbon particles which have been contacted with an oxidant, said carbon particles having an average particle diameter of less than 3.0 microns in said dispersion; (2) a dispersant; (3) an aqueous liquid dispersing medium; (b) separating substantially all of the dispersing medium from said carbon particles, where said particles are deposited on said non-conductive surface in a substantially continuous layer; and (c) electroplating a conductive metal layer over the deposited carbon layer and said non-conductive surface.
Claim 18
Dependent Claim
107 words
A process for electroplating a conductive metal layer onto the surface of a non-conductive material comprising the following steps: (a) contacting said non-conductive surface with a liquid carbon dispersion comprising: (1) carbon particles which have been contacted with an oxidant, said carbon particles having an average particle diameter of less than 3.0 microns in said dispersion; (2) a dispersant; (3) an aqueous liquid dispersing medium; (b) separating substantially all of the dispersing medium from said carbon particles, where said particles are deposited on said non-conductive surface in a substantially continuous layer; and (c) electroplating a conductive metal layer over the deposited carbon layer and said non-conductive surface.
Claim 19
Dependent Claim
23 words
A process according to claim 15 wherein the oxidant is selected from the group consisting of nitric acid, hydrogen peroxide, persulfates and permanganates.
Claim 20
Dependent Claim
40 words
A process according to any one of claims 15 through 16 wherein the plating requires less time to achieve substantially complete coverage of the non-conductive surface as compared to plating with carbon which has not been contacted with an oxidant.
Claim 21
Dependent Claim
40 words
A process according to any one of claims 15 through 16 wherein the process plates larger areas of non-conductive surface under otherwise similar conditions as compared to a process utilizing carbon which has not been contacted with an oxidant. PG,37
References Cited (Backward Citations)
US2872391A
Cited
US4041347A
Cited
US4379762A
Cited
US4434064A
Cited
US4888134A
Cited
US4964959A
Cited
US5234627A
Cited
US5389270A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-07-16 | 2000-01-15 | 2000-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-07-16 | 2004-01-15 | 2004-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-07-16 | 2008-01-15 | 2008-07-16 | $7700.00 | Window Closed / Lapsed |