Patent US5472537A successfully refreshed from Google Patents.
US5472537A
Expired / Lapsed
US
⏱️ 0.0 years remaining
End capped fibrous filter making
Assignee: Pall Corp
•
Filing: 1995-04-20
•
Granted: 1995-12-05
•
Expires: 2015-04-20
Abstract
Abstract Bonded end capped tubular or cylindrical filter elements are formed by fusing a fibrous mass of non-woven, intertwining, mechanically entangled, synthetic polymeric, microfibers possessing a temperature of dimensional heat instability and end caps formed from a dynamic vulcanizate comprising ethylene-propylene-diene-monomer (EPDM) rubber particles dispersed in a polypropylene matrix wherein the fused end capped filter exhibits minimal fiber pull back.
Inventors
- 👤 Raymond T. Friel
- 👤 Colin F. Harwood
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 23:15
CPC Classifications
B; B01; B01D; B01D29/00; B01D29/11; B01D29/111
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
172 words
A method for manufacturing end capped, cylindrical, fibrous, filter elements formed from a lofty, fibrous mass of microfibers composed from a synthetic polymer having a selected temperature of dimensional/conformational heat instability and end caps formed from a dynamic rubber vulcanizate, the method comprising the steps of: generating sufficient heat energy in the end cap to soften a selected portion thereof to induce bonding of the microfibers in the selected portion between the end cap to the fibrous mass of microfibers and filter element but insufficient to melt or cause substantial dimensional instability in the microfibers outside of the bonding zone; contacting the fibrous element with the end cap in a manner to fuse the end cap and the fibrous mass to a selected depth substantially in the selected portion; and cooling the selected portion to solidify the end cap material and to bond the portion of the fibrous mass in contact therewith in a manner to prevent fiber pull back of said fibrous mass and to establish a unitary, integrated filter element.
Claim 2
Independent Claim
172 words
A method for manufacturing end capped, cylindrical, fibrous, filter elements formed from a lofty, fibrous mass of microfibers composed from a synthetic polymer having a selected temperature of dimensional/conformational heat instability and end caps formed from a dynamic rubber vulcanizate, the method comprising the steps of: generating sufficient heat energy in the end cap to soften a selected portion thereof to induce bonding of the microfibers in the selected portion between the end cap to the fibrous mass of microfibers and filter element but insufficient to melt or cause substantial dimensional instability in the microfibers outside of the bonding zone; contacting the fibrous element with the end cap in a manner to fuse the end cap and the fibrous mass to a selected depth substantially in the selected portion; and cooling the selected portion to solidify the end cap material and to bond the portion of the fibrous mass in contact therewith in a manner to prevent fiber pull back of said fibrous mass and to establish a unitary, integrated filter element.
Claim 3
Dependent Claim
89 words
The method according to claim 1 where the fibrous mass has a substantially constant voids volume and a varying fiber diameter to achieve a graded pore structure and the dynamic vulcanizate is ethylene-propylene-diene-monomer (EPDM) rubber particles dispersed in a polypropylene matrix, and further comprising the steps of rotating the end cap and cylindrical fibrous structure relative to each other and pressing the fibrous mass into the end cap under pressure for friction contact and heat generation to provide bonding of the filter element to the end cap upon cooling.
Claim 4
Dependent Claim
70 words
The method according to claim 2 wherein the fibrous mass is composed of amorphous polypropylene fibers and has a substantially constant voids volume and a varying fiber diameter to achieve a graded pore structure and the dynamic vulcanizate is ethylene-propylene-diene-monomer (EPDM) rubber particles dispersed in a polypropylene matrix, wherein the end cap is rotated and the cylindrical fibrous fiber structure is stationary and wherein the fibers and vulcanizate are fused.
Claim 5
Dependent Claim
22 words
The method according to claim 3 wherein the end cap is rotated at a rate of about 500 to about 4000 rpm.
Claim 6
Dependent Claim
28 words
The method according to claim 4 wherein the cylindrical filter structure is pressed into the end cap at an initial pressure of about 20 to about 100 psi.
Claim 7
Dependent Claim
34 words
The method according to claim 5 further including the step of regulating the application pressure where the pressure applied to the cylindrical filter structure diminishes during the period of contact with the end cap.
Claim 8
Dependent Claim
18 words
The method according to claim 6 wherein the pressure is diminished from about 90 to about 60 psi.
Claim 9
Dependent Claim
33 words
The method according to claim 1 wherein the dynamic vulcanizate is ethylene-propylene-diene-monomer (EPDM) rubber particles dispersed in a polypropylene matrix, and wherein the end cap vulcanizate is heated with an external heating source.
Claim 10
Dependent Claim
54 words
The method according to claim 8 wherein the end cap is heated to a temperature exceeding its softening point but below the end cap vulcanizate degradation temperature and wherein the temperature is insufficient to melt the fibers, the method further including the step of vulcanizate penetration into the fibrous mass in the selected portion.
Claim 11
Dependent Claim
45 words
A method according to claim 8 wherein the fibrous mass has a substantially constant voids volume and a varying fiber diameter to achieve a graded pore structure and wherein the end cap is heated to a temperature of from about 350° to about 450° F.
Claim 12
Dependent Claim
45 words
The method according to claim 8 wherein the fibrous mass has a substantially constant voids volume and a varying fiber diameter to achieve a graded pore size and wherein the end cap is heated to a temperature of from about 350° to about 450° F.
Claim 13
Independent Claim
186 words
A method of end capping a fibrous filter cartridge comprising a mass of intertwined and mechanically entangled, non-woven, synthetic, polymeric microfibers possessing a particular temperature of dimensional heat instability and supported on a core to an end cap formed of a polypropylene rubber blend having a selected softening temperature, the method comprising the steps of rotating the end cap at a high rotational rate; pressing the filter cartridge into the end cap at sufficient pressure and for a sufficient number of revolutions to induce frictional heating of the end cap portion in contact with the filter cartridge to generate heat energy sufficient to soften the end cap portion; embedding the end of the filter cartridge in the heated end cap portion where the heat energy is insufficient to induce dimensional heat instability of the fibers outside of the embedded end but sufficient to fuse the mass of microfibers of the embedded end to the end cap where fiber pull back is prevented and the structural integrity of the filter cartridge is preserved; and cooling the end cap to provide an integrated, unitary end capped filter cartridge.
Claim 14
Independent Claim
186 words
A method of end capping a fibrous filter cartridge comprising a mass of intertwined and mechanically entangled, non-woven, synthetic, polymeric microfibers possessing a particular temperature of dimensional heat instability and supported on a core to an end cap formed of a polypropylene rubber blend having a selected softening temperature, the method comprising the steps of rotating the end cap at a high rotational rate; pressing the filter cartridge into the end cap at sufficient pressure and for a sufficient number of revolutions to induce frictional heating of the end cap portion in contact with the filter cartridge to generate heat energy sufficient to soften the end cap portion; embedding the end of the filter cartridge in the heated end cap portion where the heat energy is insufficient to induce dimensional heat instability of the fibers outside of the embedded end but sufficient to fuse the mass of microfibers of the embedded end to the end cap where fiber pull back is prevented and the structural integrity of the filter cartridge is preserved; and cooling the end cap to provide an integrated, unitary end capped filter cartridge.
Claim 15
Dependent Claim
47 words
The method according to claim 12 wherein the filter cartridge has a substantially constant voids volume and a varying fiber diameter to achieve a graded pore structure and the polypropylene rubber blend is a dynamic vulcanizate composed of ethylene-propylene-diene-monomer (EPDM) rubber particles dispersed in a polypropylene matrix.
Claim 16
Dependent Claim
44 words
The method according to claim 13 wherein the end cap is rotated at a rate of about 1725 rpm and the filter cartridge is pressed into the end cap for about 20 to about 35 revolutions at an initial pressure of about 90 psi.
Claim 17
Dependent Claim
37 words
The method according to claim 13 wherein the rotational rate of the end cap varies for a predetermined number of revolutions sufficient to achieve fusing of the fibrous mass of the filter cartridge to the end cap.
Claim 18
Independent Claim
32 words
A method for manufacturing a filter cartridge comprising: providing a filter element having microfibers; providing a filter end cap made from a dynamic vulcanizate; and embedding said microfibers into said end cap.
Claim 19
Independent Claim
32 words
A method for manufacturing a filter cartridge comprising: providing a filter element having microfibers; providing a filter end cap made from a dynamic vulcanizate; and embedding said microfibers into said end cap.
Claim 20
Dependent Claim
54 words
The method according to claim 16, wherein the embedding step includes generating sufficient heat energy in the end cap to soften a bonding zone thereof and to induce bonding of the microfibers present in the bonding zone but insufficient to melt or cause substantial dimensional instability in the microfibers outside of the bonding zone.
Claim 21
Dependent Claim
56 words
The method of claim 17, including the step of cooling the bonding zone to solidify the end cap material and to bond the portion of the microfibers in contact therewith in a manner to prevent fiber pull back of the microfibers and to establish a unitary, integrated filter element wherein the microfibers and vulcanizate are fused.
Claim 22
Dependent Claim
32 words
The method of claim 16, wherein the embedding step includes contacting the microfibers with the end cap in a manner to fuse the end cap and the microfibers to a selected depth.
Claim 23
Dependent Claim
36 words
The method of claim 16, wherein the filter element is formed from a fibrous mass of the microfibers and has a substantially constant voids volume and a varying fiber diameter to achieve a graded pore structure.
Claim 24
Dependent Claim
18 words
The method of claim 16, wherein the dynamic vulcanizate is ethylene-propylene-diene-monomer rubber particles dispersed in a polypropylene matrix.
Claim 25
Dependent Claim
76 words
The method of claim 16, further including the steps of rotating the end cap at a rate of about 500 to about 4000 rpm relative to the filter element, pressing the microfibers into the end cap at an initial pressure of about 20 to about 100 psi for friction contact and heat generation, and regulating the application pressure wherein the pressure applied to the filter element diminishes during the period of contact with the end cap.
Claim 26
Dependent Claim
49 words
The method according to claim 16, wherein the end cap is heated to a temperature exceeding its softening point but below the end cap vulcanizate degradation temperature and wherein the temperature is insufficient to melt the microfibers, the method further including the step of vulcanizate penetration into the microfibers.
References Cited (Backward Citations)
US3457339A
Cited
GB1199005A
Cited
GB1149467A
Cited
US3899378A
Cited
US3904470A
Cited
US3972973A
Cited
US4113539A
Cited
US4442004A
Cited
US4726901A
Cited
US4956089A
Cited
US4725323A
Cited
US4731184A
Cited
US4678577A
Cited
US4832615A
Cited
GB2216090A
Cited
US5102542A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-12-04 | 1999-06-05 | 1999-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-12-04 | 2003-06-05 | 2003-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-12-04 | 2007-06-05 | 2007-12-05 | $7700.00 | Window Closed / Lapsed |