Maskless method for formation of a field implant channel stop region
Assignee: United Microelectronics Corp
•
Filing: 1994-09-26
•
Granted: 1996-05-21
•
Expires: 2014-09-26
Abstract
Abstract This invention provides a method of forming a field implant channel stop region and a device using a field implant channel stop region to improve isolation between devices in integrated circuits using field effect transistors. The field implant channel stop region is formed without the use of an extra mask or extra masking steps by means of either a large angle tilted ion implant beam or a higher energy normally directed ion implant beam. The field implant channel stop region is formed with the mask used to form the light doped drain region in place. The field implant channel stop region forms a local increase in the doping level in the device well thereby forming the channel stop region.
Inventors
- 👤 Chih-Hung Lin
- 👤 Joe Ko
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:17
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/10; H10W10/13
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
363 words
A method of forming a field implant channel stop region, comprising the steps of: providing a semiconductor substrate with an isolation well formed therein; forming a field oxide isolation region in said semiconductor substrate; forming a threshold voltage adjustment region in said semiconductor substrate by means of a first ion implantation; forming a gate dielectric layer over said semiconductor substrate; forming a conducting gate electrode layer over said gate dielectric layer; forming a surface dielectric layer over said conducting gate electrode layer; forming a gate electrode pattern in said conducting gate electrode layer, said gate dielectric layer, and said surface dielectric layer; forming a second pattern in said conducting gate electrode layer and said surface dielectric layer; forming a lightly doped drain photoresist mask on said semiconductor substrate; forming a field implant channel stop region in said semiconductor substrate by means of a third ion implantation beam wherein said field implant channel step region extends continuously from below the entirety of said gate electrode pattern to below a part of said field oxide isolation region and the distance between that part of said field implant channel stop region located below said gate electrode pattern and the surface of said semiconductor substrate is between about 0.2 and 0.5 microns; forming lightly doped drain regions in said semiconductor substrate using a second ion implantation; stripping said surface dielectric layer and said lightly doped drain photoresist mask; forming source/drain regions in said semiconductor substrate above a part of said field implant channel stop region wherein said field implant channel stop region of located continuously below the entirety of said source/drain regions, below the entirety of said gate electrode pattern, and below a part of said field oxide region and the distance between that part of said field implant channel stop region located below said source/drain regions and the surface of said semiconductor substrate is between about 0.4 and 0.8 microns; forming an insulating dielectric layer with contact openings on said semiconductor substrate; forming metal contacts in said contact openings in said insulating dielectric layer; forming a patterned metal conductor electrode layer on said insulating dielectric layer; and forming a passivation layer over said insulating dielectric layer.
Claim 2
Independent Claim
363 words
A method of forming a field implant channel stop region, comprising the steps of: providing a semiconductor substrate with an isolation well formed therein; forming a field oxide isolation region in said semiconductor substrate; forming a threshold voltage adjustment region in said semiconductor substrate by means of a first ion implantation; forming a gate dielectric layer over said semiconductor substrate; forming a conducting gate electrode layer over said gate dielectric layer; forming a surface dielectric layer over said conducting gate electrode layer; forming a gate electrode pattern in said conducting gate electrode layer, said gate dielectric layer, and said surface dielectric layer; forming a second pattern in said conducting gate electrode layer and said surface dielectric layer; forming a lightly doped drain photoresist mask on said semiconductor substrate; forming a field implant channel stop region in said semiconductor substrate by means of a third ion implantation beam wherein said field implant channel step region extends continuously from below the entirety of said gate electrode pattern to below a part of said field oxide isolation region and the distance between that part of said field implant channel stop region located below said gate electrode pattern and the surface of said semiconductor substrate is between about 0.2 and 0.5 microns; forming lightly doped drain regions in said semiconductor substrate using a second ion implantation; stripping said surface dielectric layer and said lightly doped drain photoresist mask; forming source/drain regions in said semiconductor substrate above a part of said field implant channel stop region wherein said field implant channel stop region of located continuously below the entirety of said source/drain regions, below the entirety of said gate electrode pattern, and below a part of said field oxide region and the distance between that part of said field implant channel stop region located below said source/drain regions and the surface of said semiconductor substrate is between about 0.4 and 0.8 microns; forming an insulating dielectric layer with contact openings on said semiconductor substrate; forming metal contacts in said contact openings in said insulating dielectric layer; forming a patterned metal conductor electrode layer on said insulating dielectric layer; and forming a passivation layer over said insulating dielectric layer.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein said isolation well is of a P - type conductivity.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said gate dielectric layer has a thickness of between about 60 and 250 Angstroms.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said conducting gate electrode layer is polysilicon with a thickness of between about 2000 and 5000 Angstroms.
Claim 6
Dependent Claim
23 words
The method of claim 1 wherein said surface dielectric layer is silicon nitride with a thickness of between about 1000 and 3000 Angstroms,
Claim 7
Dependent Claim
28 words
The method of claim 1 wherein said third ion implantation beam forms an angle of between about 30° and 60° with a line perpendicular to said semiconductor substrate.
Claim 8
Dependent Claim
31 words
The method of claim 1 wherein said third ion implantation beam is B 11 with between about 5×10 12 and 2.5×10 13 ions/cm 2 at between about 150 and 250 keV.
Claim 9
Dependent Claim
34 words
The method of claim 1 wherein said second ion implantation uses an ion beam of P 31 with between about 1×10 13 and 1×10 14 ions/cm 2 at between about 30 and 80 keV,
Claim 10
Dependent Claim
15 words
The method of claim 1 wherein said field oxide isolation region is SiO 2 .
Claim 11
Dependent Claim
71 words
The method of claim 1 wherein said field implant channel stop region is formed after forming said field oxide isolation region; after forming said gate electrode pattern in said conducting gate electrode layer, said gate dielectric layer, and said surface dielectric layer; after forming said second pattern in said conducting gate electrode layer and said surface dielectric layer; after forming said lightly doped drain photoresist mask; and without using additional masks.
Claim 12
Independent Claim
339 words
A method of forming a field implant channel stop region, comprising the steps of: providing a semiconductor substrate with an isolation well formed therein; forming a field oxide isolation region in said semiconductor substrate; forming a threshold voltage adjustment region in said semiconductor substrate by means of a first ion implantation; forming a gate dielectric layer over said semiconductor substrate; forming a conducting gate electrode layer over said gate dielectric layer; forming a gate electrode pattern in said conducting gate electrode layer and said gate dielectric layer; forming a second pattern in said conducting gate electrode layer; forming a lightly doped drain photoresist mask on said semiconductor substrate; forming a field implant channel stop region in said semiconductor substrate by means of a third ion implantation wherein said field implant channel stop region extends continuously from below the entirety of said gate electrode pattern to below a part of said field oxide isolation region and the distance between that part of said field implant channel stop region located below said gate electrode pattern and the surface of said semiconductor substrate is between about 0.2 and 0.5 microns; forming lightly doped drain regions in said semiconductor substrate by means of a second ion implantation; stripping said lightly doped drain photoresist mask; forming source/drain regions in said semiconductor substrate above a part of said field implant channel stop region wherein said field implant channel stop region is located continuously below the entirety of said source/drain regions, below the entirety of said gate electrode pattern, and below a part of said field oxide region and the distance between that part of said field implant channel stop region located below said source/drain regions and the surface of said semiconductor substrate is between about 0.4 and 0.8 microns; forming an insulating dielectric layer with contact openings on said semiconductor substrate; forming metal contacts in said contact openings in said insulating dielectric layer; forming a patterned metal conductor electrode player on said insulating dielectric layer; and forming a passivation layer over said insulating dielectric layer.
Claim 13
Independent Claim
339 words
A method of forming a field implant channel stop region, comprising the steps of: providing a semiconductor substrate with an isolation well formed therein; forming a field oxide isolation region in said semiconductor substrate; forming a threshold voltage adjustment region in said semiconductor substrate by means of a first ion implantation; forming a gate dielectric layer over said semiconductor substrate; forming a conducting gate electrode layer over said gate dielectric layer; forming a gate electrode pattern in said conducting gate electrode layer and said gate dielectric layer; forming a second pattern in said conducting gate electrode layer; forming a lightly doped drain photoresist mask on said semiconductor substrate; forming a field implant channel stop region in said semiconductor substrate by means of a third ion implantation wherein said field implant channel stop region extends continuously from below the entirety of said gate electrode pattern to below a part of said field oxide isolation region and the distance between that part of said field implant channel stop region located below said gate electrode pattern and the surface of said semiconductor substrate is between about 0.2 and 0.5 microns; forming lightly doped drain regions in said semiconductor substrate by means of a second ion implantation; stripping said lightly doped drain photoresist mask; forming source/drain regions in said semiconductor substrate above a part of said field implant channel stop region wherein said field implant channel stop region is located continuously below the entirety of said source/drain regions, below the entirety of said gate electrode pattern, and below a part of said field oxide region and the distance between that part of said field implant channel stop region located below said source/drain regions and the surface of said semiconductor substrate is between about 0.4 and 0.8 microns; forming an insulating dielectric layer with contact openings on said semiconductor substrate; forming metal contacts in said contact openings in said insulating dielectric layer; forming a patterned metal conductor electrode player on said insulating dielectric layer; and forming a passivation layer over said insulating dielectric layer.
Claim 14
Dependent Claim
16 words
The method of claim 11 wherein said isolation well is of a P - type conductivity.
Claim 15
Dependent Claim
20 words
The method of claim 11 wherein said gate dielectric layer has a thickness of between about 60 and 250 Angstroms.
Claim 16
Dependent Claim
23 words
The method of claim 11 wherein said conducting gate electrode layer is polysilicon with a thickness of between about 2000 and 5000 Angstroms.
Claim 17
Dependent Claim
34 words
The method of claim 11 wherein said third ion implantation uses an ion beam of B 11 with between about 5×10 12 and 2.5×10 13 ions/cm 2 at between about 200 and 400 keV,
Claim 18
Dependent Claim
34 words
The method of claim 11 wherein said second ion implantation uses an ion beam of P 31 with between about 1×10 13 and 1×10 14 ions/cm 2 at between about 30 and 80 keV,
Claim 19
Dependent Claim
15 words
The method of claim 11 wherein said field oxide isolation region is SiO 2 .
Claim 20
Dependent Claim
62 words
The method of claim 11 wherein said field implant channel stop region is formed after forming said field oxide isolation region, after forming said gate electrode pattern in said conducting gate electrode layer and said gate dielectric layer, after forming said second pattern in said conducting gate electrode layer, after forming said lightly doped drain photoresist mask, and without using additional masks.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-05-21 | 1999-11-20 | 2000-05-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-05-21 | 2003-11-20 | 2004-05-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-05-21 | 2007-11-20 | 2008-05-21 | $7700.00 | Window Closed / Lapsed |