Method for making carbonaceous materials
Assignee: Northrop Grumman Corp
•
Filing: 1986-07-21
•
Granted: 1988-08-30
•
Expires: 2006-07-21
Abstract
Abstract A fluidized bed disproportionation of carbon monoxide is effected using ferrous metal component-containing catalysts in particulate form. The bed also contains an abradant to continuously remove from the surface of those particles a substantial quantity of the carbonaceous fibers formed on those surfaces. The method produces a carbonaceous material of desired carbon and ferrous metal content. The process allows the use of two beds in series for producing high carbon content products.
Inventors
- 👤 Edward F. Brooks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:26
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/127; D01F9/1278; B; B82; B82Y; B82Y30/00; C; C01; C01B; C01B32/00; C01B32/05; B01; B01J; B01J2208/00; B01J2208/00008; B01J2208/00654; B01J2208/00681; C01P; C01P2004/00; C01P2004/01; C01P2004/03
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
289 words
A method for preparing a fibrous carbonaceous/ferrous group metal material comprising the steps of: (a) introducing a feed gas containing carbon monoxide into a reaction zone having a bed containing particulate material to form a fluidized bed, the particulate material comprising a discrete abradant and a discrete catalyst containing ferrous metal, the abradant constituting at least 2/3 of the weight of the particulate material, the catalyst catalyzing the disproportionation of at least a portion of the carbon monoxide to form (i) a reacted gas stream and (ii) a fibrous carbonaceous/ferrous metal material that forms on the surface of the catalyst, the abradant being non-catalytic to carbon deposition and abrading the fibrous carbonaceous/ferrous metal material from the surface of the catalyst, wherein the feed gas is introduced into the reaction zone (i) at a temperature at least 50° C. lower than the temperature of the reaction zone and (ii) at a sufficient velocity for fluidizing the particulate material and so that the reacted gas stream elutriates abraded fibrous carbonaceous/ferrous metal material from the fluidized bed at a rate such that the bed turnover time for carbon is from 2 to 50 hours; (b) maintaining the temperature in the reaction zone from 300° to 700° C.; (c) maintaining the pressure in the reaction zone from about 1 to about 10 atmospheres; (d) withdrawing elutriated fibrous carbonaceous/ferrous material from the reaction zone, the withdrawn material comprising at least 2% by weight ferrous metal and at least 70% weight carbon, the withdrawn material having a weight average particle size of from about 1 to about 50 microns; and (e) introducing catalyst to the reaction zone for replenishing the ferrous metal withdrawn from the reaction zone as part of the fibrous carbonaceous/ferrous metal material.
Claim 2
Independent Claim
289 words
A method for preparing a fibrous carbonaceous/ferrous group metal material comprising the steps of: (a) introducing a feed gas containing carbon monoxide into a reaction zone having a bed containing particulate material to form a fluidized bed, the particulate material comprising a discrete abradant and a discrete catalyst containing ferrous metal, the abradant constituting at least 2/3 of the weight of the particulate material, the catalyst catalyzing the disproportionation of at least a portion of the carbon monoxide to form (i) a reacted gas stream and (ii) a fibrous carbonaceous/ferrous metal material that forms on the surface of the catalyst, the abradant being non-catalytic to carbon deposition and abrading the fibrous carbonaceous/ferrous metal material from the surface of the catalyst, wherein the feed gas is introduced into the reaction zone (i) at a temperature at least 50° C. lower than the temperature of the reaction zone and (ii) at a sufficient velocity for fluidizing the particulate material and so that the reacted gas stream elutriates abraded fibrous carbonaceous/ferrous metal material from the fluidized bed at a rate such that the bed turnover time for carbon is from 2 to 50 hours; (b) maintaining the temperature in the reaction zone from 300° to 700° C.; (c) maintaining the pressure in the reaction zone from about 1 to about 10 atmospheres; (d) withdrawing elutriated fibrous carbonaceous/ferrous material from the reaction zone, the withdrawn material comprising at least 2% by weight ferrous metal and at least 70% weight carbon, the withdrawn material having a weight average particle size of from about 1 to about 50 microns; and (e) introducing catalyst to the reaction zone for replenishing the ferrous metal withdrawn from the reaction zone as part of the fibrous carbonaceous/ferrous metal material.
Claim 3
Dependent Claim
55 words
The method of claim 1 wherein the bed includes a lower ferrous metal-rich region and an upper carbon-rich region, the abradant in the lower region having a weight average particle size greater than about 120 microns and the abradant in the upper region having a weight average particle size of less than about 120 microns.
Claim 4
Dependent Claim
22 words
The method of claim 2 in which the abradant in the lower region is denser than the abradant in the upper region.
Claim 5
Dependent Claim
30 words
The method of claim 3 in which the density of the abradant in the lower region is at least 1.2 times the density of the abradant in the upper region.
Claim 6
Dependent Claim
24 words
The method of claim 2 in which the introduced catalyst comprises discrete particles having a weight average particle size of greater than 120 microns.
Claim 7
Dependent Claim
16 words
The method of claim 1 in which the withdrawn material contains more than 5% ferrous metal.
Claim 8
Dependent Claim
84 words
The method of claim 1 in which the fluidized bed is in a reactor having a lower portion with a first cross sectional area and an upper portion with a second cross sectional area that is greater than the first cross sectional area, the method including the step of introducing fluidization gas into the upper portion so that the superficial velocity of gas flowing through the upper portion is at least 80% of the superficial velocity of the gas flowing through the lower portion.
Claim 9
Dependent Claim
13 words
The method of claim 7 in which the fluidization gas is feed gas.
Claim 10
Dependent Claim
60 words
The method of claim 1 which includes contacting the abraded fibrous carbonaceous/ferrous metal material with carbon monoxide for increasing the carbon-to-ferrous metal ratio in the abraded material before it exits the bed, wherein the ferrous metal of the abraded material catalyzes the disproportionation of at least some of the carbon monoxide and wherein additional carbon forms on the abraded material.
Claim 11
Dependent Claim
29 words
The method of claim 1 wherein the abradant constitutes from about 2/3 to about 4/5 by weight of the total weight of the particulate material in the fluidized bed.
Claim 12
Dependent Claim
22 words
The method of claim 10 wherein the abradant has a weight average particle size of from about 80 to about 120 microns.
Claim 13
Dependent Claim
18 words
The method of claim 1 in which the temperature of the feed gas is 250° C. or lower.
Claim 14
Dependent Claim
18 words
The method of claim 1 in which the step of maintaining the temperature comprises cooling the reaction zone.
Claim 15
Dependent Claim
68 words
The method of claim 1 including the step of forming gas bubbles from the feed gas in a bubble formation zone for agitating the fluidized bed, the bubble formation zone comprising fluidized inert particles located proximate to the location that feed gas is introduced to the reaction zone, the inert particles being non-catalytic to carbon deposition and having a weight average particle size of at least 200 microns.
Claim 16
Dependent Claim
42 words
The method of claim 14 in which the inert particles in the bubble formation zone have a bulk density of from about 1.4 to about 4 g/cm 3 and a weight average particle size of from about 200 to about 300 microns.
Claim 17
Dependent Claim
21 words
The method of claim 1 in which the withdrawn material has a weight average particle size of greater than 5 microns.
Claim 18
Dependent Claim
20 words
The method of claim 1 in which the temperature in the reaction zone is maintained from 400° to 700° C.
Claim 19
Dependent Claim
20 words
The method of claim 1 in which the weight average particle size of the catalyst is less than 100 microns.
Claim 20
Dependent Claim
21 words
The method of claim 1 in which the abradant has a weight average particle size of from 80 to 120 microns.
Claim 21
Dependent Claim
25 words
The method of claim 1 in which the feed gas contains hydrogen and the volume ratio of carbon monoxide to hydrogen is at least 1:1.
Claim 22
Dependent Claim
23 words
The method of claim 20 in which the volume ratio of carbon monoxide to hydrogen in the feed gas is at least 2:1.
Claim 23
Dependent Claim
18 words
The method of claim 1 in which the bed turnover time for carbon is less than 25 hours.
Claim 24
Dependent Claim
25 words
The method of claim 1 in which the material withdrawn from the reaction zone has a bulk density of at least 0.05 g/cm 3 .
Claim 25
Dependent Claim
25 words
The method of claim 23 in which the material withdrawn from the reaction zone has a bulk density of up to 0.7 g/cm 3 .
Claim 26
Dependent Claim
26 words
The method of claim 1 wherein the superficial velocity of the feed gas through the reaction zone is about 40 to about 70 centimeters per second.
Claim 27
Dependent Claim
26 words
The method of claim 1 wherein the superficial velocity of the feed gas through the reaction zone is about 10 to about 70 centimeters per second.
Claim 28
Independent Claim
348 words
A method for preparing a fibrous carbonaceous/ferrous group metal material comprising the steps of: (a) introducing a feed gas containing carbon monoxide and hydrogen into a reaction zone having a bed containing particulate material to form a fluidized bed, the volume ratio of carbon monoxide to hydrogen in the feed gas being at least 2:1, the particulate material comprising a discrete abradant having a weight average particle size of from 80 to 120 microns and a discrete catalyst containing ferrous metal, the abradant being present in an amount of from about 2/3 to about 4/5 by weight of the particulate material, the catalyst catalyzing the disproportionation of at least a portion of the carbon monoxide to form (i) a reacted gas stream and (ii) a fibrous carbonaceous/ferrous metal material that forms on the surface of the catalyst, the abradant being non-catalytic to carbon deposition and abrading the fibrous carbonaceous/ferrous metal material from the surface of the catalyst, wherein the feed gas has a temperature of 250° C. or less and is introduced into the reaction zone at a sufficient velocity for fluidizing the particulate material and so that reacted gas stream elutriates abraded fibrous carbonaceous/ferrous metal material from the fluidized bed, the superifical velocity of gas in the raction zone being from about 10 to about 70 cm/s, the bed turnover time for carbon being from 4 to 50 hours; (b) maintaining the temperature in the reaction zone from about 400° to about 550° by cooling the reaction zone; (c) maintaining the pressure in the reaction zone from about 1 to about 10 atmospheres; (d) withdraswing elutriated fibrous carbonaceous/ferrous metal material from the reaction zone, the withdrawn material comprising at least 2% by weight ferrous metal and at least 70% by weight carbon, the withdrawn material having a weight average particle size of from about 5 to about 50 microns and a bulk density of at least 0.5 g/cm 3 ; and (e) introducing ferrous metal to the reaction zone for replenishing the ferrous metal withdrawn from the reaction zone as part of the fibrous carbonaceous/ferrous metal material.
Claim 29
Independent Claim
348 words
A method for preparing a fibrous carbonaceous/ferrous group metal material comprising the steps of: (a) introducing a feed gas containing carbon monoxide and hydrogen into a reaction zone having a bed containing particulate material to form a fluidized bed, the volume ratio of carbon monoxide to hydrogen in the feed gas being at least 2:1, the particulate material comprising a discrete abradant having a weight average particle size of from 80 to 120 microns and a discrete catalyst containing ferrous metal, the abradant being present in an amount of from about 2/3 to about 4/5 by weight of the particulate material, the catalyst catalyzing the disproportionation of at least a portion of the carbon monoxide to form (i) a reacted gas stream and (ii) a fibrous carbonaceous/ferrous metal material that forms on the surface of the catalyst, the abradant being non-catalytic to carbon deposition and abrading the fibrous carbonaceous/ferrous metal material from the surface of the catalyst, wherein the feed gas has a temperature of 250° C. or less and is introduced into the reaction zone at a sufficient velocity for fluidizing the particulate material and so that reacted gas stream elutriates abraded fibrous carbonaceous/ferrous metal material from the fluidized bed, the superifical velocity of gas in the raction zone being from about 10 to about 70 cm/s, the bed turnover time for carbon being from 4 to 50 hours; (b) maintaining the temperature in the reaction zone from about 400° to about 550° by cooling the reaction zone; (c) maintaining the pressure in the reaction zone from about 1 to about 10 atmospheres; (d) withdraswing elutriated fibrous carbonaceous/ferrous metal material from the reaction zone, the withdrawn material comprising at least 2% by weight ferrous metal and at least 70% by weight carbon, the withdrawn material having a weight average particle size of from about 5 to about 50 microns and a bulk density of at least 0.5 g/cm 3 ; and (e) introducing ferrous metal to the reaction zone for replenishing the ferrous metal withdrawn from the reaction zone as part of the fibrous carbonaceous/ferrous metal material.
Claim 30
Dependent Claim
25 words
The method of claim 27 in which the material withdrawn from the reaction zone has a bulk density of up to 0.7 g/cm 3 .
Claim 31
Dependent Claim
25 words
The method of claim 27 wherein the superficial velocity of the gas through the reaction zone is about 40 to about 70 centimeters per second.
Claim 32
Independent Claim
307 words
A method for preparing a fibrous carboneous/ferrous group metal comprising the steps of: (a) introducing a feed gas containing carbon monoxide into a reaction zone having a bed containing particulate material for forming a fluidized bed, the particulate material comprising a discrete abradant and a discrete catalyst containing ferrous metal, the abradant constituting at least 2/3 of the total weight of the particulate material in the fluidized bed, the catalyst catalyzing the disproportionation of at least a portion of the carbon monoxide to form (i) a reacted gas stream and (ii) a fibrous carbonaceous/ferrous metal material that forms on the surface of the catalyst, the abradant being non-catalytic to carbon deposition and abrading the fibrous carbonaceous/ferrous metal material from the surface of the catalyst, wherein the feed gas has a temperature of no more than 250° C. and is introduced into the reaction zone at a sufficient velocity for fluidizing the particulate material and so that the reacted gas elutriates abraded fibrous carbonaceous/ferrous metal material from the fluidized bed at a rate such that the bed turnover time for carbon is from 2 to 50 hours; (b) maintaining the temperature in the reaction zone from about 400° to about 470° C.; (c) maintaining the pressure in the reaction zone from about 1 to about 10 atmospheres; (d) withdrawing elutriated fibrous carbonaceous/ferrous metal material from the reaction zone, the wtihdrawn material comprising from 3 to 10% by weight ferrous metal, having a weight average particle size of from 1 to about 10 microns, and a bulk density of at least 0.05 g/cm 3 ; and (e) introducing ferrous metal catalyst to the reaction zone for replenishing the ferrous metal withdrawn from the reaction zone as part of the fibrous carbonaceous/ferrous metal material, the ferrous metal catalyst having a weight average particle size of from 0.1 to 100 microns.
Claim 33
Independent Claim
307 words
A method for preparing a fibrous carboneous/ferrous group metal comprising the steps of: (a) introducing a feed gas containing carbon monoxide into a reaction zone having a bed containing particulate material for forming a fluidized bed, the particulate material comprising a discrete abradant and a discrete catalyst containing ferrous metal, the abradant constituting at least 2/3 of the total weight of the particulate material in the fluidized bed, the catalyst catalyzing the disproportionation of at least a portion of the carbon monoxide to form (i) a reacted gas stream and (ii) a fibrous carbonaceous/ferrous metal material that forms on the surface of the catalyst, the abradant being non-catalytic to carbon deposition and abrading the fibrous carbonaceous/ferrous metal material from the surface of the catalyst, wherein the feed gas has a temperature of no more than 250° C. and is introduced into the reaction zone at a sufficient velocity for fluidizing the particulate material and so that the reacted gas elutriates abraded fibrous carbonaceous/ferrous metal material from the fluidized bed at a rate such that the bed turnover time for carbon is from 2 to 50 hours; (b) maintaining the temperature in the reaction zone from about 400° to about 470° C.; (c) maintaining the pressure in the reaction zone from about 1 to about 10 atmospheres; (d) withdrawing elutriated fibrous carbonaceous/ferrous metal material from the reaction zone, the wtihdrawn material comprising from 3 to 10% by weight ferrous metal, having a weight average particle size of from 1 to about 10 microns, and a bulk density of at least 0.05 g/cm 3 ; and (e) introducing ferrous metal catalyst to the reaction zone for replenishing the ferrous metal withdrawn from the reaction zone as part of the fibrous carbonaceous/ferrous metal material, the ferrous metal catalyst having a weight average particle size of from 0.1 to 100 microns.
Claim 34
Dependent Claim
25 words
The method of claim 30 in which the material withdrawn from the reaction zone has a bulk density of up to 0.25 g/cm 3 .
Claim 35
Dependent Claim
25 words
The method of claim 30 in which the material withdrawn from the reaction zone has a bulk density of up to 0.7 g/cm 3 .
Claim 36
Dependent Claim
25 words
The method of claim 32 in which the material withdrawn from the reaction zone has a bulk density of up to 0.25 g/cm 3 .
Claim 37
Dependent Claim
26 words
The method of claim 30 wherein the superficial velocity of the feed gas through the reaction zone is about 40 to about 70 centimeters per second.
References Cited (Backward Citations)
US1964744A
Cited
US2008270A
Cited
US2704293A
Cited
GB865490A
Cited
US3816609A
Cited
US3861885A
Cited
US4242103A
Cited
US4242104A
Cited
US4642125A
Cited
US4650657A
Cited
US4591334A
Cited
US4583299A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-08-30 | 1992-02-29 | 1992-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-08-30 | 1996-02-29 | 1996-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-08-30 | 2000-02-29 | 2000-08-30 | $7700.00 | Window Closed / Lapsed |