Modified hydrogen silsesquioxane resin
Assignee: Dow Silicones Corp
•
Filing: 1995-05-12
•
Granted: 1996-05-14
•
Expires: 2015-05-12
Abstract
Abstract Disclosed is a novel resin of the structure (HSiO 1 .5) x (R 1 R 2 R 3 SiO 0 .5) y , wherein R 1 , R 2 , and R 3 are independently selected from hydrogen, alkyls and aryls, x is 0.25 to 0.99, y is 0.01 to 0.75 and x+y=1.0. Also disclosed is a method for making these resins.
Inventors
- 👤 Gregg A. Zank
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:00
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/04; C08G77/06; C08G77/10; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/571; C08G77/12
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
120 words
A method for modifying hydrogen silsesquioxane resin comprising: refluxing a mixture comprising 1 part by weight hydrogen silsesquioxane resin of the structure HSi(OH) x (X) y O z/2 , in which each X is a hydrolyzable substituent, x=0-2, y=0-2, z=1-3, x+y+z=3, between 0.1 and 10 parts by weight of an endcapping agent of the structure (R 1 R 2 R 3 Si) 2 O, wherein R 1 , R 2 , and R 3 are independently selected from hydrogen, alkyls, alkenyls or aryls, between 0.0001 and 0.05 parts by weight of an acid and between 0.01 and 0.5 parts by weight water, for a time sufficient to modify the hydrogen silsesquioxane resin; cooling the reaction mixture; and recovering the resin.
Claim 2
Independent Claim
120 words
A method for modifying hydrogen silsesquioxane resin comprising: refluxing a mixture comprising 1 part by weight hydrogen silsesquioxane resin of the structure HSi(OH) x (X) y O z/2 , in which each X is a hydrolyzable substituent, x=0-2, y=0-2, z=1-3, x+y+z=3, between 0.1 and 10 parts by weight of an endcapping agent of the structure (R 1 R 2 R 3 Si) 2 O, wherein R 1 , R 2 , and R 3 are independently selected from hydrogen, alkyls, alkenyls or aryls, between 0.0001 and 0.05 parts by weight of an acid and between 0.01 and 0.5 parts by weight water, for a time sufficient to modify the hydrogen silsesquioxane resin; cooling the reaction mixture; and recovering the resin.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein X is selected from the group consisting of Cl and alkoxy.
Claim 4
Dependent Claim
26 words
The method of claim 1 wherein R 1 , R 2 , and R 3 are independently selected from the group consisting of hydrogen and methyl.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein the endcapping agent is selected from the group consisting of tetramethyldisiloxane and hexamethyldisiloxane.
Claim 6
Dependent Claim
43 words
The method of claim 1 wherein the hydrogen silsesquioxane resin is diluted in a solvent selected from the group consisting of aromatic hydrocarbons, alkanes, ketones, esters, ethers and volatile polysiloxanes at a concentration in the range of between 0.1 and 50 weight %.
Claim 7
Dependent Claim
11 words
The method of claim 1 wherein the acid is trifluoroacetic acid.
Claim 8
Dependent Claim
16 words
The method of claim 1 wherein the mixture is refluxed for between 1 and 24 hours.
Claim 9
Dependent Claim
18 words
The method of claim 1 wherein the mixture is refluxed at a temperature between 20° and 150° C.
Claim 10
Dependent Claim
52 words
Modified hydrogen silsesquioxane resin of the structure (HSiO 1 .5) x (R 1 R 2 R 3 SiO 0 .5) y , wherein R 1 , R 2 , and R 3 are independently selected from hydrogen, alkyls or aryls, x is 0.25 to 0.99, y is 0.01 to 0.75 and x+y=1.0.
Claim 11
Dependent Claim
52 words
Modified hydrogen silsesquioxane resin of the structure (HSiO 1 .5) x (R 1 R 2 R 3 SiO 0 .5) y , wherein R 1 , R 2 , and R 3 are independently selected from hydrogen, alkyls or aryls, x is 0.25 to 0.99, y is 0.01 to 0.75 and x+y=1.0.
Claim 12
Dependent Claim
37 words
The modified hydrogen silsesquioxane resin of claim 9 wherein R 1 , R 2 , and R 3 are independently selected from hydrogen or methyl, x is 0.5 to 0.99, y is 0.01 to 0.5 and x+y=1.0.
Claim 13
Dependent Claim
35 words
The modified hydrogen silsesquioxane resin of claim 9 having the structure (HSiO 1 .5) x (Me 2 HSiO 0 .5) y , wherein x is 0.5 to 0.99, y is 0.01 to 0.5 and x+y=1.0.
Claim 14
Dependent Claim
21 words
The modified hydrogen silsesquioxane resin of claim 9 having an Mn in the range of between about 500 and about 2500.
References Cited (Backward Citations)
US3615272A
Cited
US4388449A
Cited
JPS6086017A
Cited
US5010159A
Cited
US5210168A
Cited
US5387480A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-05-14 | 1999-11-13 | 2000-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-05-14 | 2003-11-13 | 2004-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-05-14 | 2007-11-13 | 2008-05-14 | $7700.00 | Window Closed / Lapsed |