Method of making a micromechanical silicon-on-glass tuning fork gyroscope
Assignee: Charles Stark Draper Laboratory Inc
•
Filing: 1994-02-04
•
Granted: 1996-02-20
•
Expires: 2014-02-04
Abstract
Abstract A micromechanical tuning fork gyroscope fabricated by a dissolved silicon wafer process whereby electrostatic bonding forms a hermetic seal between an etched glass substrate, metal electrodes deposited thereon, and a silicon comb-drive tuning fork gyroscope. The dissolved silicon wafer process involves single sided processing of a silicon substrate, including the steps of etching recesses, diffusing an etch resistant dopant into the silicon substrate, and releasing various components of the silicon gyroscope by etching through the diffusion layer in desired locations. The glass substrate also undergoes single sided processing, including the steps of etching recesses, depositing a multi-metal system in the recesses, and selectively etching portions of the multi-metal system. One substrate is inverted over the other and aligned before anodic bonding of the two substrates is performed.
Inventors
- 👤 Steve T. Cho
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:38
CPC Classifications
G; G01; G01C; G01C19/00; G01C19/56; G01C19/5719; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/924
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
124 words
A method for fabricating a comb drive tuning fork gyroscope, including associated 'electrodes, transducers, and interconnecting electrical leads, said gyroscope adapted for inertial rate sensitivity, comprising the steps of: providing a silicon substrate having a first surface; forming discrete elements of said gyroscope in selected regions of said first surface of said silicon substrate; providing a glass substrate having a first surface; forming a plurality of multilayer metal deposits in a plurality of recessed regions of said first surface of said glass substrate; removing selected portions of said multilayer metal deposit from selected ones of said plurality of recessed regions; bonding said first surface of said silicon substrate to said first surface of said glass substrate; and exposing said silicon substrate to an etchant.
Claim 2
Independent Claim
124 words
A method for fabricating a comb drive tuning fork gyroscope, including associated 'electrodes, transducers, and interconnecting electrical leads, said gyroscope adapted for inertial rate sensitivity, comprising the steps of: providing a silicon substrate having a first surface; forming discrete elements of said gyroscope in selected regions of said first surface of said silicon substrate; providing a glass substrate having a first surface; forming a plurality of multilayer metal deposits in a plurality of recessed regions of said first surface of said glass substrate; removing selected portions of said multilayer metal deposit from selected ones of said plurality of recessed regions; bonding said first surface of said silicon substrate to said first surface of said glass substrate; and exposing said silicon substrate to an etchant.
Claim 3
Dependent Claim
77 words
The method of claim 1 wherein said step of forming gyroscope elements includes the steps of: forming a plurality of raised regions in said first surface of said silicon substrate; forming a doped region and an undoped region in said silicon substrate by diffusing into said silicon substrate first surface a dopant resistant to a silicon etchant; and removing selected portions of said first surface of said silicon substrate to define said discrete elements of said gyroscope.
Claim 4
Dependent Claim
58 words
The method of claim 1 wherein said step of forming multilayer metal deposits includes the steps of: etching said first surface of said glass substrate to form a plurality of recessed regions; and forming in each of said recessed regions of said glass substrate said plurality of multilayer metal deposits by successive depositions of individual conductive metal layers.
Claim 5
Dependent Claim
33 words
The method of claim 1 wherein said step of removing a first metallic layer includes the steps of: etching through said first metallic layer to expose a planar surface of said second layer.
Claim 6
Dependent Claim
32 words
The method of claim 1 wherein said step of removing selected portions of said multilayer metal deposit includes the steps of: etching said first metallic layer to form a plurality of stand-offs.
Claim 7
Dependent Claim
34 words
The method of claim 5 wherein said step of etching through said first metallic layer includes the steps of: masking said first metallic layer; and exposing said masked first metallic layer to an etchant.
Claim 8
Dependent Claim
26 words
The method of claim 6 wherein said step of etching said first metallic layer forms a regularly spaced array of said stand-offs in said first layer.
Claim 9
Dependent Claim
42 words
The method of claim 5 wherein said step of etching through said first metallic layer includes the steps of: etching through said first metallic layer to expose said second metallic layer; masking said second metallic layer; and etching said second metallic layer.
Claim 10
Dependent Claim
26 words
The method of claim 8 wherein said step of etching said second metallic layer forms a regularly spaced array of said stand-offs in said second layer.
Claim 11
Dependent Claim
30 words
The method of claim 8 wherein said step of etching said second metallic layer includes the step of exposing a third metallic layer from which said plurality of stand-offs extend.
Claim 12
Dependent Claim
34 words
The method of claim 8 wherein said step of etching said second metallic layer includes the step of forming a planar surface of said second metallic layer from which said plurality of stand-offs extend.
Claim 13
Dependent Claim
51 words
The method of claim 1 wherein said step of bonding said first surface of said silicon substrate to said first surface of said glass substrate includes the steps of: inverting one of said silicon substrate and said glass substrate; disposing said substrates in an aligned orientation; and bonding said substrates together.
Claim 14
Dependent Claim
18 words
The method of claim 12 wherein said step of bonding includes the step of anodically bonding the substrates.
Claim 15
Dependent Claim
161 words
A process for forming a micromechanical tuning fork structure adapted for use in rate sensor applications comprising the steps of: providing a silicon substrate having a planar first surface; forming a height varying pattern in said first surface of said silicon substrate; exposing said first surface of said silicon substrate to a silicon dopant for a discrete time period; removing selected portions of said silicon substrate; providing a second substrate having a planar first surface, said first surface of said second substrate comprised of glass; forming a plurality of recesses in said first surface of said second substrate; depositing a plurality of superimposed metallic layers in said plurality of recesses; removing a first metallic layer to expose a second metallic layer from at least one of said plurality of recesses; disposing said first surface of said silicon substrate against said first surface of said second substrate; and removing a second surface of said silicon substrate not exposed to said silicon dopant.
Claim 16
Dependent Claim
161 words
A process for forming a micromechanical tuning fork structure adapted for use in rate sensor applications comprising the steps of: providing a silicon substrate having a planar first surface; forming a height varying pattern in said first surface of said silicon substrate; exposing said first surface of said silicon substrate to a silicon dopant for a discrete time period; removing selected portions of said silicon substrate; providing a second substrate having a planar first surface, said first surface of said second substrate comprised of glass; forming a plurality of recesses in said first surface of said second substrate; depositing a plurality of superimposed metallic layers in said plurality of recesses; removing a first metallic layer to expose a second metallic layer from at least one of said plurality of recesses; disposing said first surface of said silicon substrate against said first surface of said second substrate; and removing a second surface of said silicon substrate not exposed to said silicon dopant.
Claim 17
Dependent Claim
40 words
The method of claim 14 wherein said step of forming a height varying pattern in said first surface of said silicon substrate includes the step of etching said first surface of said silicon substrate using potassium hydroxide or plasma techniques.
Claim 18
Dependent Claim
31 words
The method of claim 14 wherein said step of exposing said first surface of said silicon substrate includes the step of diffusing boron into said first surface of said silicon substrate.
Claim 19
Dependent Claim
25 words
The method of claim 14 wherein said step of removing selected portions of said silicon substrate includes using trifluorobromomethane chemistry in a parallel plate reactor.
Claim 20
Dependent Claim
24 words
The method of claim 14 wherein said step of providing a second substrate includes the step of providing a second substrate comprised of glass.
Claim 21
Dependent Claim
30 words
The method of claim 14 wherein said step of providing a second substrate includes the step of providing a second substrate on which a deposition of glass has been sputtered.
Claim 22
Dependent Claim
36 words
The method of claim 14 wherein said step of forming a plurality of recesses in said first surface of said second substrate includes the step of etching said second substrate using hydroflouric acid or plasma techniques.
Claim 23
Dependent Claim
43 words
The method of claim 14 wherein said step of depositing a plurality of superimposed metallic layers in said plurality of recesses includes the step of sequentially depositing a third substrate of titanium, a second substrate of platinum, and a first substrate of gold.
Claim 24
Dependent Claim
40 words
The method of claim 14 wherein said step of removing a first metallic layer to expose a second metallic layer includes the steps of: etching said first metallic layer; masking said second metallic layer; and etching said second metallic layer.
Claim 25
Dependent Claim
25 words
The method of claim 22 wherein said step of etching said second metallic layer forms a plurality of stand-offs extending from said second metallic layer.
Claim 26
Dependent Claim
37 words
The method of claim 14 wherein said step of disposing said first surface of said silicon substrate against said first surface of said second substrate includes the step of anodically bonding said first and second surfaces together.
Claim 27
Dependent Claim
27 words
The method of claim 14 wherein said step of removing a second surface of said silicon substrate includes the step of exposing said second surface to ethylene-diamine-pyrocatechol-water.
References Cited (Backward Citations)
US4654663A
Cited
US4764244A
Cited
US4815472A
Cited
US4881410A
Cited
US5013396A
Cited
US5216490A
Cited
US5055838A
Cited
US5169472A
Cited
US5353638A
Cited
US5313835A
Cited
US5329815A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-02-19 | 1999-08-21 | 2000-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-02-19 | 2003-08-21 | 2004-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-02-19 | 2007-08-21 | 2008-02-20 | $7700.00 | Window Closed / Lapsed |