Process for producing circuitized layers and multilayer ceramic sub-laminates and composites thereof
Assignee: International Business Machines Corp
•
Filing: 1993-12-30
•
Granted: 1996-01-02
•
Expires: 2013-12-30
Abstract
Abstract Process for producing circuitized greensheets including multi-layer ceramic sub-laminates and composites comprising thin ceramic greensheets carrying and thin, fine line patterned conductive metal layers. The invention comprises releasably-supporting the thin greensheets on a temporary carrier support having an ablatable release layer, preferably over a patterned conductive layer, and filling the vias with conductive metal paste, whereby the thin greensheets are supported against warpage and distortion. The supported greensheets are formed as single layers, pairs and stacks thereof, as desired, and thereafter separated from the temporary support for use.
Inventors
- 👤 Jon A. Casey
- 👤 David B. Goland
- 👤 Dinesh Gupta
- 👤 Lester W. Herron
- 👤 James N. Humenik
- 👤 Thomas E. Lombardi
- 👤 John U. Knickerbocker
- 👤 Robert J. Sullivan
- 👤 James R. Wylder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 03:04
CPC Classifications
H; H10; H10W; H10W74/00; H10W74/01; H10W74/019; H05; H05K; H05K3/00; H05K3/10; H05K3/20; H05K3/40; H05K3/4038; H05K3/4053; H05K3/4061; H05K3/46; H05K3/4611; H05K3/4614; H05K3/4617; H05K3/4626; H05K3/4629; H10P; H10P72/00; H10P72/70; H10P72/74; H10W70/00; H10W70/01; H10W70/05; H10W70/60; H10W70/611; H10W70/67; H10W70/68; H10W70/685; H10W90/00; H10W90/401; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1056; Y10T156/11; Y10T156/1142; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49126; Y10T29/49128
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
139 words
Process for producing circuitized ceramic greensheets while preventing warpage and distortion thereof, comprising the steps of: (a) forming a thin ceramic greensheet; (b) forming vias in said greensheet, either before or after step (f); (c) applying an ablatable release layer to the surface of a temporary rigid carrier support; (d) applying a thin non-ablatable, adhesive layer over said release layer; (e) forming a conductive patterned circuit layer by plating such layer over said adhesive layer; (f) lightly-laminating the thin ceramic greensheet of step (a) over said plated circuit layer; (g) applying conductive metal paste to fill the vias and to form interconnections with the patterned conductive circuit layer formed on the adhesive-coated surface of said carrier support to form a circuitized greensheet; and (h) ablating said release layer to separate said circuitized greensheet from said temporary rigid carrier support.
Claim 2
Dependent Claim
139 words
Process for producing circuitized ceramic greensheets while preventing warpage and distortion thereof, comprising the steps of: (a) forming a thin ceramic greensheet; (b) forming vias in said greensheet, either before or after step (f); (c) applying an ablatable release layer to the surface of a temporary rigid carrier support; (d) applying a thin non-ablatable, adhesive layer over said release layer; (e) forming a conductive patterned circuit layer by plating such layer over said adhesive layer; (f) lightly-laminating the thin ceramic greensheet of step (a) over said plated circuit layer; (g) applying conductive metal paste to fill the vias and to form interconnections with the patterned conductive circuit layer formed on the adhesive-coated surface of said carrier support to form a circuitized greensheet; and (h) ablating said release layer to separate said circuitized greensheet from said temporary rigid carrier support.
Claim 3
Dependent Claim
26 words
Process according to claim 1 which comprises forming a plurality of said circuitized greensheets and laminating them to one another to form a multilayer ceramic laminate.
Claim 4
Dependent Claim
85 words
Process according to claim 1 in which said thin ceramic greensheet of step (a) has releasably-adhered to the upper surface thereof a thin masking film, and step (b) comprises the steps of machining vias through said film and through said greensheet in predetermined areas, conducting step (g) of claim 1 by wiping the conductive metal paste over the surface of said masking film to fill said vias therewith, and peeling said masking film from said via - filled thin greensheet to form said circuitized greensheet.
Claim 5
Dependent Claim
24 words
Process according to claim 1 in which step (d) comprises applying a non-ablatable thin adhesive layer of polyvinyl butyral resin over said release layer.
Claim 6
Dependent Claim
47 words
Process according to claim 4 in which said release layer comprises a photo-reactive polymeric composition which ablates when exposed to radiation to which said adhesive layer is substantially inert, and applying said radiation to release the adhesive layer and patterned conductive layer from the temporary carrier support.
Claim 7
Dependent Claim
28 words
Process according to claim 1 which comprises the further steps of stacking a plurality of said circuitized greensheets and firing the stack to form a multi-layer ceramic body.
Claim 8
Dependent Claim
122 words
Process according to claim 1 which comprises the further step of forming a second thin patterned conductive layer over the supported circuitized greensheet of step (g), prior to step (h) , by (1) applying an abratable release layer to a second rigid carrier; (2) plating a second thin patterned conductive layer over said release layer, (3) aligning said second thin patterned conductive layer with the upper surface of the via-filled greensheet of step (g), (4) laminating said aligned sheets to form a supported pair comprising said via-filled greensheet layer having bonded to the opposed surfaces thereof said patterned conductive layers, and (5) conducting step (h) to release both of said greensheet layers from both of said temporary carriers as a self-supporting pair.
Claim 9
Dependent Claim
58 words
Process according to claim 7 in which said pair is released from one of said temporary carriers, aligned with another supported circuitized greensheet produced according to claim 1, with the filled vias of the greensheet of the circuitized greensheet in contact with a patterned conductive layer of the said pair, and laminated to form a supported multilayer ceramic.
Claim 10
Dependent Claim
35 words
Process according to claim 8 comprising releasing said multi-layer ceramic from both of said temporary carriers as a self-supporting sub-laminate, and stacking, laminating and firing a plurality of said sublaminates to form multi-layer ceramic body.
Claim 11
Dependent Claim
44 words
Process according to claim 8 comprising releasing said multi-layer ceramic from one of said temporary carriers, aligning it with another supported circuitized greensheet produced according to claim 1, and repeating the steps of claim 8 to produce a multi-layer ceramic incorporating another circuitized greensheet.
Claim 12
Dependent Claim
17 words
Process according to claim 1 in which the plated circuit layer of step (e) comprises plated copper.
References Cited (Backward Citations)
US3870776A
Cited
US3882059A
Cited
US3948706A
Cited
US4933124A
Cited
SU1443781A1
Cited
US4799983A
Cited
US5009744A
Cited
US4889573A
Cited
US4977006A
Cited
US5120590A
Cited
US5104707A
Cited
EP0425148A2
Cited
US5046238A
Cited
JPH0497591A
Cited
JPH0497590A
Cited
US5356512A
Cited
US5271150A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-01 | 1999-07-03 | 2000-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-01 | 2003-07-03 | 2004-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-01 | 2007-07-03 | 2008-01-02 | $7700.00 | Window Closed / Lapsed |