Conductor-filled thermosetting resin
Assignee: Lord Corp
•
Filing: 1993-12-07
•
Granted: 1995-12-12
•
Expires: 2013-12-07
Abstract
Abstract Conductor-filled thermosetting resins having a free radical based cure chemistry are prepared for use as solder paste replacements for electrical conducting attachments of surface mount electronics components to printed circuit boards and as a die attach adhesive. The thermosetting resins exhibit rheological properties that allow them to be substituted for state-of-the-art solder paste and die attach adhesives. The conductor filled resins can be thermally cured in in-line processing operations to provide a low stress, substrate adherent, electrically conductive resin matrix.
Inventors
- 👤 William L. Jamison
- 👤 Andrzej Moscicki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:43
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; H01B1/22; C; C08; C08K; C08K3/00; C08K3/02; C08K3/08; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/321; H10; H10W; H10W20/00; H10W20/40; H05K1/00; H05K1/18; H05K1/181; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/0129; H05K2201/0137; H05K2201/0145; H05K2201/02; H05K2201/0203; H05K2201/0242; H05K2201/0245; H05K2203/00; H05K2203/11; H05K2203/1105
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
118 words
A thermosetting resin formulation comprising about 15 to about 60 weight percent of a resin composition comprising about 30 to about 80 weight percent of a free radical cross-linkable unsaturated polyester or vinyl ester, about 5 to about 35 weight percent of a thermoplastic resin and about 0 to about 70 weight percent of an unsaturated monomer capable of cross-linking the cross-linkable polyester or vinyl ester, about 40 to about 85 weight percent of an electrically conductive microparticulate filler, and a free radical initiating agent in an amount effective to promote thermosetting of said formulation to a shape retaining electrically conducting resin matrix in about 30 seconds to about 5 minutes at about 100° to about 200° C.
Claim 2
Dependent Claim
118 words
A thermosetting resin formulation comprising about 15 to about 60 weight percent of a resin composition comprising about 30 to about 80 weight percent of a free radical cross-linkable unsaturated polyester or vinyl ester, about 5 to about 35 weight percent of a thermoplastic resin and about 0 to about 70 weight percent of an unsaturated monomer capable of cross-linking the cross-linkable polyester or vinyl ester, about 40 to about 85 weight percent of an electrically conductive microparticulate filler, and a free radical initiating agent in an amount effective to promote thermosetting of said formulation to a shape retaining electrically conducting resin matrix in about 30 seconds to about 5 minutes at about 100° to about 200° C.
Claim 3
Dependent Claim
23 words
The resin formulation of claim 1 wherein the monomer is selected from the group consisting of divinylbenzene, divinylpyridine, diallyl phthalate and diallyl isopthalate.
Claim 4
Dependent Claim
28 words
The resin formulation of claim 1 wherein the electrically conductive microparticulate filler comprises a metal selected from the group consisting of silver, gold, platinum, palladium, nickel and copper.
Claim 5
Dependent Claim
20 words
The resin formulation of claim 3 wherein the electrically conductive microparticulate filler comprises a silver having a tap density >3.
Claim 6
Dependent Claim
24 words
The resin formulation of claim 4 wherein the electrically conductive microparticulate filler is silver powder or silver flake having a tap density of >4.
Claim 7
Dependent Claim
16 words
The resin formulation of claim 1 wherein the unsaturated monomer is diallyl phthalate or diallyl isopthalate.
Claim 8
Dependent Claim
28 words
The resin formulation of claim 6 wherein the electrically conductive microparticulate filler comprises a metal selected from the group consisting of silver, gold, platinum, palladium, nickel and copper.
Claim 9
Dependent Claim
24 words
The resin formulation of claim 7 wherein the electrically conductive microparticulate filler comprises silver flake or silver powder having a tap density of >3.0.
Claim 10
Dependent Claim
24 words
The resin formulation of claim 8 wherein the electrically conductive microparticulate filler comprises silver powder or silver flake having a tap density of >4.0.
Claim 11
Dependent Claim
137 words
The resin formulation of claim 1 comprising about 20 to about 50 weight percent of a resin composition comprising about 50 to about 80 weight percent of a vinyl ester or an unsaturated polyester, about 10 to about 30 weight percent of a thermoplastic resin, and about 10 to about 50 weight percent of a bifunctional olefinic monomer selected from the group consisting of divinylbenzene, divinylpyridine, diallyl phthalate, and diallyl isophthalate, about 50 to about 80 weight percent of an electrically conductive microparticulate filler comprising a metal selected from the group consisting of silver, gold, palladium, nickel and copper, and a free radical initiating agent in an amount effective to promote thermosetting of said formulation to a shape-retaining, electrically conducting resin matrix in about 30 seconds to about 5 minutes at about 100° to about 200° C.
Claim 12
Dependent Claim
16 words
The resin formulation of claim 10 wherein the thermoplastic resin is a low profile thermoplastic resin.
Claim 13
Dependent Claim
16 words
The resin formulation of claim 11 wherein the free radical cross-linkable polymer is a vinyl ester.
Claim 14
Dependent Claim
16 words
The resin formulation of claim 12 wherein the unsaturated monomer is diallyl phthalate or diallyl isophthalate.
Claim 15
Dependent Claim
23 words
The resin formulation of claim 13 wherein the electrically conductive microparticulate filler comprises silver powder or silver flake having a tap density >3.0.
Claim 16
Dependent Claim
41 words
The resin formulation of claim 14 wherein the free radical initiating agent is in an amount effective to promote thermosetting of said formulation to a shape-retaining, electrically conducting resin matrix in less than 2 minutes at a temperature of 200° C.
Claim 17
Dependent Claim
41 words
The resin formulation of claim 1 wherein the free radical initiating agent is in an amount effective to promote thermosetting of said formulation to a shape-retaining, electrically conducting resin matrix in less than 2 minutes at a temperature of 200° C.
Claim 18
Dependent Claim
18 words
The resin formulation of claim 1 further comprising about 0.05 to about 1 weight percent of an antioxidant.
References Cited (Backward Citations)
US4288571A
Cited
GB1372608A
Cited
US3903027A
Cited
JPS53102930A
Cited
US4327369A
Cited
EP0099717A2
Cited
JPS60223872A
Cited
US4767806A
Cited
JPH01103906A
Cited
JPH01251625A
Cited
JPH0395275A
Cited
JPH03152177A
Cited
US5158708A
Cited
US5250228A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-12-11 | 1999-06-12 | 1999-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-12-11 | 2003-06-12 | 2003-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-12-11 | 2007-06-12 | 2007-12-12 | $7700.00 | Window Closed / Lapsed |