US5439164A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Methods for joining copper or its alloys
Assignee: Panasonic Holdings Corp
•
Filing: 1993-06-04
•
Granted: 1995-08-08
•
Expires: 2013-06-04
Abstract
Abstract The copper or its alloys can be bonded to each other or can be bonded to noble metals or to other metals whose surface is covered with a noble metal thin film in an oxidative atmosphere. The surface of the copper or its alloys to be bonded should be covered with the layer of a noble metal thin film or a metal oxide remover or a conductive paste mainly consisting of a copper or copper alloy particles and the metal oxide remover. This method can be applied to a metallurgical industry and also to an electronics industry. This method is especially suitable for the production of a multilayered printed wiring board.
Inventors
- 👤 Yo Hasegawa
- 👤 Masahiro Nagasawa
- 👤 Masahide Tsukamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:01
CPC Classifications
B; B23; B23K; B23K20/00; B23K20/16; B23K35/00; B23K35/001; B23K35/007; H; H05; H05K; H05K3/00; H05K3/40; H05K3/4038; H05K3/4053; H05K3/4069; B23K2101/00; B23K2101/36; B23K35/02; B23K35/0222; B23K35/0244; B23K35/025; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/095; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2201/10; H05K2201/10227; H05K2201/10378; H05K2203/00; H05K2203/14; H05K2203/1461; H05K3/46; H05K3/4611; H05K3/4614; H05K3/462; H05K3/4623
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
112 words
A method for joining at least two contacting surfaces of Cu or Cu alloy by diffusing Cu atoms into an opposite metal surface from the Cu or Cu alloy surface, which comprises: providing the contacting surfaces with a layer selected from the group comprising a noble metal thin layer, a metal oxide remover layer and a conductive paste layer mainly consisting of a Cu or Cu alloy particles and the metal oxide remover; and pressing the contacting metal surfaces at a temperature higher than about 170° C. whereat the Cu atoms at interface of the Cu or Cu alloy surfaces to be joined can be diffused, to give a joined metal body.
Claim 2
Independent Claim
112 words
A method for joining at least two contacting surfaces of Cu or Cu alloy by diffusing Cu atoms into an opposite metal surface from the Cu or Cu alloy surface, which comprises: providing the contacting surfaces with a layer selected from the group comprising a noble metal thin layer, a metal oxide remover layer and a conductive paste layer mainly consisting of a Cu or Cu alloy particles and the metal oxide remover; and pressing the contacting metal surfaces at a temperature higher than about 170° C. whereat the Cu atoms at interface of the Cu or Cu alloy surfaces to be joined can be diffused, to give a joined metal body.
Claim 3
Dependent Claim
30 words
The method for joining at least two contacting surfaces of Cu or Cu alloy according to claim 1, wherein the contacting surfaces are included in a multilayer printed wiring board.
Claim 4
Dependent Claim
38 words
The method for joining at least two contacting surfaces of Cu or Cu alloy according to claim 1, wherein the metal oxide remover is selected from the group comprising carboxylic acids and polymers or oligomers having carboxyl groups.
Claim 5
Independent Claim
114 words
A method for joining at least two contacting metal surfaces, wherein one of the contacting metal surfaces is comprised of Cu or Cu alloy coated with a layer of a metal oxide remover, and the other contacting metal surface is comprised of a noble metal or alloy thereof or of any other metal provided with a thin layer of a noble metal or alloy thereof by means of electroplating, vacuum deposition or sputtering, comprising pressing the two contacting metal surfaces at a temperature higher than about 170° C. so that the Cu atoms at interface of the Cu or Cu alloy surfaces to be joined can be diffused, to give a joined metal body.
Claim 6
Independent Claim
114 words
A method for joining at least two contacting metal surfaces, wherein one of the contacting metal surfaces is comprised of Cu or Cu alloy coated with a layer of a metal oxide remover, and the other contacting metal surface is comprised of a noble metal or alloy thereof or of any other metal provided with a thin layer of a noble metal or alloy thereof by means of electroplating, vacuum deposition or sputtering, comprising pressing the two contacting metal surfaces at a temperature higher than about 170° C. so that the Cu atoms at interface of the Cu or Cu alloy surfaces to be joined can be diffused, to give a joined metal body.
Claim 7
Independent Claim
120 words
A method for joining at least two contacting surfaces of Cu or Cu alloy by diffusing Cu atoms into an opposite metal surface from the Cu or Cu alloy surface, which comprises: providing the contacting surfaces with a layer selected from the group consisting of a noble metal thin layer, a metal oxide remover layer and a conductive paste layer mainly consisting of a Cu or Cu alloy particles and the metal oxide remover; and pressing the contacting metal surfaces in air or oxidative atmosphere at a temperature of at least about 170° C. so that the Cu atoms at interface of the Cu or Cu alloy surfaces to be joined can be diffused, to give a joined metal body.
Claim 8
Independent Claim
120 words
A method for joining at least two contacting surfaces of Cu or Cu alloy by diffusing Cu atoms into an opposite metal surface from the Cu or Cu alloy surface, which comprises: providing the contacting surfaces with a layer selected from the group consisting of a noble metal thin layer, a metal oxide remover layer and a conductive paste layer mainly consisting of a Cu or Cu alloy particles and the metal oxide remover; and pressing the contacting metal surfaces in air or oxidative atmosphere at a temperature of at least about 170° C. so that the Cu atoms at interface of the Cu or Cu alloy surfaces to be joined can be diffused, to give a joined metal body.
Claim 9
Dependent Claim
21 words
A method according to claim 5 wherein the contacting metal surfaces are pressed at a temperature higher than about 170° C.
References Cited (Backward Citations)
FR1213876A
Cited
US4383363A
Cited
US4228944A
Cited
EP0138672A2
Cited
US4569876A
Cited
US4768787A
Cited
JPH04146972A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-08-07 | 1999-02-06 | 1999-08-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-08-07 | 2003-02-06 | 2003-08-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-08-07 | 2007-02-06 | 2007-08-08 | $7700.00 | Window Closed / Lapsed |