Method of making multi-layer address lines for amorphous silicon liquid crystal display devices
Assignee: General Electric Co
•
Filing: 1992-06-12
•
Granted: 1996-03-12
•
Expires: 2012-06-12
Abstract
Abstract Each scan line of a liquid crystal display (LCD) includes: a first layer of titanium disposed on the LCD substrate surface to promote adhesion of the scan line to the substrate surface; a layer of molybdenum or aluminum disposed on the first titanium layer to provide a low resistance address line; and a second layer of titanium disposed on the molybdenum layer to promote adhesion of a subsequently deposited layer of passivation material, semiconductor material or the like over the scan line. The multi-layered scan line side walls may be etched to promote step coverage of subsequently deposited layers of material. The data lines may also have a multi-layer conductor structure similar to the scan lines.
Inventors
- 👤 Nathan R. Whetten
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:28
CPC Classifications
G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/136; G02F1/1362; G02F1/1368; H; H10; H10D; H10D86/00; H10D86/40; H10D86/441; H10D86/60; G02F1/136286; G02F1/13629; H10D30/00; H10D30/60; H10D30/67; H10D30/6729; H10D30/6737; H10D30/6739; H10D30/674; H10D30/6741; H10D30/6743
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
122 words
A method for fabricating scan and data lines for a liquid crystal display, comprising the steps of: (a) forming a first layer of titanium in a first pattern on a substrate surface of the liquid crystal display; (b) forming at least a second layer selected from the group consisting of molybdenum and aluminum, on the first titanium layer to form a multi-layer scan line; (c) forming at least one layer of material on the multi-layer scan line to insulate the scan line from all data lines; and (d) forming at least a third layer selected from the group consisting of molybdenum and aluminum, in a second pattern and on the at least one insulation layer to form each of the data lines.
Claim 2
Independent Claim
122 words
A method for fabricating scan and data lines for a liquid crystal display, comprising the steps of: (a) forming a first layer of titanium in a first pattern on a substrate surface of the liquid crystal display; (b) forming at least a second layer selected from the group consisting of molybdenum and aluminum, on the first titanium layer to form a multi-layer scan line; (c) forming at least one layer of material on the multi-layer scan line to insulate the scan line from all data lines; and (d) forming at least a third layer selected from the group consisting of molybdenum and aluminum, in a second pattern and on the at least one insulation layer to form each of the data lines.
Claim 3
Dependent Claim
23 words
The method of claim 1, wherein steps (a) and (b) comprise the steps of sputtering each of the layers during a single pumpdown.
Claim 4
Dependent Claim
31 words
The method of claim 1, further comprising the step of tapering the multi-layer scan line to a degree selected to promote step coverage of materials subsequently deposited upon the scan line.
Claim 5
Dependent Claim
42 words
The method of claim 3, wherein the second layer is aluminum and the tapering step comprises the step of etching the first titanium layer and the second aluminum layer in a mixture of BCl 3 , CCl 4 and O 2 gases.
Claim 6
Dependent Claim
20 words
The method of claim 3, further comprising the step of forming a fourth layer of titanium on the second layer.
Claim 7
Dependent Claim
23 words
The method of claim 5, wherein the tapering step comprises the step of wet etching the first titanium layer with HBF 4 .
Claim 8
Dependent Claim
29 words
The method of claim 5, wherein the second layer is molybdenum and the tapering step comprises the step of wet etching the second molybdenum layer with a PAWN solution.
Claim 9
Dependent Claim
29 words
The method of claim 5, wherein the tapering step comprises the step of dry etching the fourth titanium layer in an atmosphere of SF 6 and O 2 .
Claim 10
Dependent Claim
29 words
The method of claim 5, wherein the tapering step comprises the step of dry etching the fourth titanium layer in an atmosphere of CF 4 and O 2 .
Claim 11
Dependent Claim
24 words
The method of claim 1, further comprising the step of forming a fifth layer of titanium in the second pattern after step (d) .
Claim 12
Dependent Claim
24 words
The method of claim 1, further comprising the step of forming a fifth layer of titanium in the second pattern before step (d) .
Claim 13
Dependent Claim
24 words
The method of claim 11, further comprising the step of forming a sixth layer of titanium in the second pattern after step (d) .
References Cited (Backward Citations)
US4673969A
Cited
US4543573A
Cited
US4804953A
Cited
US5028551A
Cited
US4918504A
Cited
US5148248A
Cited
US5062690A
Cited
US5153754A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-12 | 1999-09-11 | 2000-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-12 | 2003-09-11 | 2004-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-12 | 2007-09-11 | 2008-03-12 | $7700.00 | Window Closed / Lapsed |