Abstract Caprolactam is obtained from mixtures which contain polymers or thermoplastic molding materials having the repeating unit -N(H)-(CH2)5-C(O)- (a) by cleavage at elevated temperatures in the presence of a base under reduced pressure or (b) in the presence of water, by using a mixture essentially comprising from 50 to 99.9% by weight of a polymer or of a thermoplastic molding material having the repeating unit -N(H)-(CH2)5-C(O)- from 0.1 to 50% by weight of additives selected from the group consisting of inorganic fillers, organic and inorganic pigments and dyes, from 0 to 10% by weight of organic and/or inorganic additives, from 0 to 40% by weight of non-polyamide-containing polymers and from 0 to 20% by weight of polyamides, with the exception of polycaprolactam and copolyamides prepared from caprolactam, and carrying out the cleavage in the presence of a base under reduced pressure, the water content of the mixture used being not more than 0.01% by weight, or carrying out the cleavage in the presence of water without the addition of acid or base at from 270 DEG to 350 DEG C. and a weight ratio of water to polymer or thermoplastic molding material of from 1:1 to 20:1 and in a reaction time of less than 3 hours.
A process for obtaining caprolactam from mixtures which contain polymers or thermoplastic molding materials having the repeating unit --N(H)--(CH.sub.2).sub.5 --C(O)-- (a) by cleavage at elevated temperatures in the presence of a base under reduced pressure or (b) in the presence of water, which comprises using a mixture essentially comprising from 50 to 99.9% by weight of a polymer or of a thermoplastic molding material having the repeating unit --N(H)--(CH.sub.2).sub.5 --C(O)-- 0.1 to 50% by weight of additives selected from the group consisting of inorganic fillers, organic and inorganic pigments and dyes, from 0 to 10% by weight of organic or inorganic additives, from 0 to 40% by weight of non-polyamide-containing polymers and from 0 to 20% by weight of polyamides, with the exception of polycaprolactam and copolyamides prepared from caprolactam, and carrying out the cleavage in the presence of a base under reduced pressure, the water content of the mixture used being not more than 0.01% by weight, or carrying out the cleavage in the presence of water without the addition of acid or base at from 270° to 350° C. and a weight ratio of water to polymer or thermoplastic molding material of from 1:1 to 20:1 and in a reaction time of less than 3 hours.
Claim 2
Dependent Claim
208 words
A process for obtaining caprolactam from mixtures which contain polymers or thermoplastic molding materials having the repeating unit --N(H)--(CH.sub.2).sub.5 --C(O)-- (a) by cleavage at elevated temperatures in the presence of a base under reduced pressure or (b) in the presence of water, which comprises using a mixture essentially comprising from 50 to 99.9% by weight of a polymer or of a thermoplastic molding material having the repeating unit --N(H)--(CH.sub.2).sub.5 --C(O)-- 0.1 to 50% by weight of additives selected from the group consisting of inorganic fillers, organic and inorganic pigments and dyes, from 0 to 10% by weight of organic or inorganic additives, from 0 to 40% by weight of non-polyamide-containing polymers and from 0 to 20% by weight of polyamides, with the exception of polycaprolactam and copolyamides prepared from caprolactam, and carrying out the cleavage in the presence of a base under reduced pressure, the water content of the mixture used being not more than 0.01% by weight, or carrying out the cleavage in the presence of water without the addition of acid or base at from 270° to 350° C. and a weight ratio of water to polymer or thermoplastic molding material of from 1:1 to 20:1 and in a reaction time of less than 3 hours.