US5489398A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Phosphor and method of making same
Assignee: Osram Sylvania Inc
•
Filing: 1993-12-06
•
Granted: 1996-02-06
•
Expires: 2013-12-06
Abstract
Abstract Electroluminescent phosphors having substantially increased luminance and maintenance over that of prior art electroluminescent phosphors may be made by (1) doping an inorganic intercalation compound having an atomic structure interspersed with vacant spaces, with selected activator ions capable of luminescent emission, and (2) introducing organic monomers or other conductive material into the vacant spaces of the atomic structure of the doped inorganic intercalation compound. The organic monomers may be polymerized in situ to form conductive polymers therein.
Inventors
- 👤 Vaddi B. Reddy
- 👤 Ronald E. Karam
- 👤 Shellie K. Northrop
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:29
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/59; C09K11/592; C09K11/02; C09K11/025; C09K11/0805; C09K11/61; C09K11/611; C09K11/64; C09K11/646; C09K11/67; C09K11/671; H; H05; H05B; H05B33/00; H05B33/12; H05B33/14
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
175 words
A method of making blue-emitting titanium-activated crystalline alpha zirconium phosphate phosphor particles having a layered atomic structure and having the general formula Zr 1-x Ti x (HPO 4 ) 2 .H 2 O, where x is up to 0.08, comprising the steps of: forming a first aqueous solution of zirconium oxychloride, forming a second aqueous solution containing titanium, wherein the sum of the moles of zirconium oxychloride and the moles of titanium equals one mole, combining said first and said second solutions to form a third solution, adding an amount of 49% hydrofluoric acid to yield a molar ratio of HF to ZrOCl 2 .8H 2 O of about 7:1 to said third solution to form a fourth solution, adding an excess of stoichiometric amount of 85% phosphoric acid to said fourth solution to form a fifth solution, and passing nitrogen gas through said fifth solution over a sufficient time period to evaporate hydrogen fluoride gas from said fifth solution and form a precipitate consisting essentially of particles of titanium-activated crystalline alpha zirconium phosphate phosphor.
Claim 2
Independent Claim
175 words
A method of making blue-emitting titanium-activated crystalline alpha zirconium phosphate phosphor particles having a layered atomic structure and having the general formula Zr 1-x Ti x (HPO 4 ) 2 .H 2 O, where x is up to 0.08, comprising the steps of: forming a first aqueous solution of zirconium oxychloride, forming a second aqueous solution containing titanium, wherein the sum of the moles of zirconium oxychloride and the moles of titanium equals one mole, combining said first and said second solutions to form a third solution, adding an amount of 49% hydrofluoric acid to yield a molar ratio of HF to ZrOCl 2 .8H 2 O of about 7:1 to said third solution to form a fourth solution, adding an excess of stoichiometric amount of 85% phosphoric acid to said fourth solution to form a fifth solution, and passing nitrogen gas through said fifth solution over a sufficient time period to evaporate hydrogen fluoride gas from said fifth solution and form a precipitate consisting essentially of particles of titanium-activated crystalline alpha zirconium phosphate phosphor.
Claim 3
Dependent Claim
24 words
A method according to claim 1 wherein said solution containing titanium consists essentially of an aqueous solution of a water-soluble or acid-soluble titanium compound.
Claim 4
Dependent Claim
14 words
A method according to claim 2 wherein said titanium compound is titanium sulfate hydrate.
Claim 5
Dependent Claim
15 words
A method according to claim 2 wherein said titanium compound is ammonium titanyl oxalate hydrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-02-05 | 1999-08-07 | 2000-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-02-05 | 2003-08-07 | 2004-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-02-05 | 2007-08-07 | 2008-02-06 | $7700.00 | Window Closed / Lapsed |