Method for forming a thin film
Assignee: Tokyo Electron Ltd
•
Filing: 1994-09-14
•
Granted: 1996-04-16
•
Expires: 2014-09-14
Abstract
Abstract In order to decompose TiCl4 to Ti and Cl completely, extremely high energy of more than 400 kcal mol-1 is required. In the method according to the present invention, use of unequilibrium plasma under reduced pressure is noticed, and it is especially noticed that in the plasma generated by resonance phenomenon, there are high energy electrons, which collide and enhance decomposition and reduction. Therefore, itis possible to form a Ti film without such high substrate temperature as 2000 DEG C., and more, to form a Tifilm with good step coverage even in a fine contact hole.
Inventors
- 👤 Takashi Akahori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:42
CPC Classifications
H; H01; H01J; H01J37/00; H01J37/32; H01J37/32009; H01J37/32192; H10; H10P; H10P95/00; C; C23; C23C; C23C16/00; C23C16/02; C23C16/0272; C23C16/0281; C23C16/06; C23C16/08; C23C16/14; C23C16/22; C23C16/30; C23C16/34; C23C16/44; C23C16/50; C23C16/505; C23C16/509; C23C16/511; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H01J2237/00; H01J2237/32; H01J2237/33; H01J2237/332
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
129 words
A method for forming a thin film of Ti on a substrate by a plasma CVD method using an electron cyclotron resonance (ECR) plasma system, comprising the steps of: (a) placing a substrate on a stage in a vacuum chamber of said ECR plasma system; (b) exhausting a gas in said vacuum chamber to reduce gas pressure; (c) supplying an H 2 gas and/or an Ar gas into said vacuum chamber; (d) generating an ECR plasma in said vacuum chamber by introducing a microwave and applying a magnetic flux density; (e) supplying a TiCl 4 gas into said vacuum chamber; (f) depositing a Ti film on said substrate; (g) stopping supplying said TiCl 4 gas into said vacuum chamber; and (h) stopping generating said ECR plasma after step (g).
Claim 2
Independent Claim
129 words
A method for forming a thin film of Ti on a substrate by a plasma CVD method using an electron cyclotron resonance (ECR) plasma system, comprising the steps of: (a) placing a substrate on a stage in a vacuum chamber of said ECR plasma system; (b) exhausting a gas in said vacuum chamber to reduce gas pressure; (c) supplying an H 2 gas and/or an Ar gas into said vacuum chamber; (d) generating an ECR plasma in said vacuum chamber by introducing a microwave and applying a magnetic flux density; (e) supplying a TiCl 4 gas into said vacuum chamber; (f) depositing a Ti film on said substrate; (g) stopping supplying said TiCl 4 gas into said vacuum chamber; and (h) stopping generating said ECR plasma after step (g).
Claim 3
Dependent Claim
32 words
A method of claim 1 wherein said H 2 gas and/or said Ar gas is supplied at a flow rate less than half of a flow rate of said TiCl 4 gas.
Claim 4
Dependent Claim
18 words
A method of claim 1 or 2 wherein a temperature of said substrate is less than 500° C.
Claim 5
Independent Claim
148 words
A method for forming a multi-layer film comprising Ti and TiN on a substrate by a plasma CVD method using an ECR plasma system, comprising the steps of: (a) placing a substrate on a stage in a vacuum chamber of said ECR plasma system; (b) exhausting a gas in said vacuum chamber to reduce gas pressure; (c) supplying an H 2 gas and/or an Ar gas into said vacuum chamber; (d) generating an ECR plasma in said vacuum chamber by introducing a microwave and applying a magnetic flux density; (e) supplying a TiCl 4 gas into said vacuum chamber; (f) depositing a Ti film on said substrate; (g) depositing a TiN film on the Ti deposited substrate by supplying a N 2 gas into said vacuum chamber; (h) stopping supplying said TiCl 4 gas into said vacuum chamber; and (i) stopping generating said ECR plasma after step (h).
Claim 6
Independent Claim
148 words
A method for forming a multi-layer film comprising Ti and TiN on a substrate by a plasma CVD method using an ECR plasma system, comprising the steps of: (a) placing a substrate on a stage in a vacuum chamber of said ECR plasma system; (b) exhausting a gas in said vacuum chamber to reduce gas pressure; (c) supplying an H 2 gas and/or an Ar gas into said vacuum chamber; (d) generating an ECR plasma in said vacuum chamber by introducing a microwave and applying a magnetic flux density; (e) supplying a TiCl 4 gas into said vacuum chamber; (f) depositing a Ti film on said substrate; (g) depositing a TiN film on the Ti deposited substrate by supplying a N 2 gas into said vacuum chamber; (h) stopping supplying said TiCl 4 gas into said vacuum chamber; and (i) stopping generating said ECR plasma after step (h).
Claim 7
Dependent Claim
29 words
A method of claim 4 wherein said N 2 gas is supplied at a flow rate of less than half of a flow rate of said TiCl 4 gas.
Claim 8
Dependent Claim
33 words
A method of claim 4 wherein said H 2 gas and/or said Ar gas is supplied at a flow rate of less than half of a flow rate of said TiCl 4 gas.
Claim 9
Dependent Claim
19 words
A method of claim 4, 5 or 6 wherein a temperature of said substrate is less than 500° C.
Claim 10
Independent Claim
197 words
A method for forming a multi-layer film comprising a Ti and a TiN on a substrate by a plasma CVD method using an ECR plasma system which comprises of vacuum chamber A and vacuum chamber B, the method comprising the steps of: (a) exhausting a gas in two or more vacuum chambers to reduce gas pressure; (b) supplying an H 2 gas and/or an Ar gas into said vacuum chamber A; (c) supplying an H 2 gas and/or an Ar gas and N 2 gas into said vacuum chamber B; (d) generating an ECR plasma in said vacuum chamber A and vacuum chamber B by introducing a microwave and applying a magnetic flux density; (e) supplying a TiCl 4 gas into said vacuum chamber A and vacuum chamber B; (f) placing a substrate on a stage in one of said vacuum chambers of said ECR plasma system; (g) depositing a Ti film on said substrate in said chamber A; (h) transferring the substrate from vacuum chamber A to vacuum chamber B after depositing said Ti film on said substrate in vacuum chamber A; and (i) depositing a TiN film on said substrate in said vacuum chamber B.
Claim 11
Independent Claim
197 words
A method for forming a multi-layer film comprising a Ti and a TiN on a substrate by a plasma CVD method using an ECR plasma system which comprises of vacuum chamber A and vacuum chamber B, the method comprising the steps of: (a) exhausting a gas in two or more vacuum chambers to reduce gas pressure; (b) supplying an H 2 gas and/or an Ar gas into said vacuum chamber A; (c) supplying an H 2 gas and/or an Ar gas and N 2 gas into said vacuum chamber B; (d) generating an ECR plasma in said vacuum chamber A and vacuum chamber B by introducing a microwave and applying a magnetic flux density; (e) supplying a TiCl 4 gas into said vacuum chamber A and vacuum chamber B; (f) placing a substrate on a stage in one of said vacuum chambers of said ECR plasma system; (g) depositing a Ti film on said substrate in said chamber A; (h) transferring the substrate from vacuum chamber A to vacuum chamber B after depositing said Ti film on said substrate in vacuum chamber A; and (i) depositing a TiN film on said substrate in said vacuum chamber B.
Claim 12
Dependent Claim
29 words
A method of claim 8 wherein said N 2 gas is supplied at a flow rate of less than half of a flow rate of said TiCl 4 gas.
Claim 13
Dependent Claim
33 words
A method of claim 8 wherein said H 2 gas and/or said Ar gas is supplied at a flow rate of less than half of a flow rate of said TiCl 4 gas.
Claim 14
Dependent Claim
19 words
A method of claim 8, 9 or 10 wherein a temperature of said substrate is less than 500° C.
Claim 15
Dependent Claim
32 words
A method of claim 8, 9 or 10 further comprising the step of applying a heat treatment before depositing a TiN film on said Ti deposited substrate in said vacuum chamber B.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-04-16 | 1999-10-16 | 2000-04-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-04-16 | 2003-10-16 | 2004-04-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-04-16 | 2007-10-16 | 2008-04-16 | $7700.00 | Window Closed / Lapsed |