US5500200A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fibrils
Assignee: Hyperion Catalysis International Inc
•
Filing: 1995-06-07
•
Granted: 1996-03-19
•
Expires: 2015-06-07
Abstract
Abstract This invention relates to fibrils. It more particularly refers to carbon/graphite fibrils and to an improved process for producing such. Carbon fibrils as used herein means graphitic fibrils having high surface area, high Young's modulus of elasticity and high tensile strength which are grown catalytically from available sources of carbon.
Inventors
- 👤 W. Harry Mandeville
- 👤 Larry K. Truesdale
- 👤 Howard Tennent
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:11
CPC Classifications
B; B01; B01J; B01J27/00; B01J27/20; B01J35/00; B01J35/50; B01J35/58; B82; B82Y; B82Y30/00; C; C04; C04B; C04B14/00; C04B14/38; C04B14/386; C04B35/00; C04B35/622; C04B35/62227; C04B35/62272; C04B35/71; C04B35/78; C04B35/80; C04B35/83; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/06; D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/127; D01F9/00; D01F9/08; D01F9/12; D01F9/127; F; F16; F16D; F16D69/00; F16D69/02; F16D69/023; H; H01; H01B; H01B1/00; H01B1/02; H01B1/04; H01B1/14; H01B1/16; H01B1/18; H01B1/20; H01B1/24; B29; B29K; B29K2307/00
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
148 words
In the process of producing carbon fibrils by decomposing a source of carbon at elevated temperatures in contact with a multivalent transition metal and recovering the fibrils formed thereby; the improvement which comprises injecting catalyst particles having a size of up to 400 microns and comprising at least one multivalent transition metal on a particulate substrate into a reactor heated to a temperature below the thermal decomposition temperature of said source of carbon, and continuously recovering the fibrils formed thereby, said metal being present on said substrate as a multiplicity of discontinuous catalytic sites which, at least during fibril formation, have a size of about 35 to 700 A which size is measured by measuring the size of transition metal particles recovered along with produced fibrils and said fibrils comprising an inner core region of less ordered carbon atoms surrounded by an outer region of ordered carbon atoms.
Claim 2
Dependent Claim
148 words
In the process of producing carbon fibrils by decomposing a source of carbon at elevated temperatures in contact with a multivalent transition metal and recovering the fibrils formed thereby; the improvement which comprises injecting catalyst particles having a size of up to 400 microns and comprising at least one multivalent transition metal on a particulate substrate into a reactor heated to a temperature below the thermal decomposition temperature of said source of carbon, and continuously recovering the fibrils formed thereby, said metal being present on said substrate as a multiplicity of discontinuous catalytic sites which, at least during fibril formation, have a size of about 35 to 700 A which size is measured by measuring the size of transition metal particles recovered along with produced fibrils and said fibrils comprising an inner core region of less ordered carbon atoms surrounded by an outer region of ordered carbon atoms.
Claim 3
Dependent Claim
23 words
The improved process of claim 1 wherein said transition metal comprises iron with a catalyst site size of about 60 to 300 A.
Claim 4
Dependent Claim
35 words
The improved process of claim 1 wherein said transition metal is iron mixed with at least one other transition metal and said transition metals are present in an amount less than about 25 wt. %.
Claim 5
Dependent Claim
24 words
The improved process of claim 3 wherein said other transition metal is at least one selected from the group consisting of molybdenum and chromium.
Claim 6
Dependent Claim
15 words
The improved process of claim 1 wherein said carbon source is a mixture of hydrocarbons.
Claim 7
Dependent Claim
48 words
The improved process of claim 1 wherein said carbon source is at least one member selected from the group consisting of methane, ethane, propane, butane, benzene, butene, isobutene, cyclohexane, ethylene, propylene, acetylene, toluene, xylene, cumene, ethyl benzene, naphthalene, phenanthrene, anthracene, formaldehyde, acetaldehyde, acetone, methanol, ethanol, and carbon monoxide.
Claim 8
Dependent Claim
28 words
The improved process as claimed in claim 1 carried out in an ebulliating bed wherein said catalyst particles have a particle size of about 50 to 300 microns.
Claim 9
Dependent Claim
28 words
The improved process as claimed in claim 1 carried out in an transport bed wherein said catalyst particles have a particle size of less than about 10 microns.
Claim 10
Dependent Claim
20 words
The improved process of claim 8 wherein said catalyst particles have a particle size of less than about 1 micron.
Claim 11
Dependent Claim
22 words
The improved process of claim 1 including physically cofeeding said catalyst particles and said source of carbon downflow through a reaction zone.
Claim 12
Dependent Claim
22 words
The improved process of claim 1 including physically cofeeding said catalyst particles and said source of carbon upflow through a reaction zone.
Claim 13
Dependent Claim
16 words
The improved process of claim 1 including cofeeding a non-hydrocarbonaceous gas with said carbon contributing feed.
Claim 14
Dependent Claim
17 words
The improved process of claim 1 including dispersing said catalyst particles throughout the volume of the reactor.
Claim 15
Dependent Claim
22 words
The improved process of claim 1 wherein said catalyst particles are added to the heated reactor over the course of the reaction.
Claim 16
Dependent Claim
19 words
The improved process of claim 14 wherein said catalyst particles are added intermittently over the course of the reaction.
Claim 17
Dependent Claim
17 words
The improved process of claim 1 wherein said source of carbon is added to the heated reactor.
Claim 18
Dependent Claim
23 words
The improved process of claim 1 wherein said source of carbon is added to the heated reactor over the course of the reaction.
Claim 19
Dependent Claim
27 words
The improved process of claim 1 wherein said catalyst particles and said source of carbon are added to the heated reactor over the course of the reaction.
Claim 20
Dependent Claim
17 words
The improved process of claim 1 carried out at a temperature between about 500° and 1500° C.
Claim 21
Dependent Claim
40 words
The improved process of claim 1 including recovering a high yield of product comprising carbon fibrils characterized as tubes that are substantially free of pyrolytically deposited thermal carbon and have graphitic layers that are substantially parallel to the fibril axis.
Claim 22
Dependent Claim
19 words
The improved process of claim 1 wherein the diameter of said fibrils is between 3.5 and 70 nanometers, inclusive.
Claim 23
Dependent Claim
16 words
The improved process of claim 1 wherein said process is carried out in a fluidized bed.
Claim 24
Dependent Claim
138 words
A process for producing high yields of long, thin fibrils comprising at least long portions having atomically ordered outer surfaces, as made by contacting a vaporous source of the atoms which will comprise said outer surface with catalytic particles; which process comprises injecting said catalyst particles into a reactor heated to a temperature below the thermal composition temperature of said source of carbon, said catalyst particles having a size of up to 400 microns and comprising at least one multivalent transition metal on a particulate substrate, said metal being present on said substrate as multiplicity of discontinuous catalytic sites which, at least during fibril formation, have a size of about 35 to 700 A which size is measured by measuring the size of transition metal particles recovered along with produced fibrils, and continuously recovering the fibrils formed thereby.
Claim 25
Dependent Claim
138 words
A process for producing high yields of long, thin fibrils comprising at least long portions having atomically ordered outer surfaces, as made by contacting a vaporous source of the atoms which will comprise said outer surface with catalytic particles; which process comprises injecting said catalyst particles into a reactor heated to a temperature below the thermal composition temperature of said source of carbon, said catalyst particles having a size of up to 400 microns and comprising at least one multivalent transition metal on a particulate substrate, said metal being present on said substrate as multiplicity of discontinuous catalytic sites which, at least during fibril formation, have a size of about 35 to 700 A which size is measured by measuring the size of transition metal particles recovered along with produced fibrils, and continuously recovering the fibrils formed thereby.
References Cited (Backward Citations)
US4014980A
Cited
US4710483A
Cited
JPS55118913A
Cited
JPS57117622A
Cited
JPS58966A
Cited
US4650657A
Cited
US4767737A
Cited
US4435376A
Cited
JPS60231821A
Cited
US4816289A
Cited
JPS61132600A
Cited
US4663230A
Cited
EP0198558A2
Cited
WO1987001317A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-19 | 1999-09-18 | 2000-03-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-19 | 2003-09-18 | 2004-03-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-19 | 2007-09-18 | 2008-03-19 | $7700.00 | Window Closed / Lapsed |