Abstract
Abstract A coating film which can sufficiently improve the wear resistance of a cutting tool or a wear-resistant tool and which reveals excellent qualities as a wear-resistant or protective film for an electric or electronic part or a sliding or machine part. Such a coating film is in the form of an ultra-thin film laminate comprising at least one nitride or carbonitride of at least one element selected from the group consisting of the elements in the groups IVa, Va and VIa in the periodic table and Al and B and having a cubic crystal structure and having mainly metallic bonding properties, and at least one compound having a crystal structure other than the cubic crystal structure at normal temperature and normal pressure and under equilibrium state and having mainly covalent bonding properties, the at least one nitride or carbonitride and the compound being alternately laminated in the form of layers, each layer of the compound having a thickness of 0.2-50 nm, the laminate having a cubic crystalline X-ray diffraction pattern as a whole.
Inventors
- 👤 Makoto Setoyama
- 👤 Motoyuki Tanaka
- 👤 Akira Nakayama
- 👤 Takashi Yoshida
- 👤 Yasuhisa Hashimoto
- 👤 Kazuo Yamagata
- 👤 Mitsunori Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:09
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3429; C03C17/3435; C04B41/45; C04B41/50; C04B41/5053; C04B41/5062; C04B41/52; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C04B41/89; C23; C23C; C23C14/00; C23C14/06; C23C14/0641; C23C14/0664; C04B2111/00; C04B2111/00034; C04B2111/00189; C04B2111/00241; C04B2111/00344; C04B2111/00353; C04B2111/00405; C04B2111/00474; C04B2111/00844; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
176 words
A wear-resistant member comprising a hard or surface-hardened substrate made of a WC-based cemented carbide, a cement or a hard-speed steel and an ultra-thin film laminate having a thickness of 0.5 to 10 μm coated on the surface of said substrate, said ultra-thin film laminate comprising at least one nitride or carbonitride of at least one element selected from the group consisting of the elements in the Groups IVa, Va and VIa in the Periodic Table and Al and B, said nitride or carbonitride having a cubic crystal structure and having mainly metallic bonding properties, and at least one compound having a crystal structure other than the cubic crystal structure at normal temperature and normal pressure and under an equilibrium state and having mainly covalent bonding properties, said at least one nitride or carbonitride and said at least one compound being alternately laminated in the form of layers, each layer of said nitride or carbonitride and said compound having a thickness of 0.2-20 nm, said laminate having a cubic crystalline X-ray diffraction pattern as a whole.
Claim 2
Dependent Claim
176 words
A wear-resistant member comprising a hard or surface-hardened substrate made of a WC-based cemented carbide, a cement or a hard-speed steel and an ultra-thin film laminate having a thickness of 0.5 to 10 μm coated on the surface of said substrate, said ultra-thin film laminate comprising at least one nitride or carbonitride of at least one element selected from the group consisting of the elements in the Groups IVa, Va and VIa in the Periodic Table and Al and B, said nitride or carbonitride having a cubic crystal structure and having mainly metallic bonding properties, and at least one compound having a crystal structure other than the cubic crystal structure at normal temperature and normal pressure and under an equilibrium state and having mainly covalent bonding properties, said at least one nitride or carbonitride and said at least one compound being alternately laminated in the form of layers, each layer of said nitride or carbonitride and said compound having a thickness of 0.2-20 nm, said laminate having a cubic crystalline X-ray diffraction pattern as a whole.
Claim 3
Dependent Claim
183 words
A wear-resistant member comprising a hard or surface-hardened substrate made of a WC-based cemented carbide, a cement or a hard-speed steel and an ultra-thin film laminate having a thickness of 0.5 to 10 μm coated on the surface of said substrate, said ultra-thin laminate comprising at least one nitride or carbonitride of at least one element selected from the group consisting of the elements in the Groups IVa, Va and VIa in the Periodic Table and Al, said nitride or carbonitride having a cubic crystal structure and having mainly metallic bonding properties, and at least one nitride containing Al and/or B as main components and having a crystal structure other than the cubic crystal structure at normal temperature and normal pressure and under an equilibrium state and having mainly covalent bonding properties, said at least one nitride or carbonitride and said at least one nitride being alternately laminated in the form of layers, each layer of said nitride or carbonitride and said compound having a thickness of 0.2 to 20 nm, said laminate having a cubic crystalline X-ray diffraction pattern as a whole.
Claim 4
Dependent Claim
183 words
A wear-resistant member comprising a hard or surface-hardened substrate made of a WC-based cemented carbide, a cement or a hard-speed steel and an ultra-thin film laminate having a thickness of 0.5 to 10 μm coated on the surface of said substrate, said ultra-thin laminate comprising at least one nitride or carbonitride of at least one element selected from the group consisting of the elements in the Groups IVa, Va and VIa in the Periodic Table and Al, said nitride or carbonitride having a cubic crystal structure and having mainly metallic bonding properties, and at least one nitride containing Al and/or B as main components and having a crystal structure other than the cubic crystal structure at normal temperature and normal pressure and under an equilibrium state and having mainly covalent bonding properties, said at least one nitride or carbonitride and said at least one nitride being alternately laminated in the form of layers, each layer of said nitride or carbonitride and said compound having a thickness of 0.2 to 20 nm, said laminate having a cubic crystalline X-ray diffraction pattern as a whole.
Claim 5
Dependent Claim
20 words
A wear resistant member as in claims 1 or 2 wherein the compositions of the adjacent compound layers change continuously.
Claim 6
Dependent Claim
83 words
A wear-resistant member as claimed in claim 1, 2 or 3 further comprising an intermediate layer provided between said substrate and said ultra-thin film laminate, said intermediate layer having a thickness of 0.05-5 μm and made of at least one compound selected from compounds comprising at least one element selected from the group consisting of the elements in the IVa, Va and VIa groups, compounds of at least one element selected from C and N, and oxides of elements in the IVa group.
Claim 7
Dependent Claim
55 words
A wear resistant member as claimed in claim 4, further comprising a surface layer provided on the surface of said ultra-thin film laminate, said surface layer having a thickness of 0.1-5 μm and made of at least one compound selected from nitrides, carbides, carbonitrides and oxides of elements in the IVa, Va and VIa groups.
Claim 8
Dependent Claim
32 words
A wear resistant member as claimed in any of claims 1, 2 or 3 which is used as a cutting tool such as a cutting insert, a drill and an end mill.
Claim 9
Dependent Claim
51 words
A wear resistant member as claimed in claim 6 in the form of a cutting insert having a rake face and a flank face both coated with said ultra-thin film laminate, said laminate formed on the rake face having a larger laminating cycle than said laminate formed on the flank face.
Claim 10
Dependent Claim
49 words
A wear resistant member as claimed in claim 6 in the form of a cutting insert having a rake face and a flank both coated with said ultra-thin film laminate, said laminate formed on the flank having a larger laminating cycle than said laminate formed on the rake face.
Claim 11
Dependent Claim
48 words
A wear resistant member wherein the ultra-thin film laminate as claimed in any of claims 1, 2 or 3 is used as a wear-resistant or protective layer of electric or electronic parts or sliding or machine parts, said ultra-thin film laminate having a thickness of 5 nm-10 μm.
References Cited (Backward Citations)
US4554201A
Cited
EP0162656A2
Cited
US4643951A
Cited
DE3532733A1
Cited
US4835062A
Cited
JPS61235555A
Cited
US4686156A
Cited
US4714660A
Cited
US4753854A
Cited
US4776863A
Cited
US4895770A
Cited
US4984940A
Cited
US5075181A
Cited
US5071693A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-12-25 | 1999-06-26 | 1999-12-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-12-25 | 2003-06-26 | 2003-12-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-12-25 | 2007-06-26 | 2007-12-26 | $7700.00 | Window Closed / Lapsed |