Point bonded nonwoven fabrics
Assignee: Kimberly Clark Worldwide Inc
•
Filing: 1994-02-25
•
Granted: 1995-06-13
•
Expires: 2014-02-25
Abstract
Abstract The present invention provides a point bonded polyolefin nonwoven fabric fabricated from conjugate fibers containing a polyolefin and a polyamide. Advantageously, the nonwoven fabric can be point bonded at a temperature significantly below conventional polyolefin nonwoven web bonding temperatures and in a wide range of different bonding temperatures without significantly sacrificing its tensile strength. Additionally provided is a process for producing the point bonded nonwoven fabric.
Inventors
- 👤 Ty J. Stokes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 02:27
CPC Classifications
D; D01; D01F; D01F8/00; D01F8/04; D01F8/06; D04; D04H; D04H3/00; D04H3/08; D04H3/16; D01F8/12; D04H1/00; D04H1/40; D04H1/54; D04H1/541; D04H1/5412; D04H1/5414; D04H1/542; D04H1/544; D04H1/549; D04H1/5416; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1023; Y10T156/17; Y10T156/1702; Y10T156/1712; Y10T156/1741; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24595; Y10T428/24603; Y10T428/24802; Y10T428/24826; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2931; Y10T442/00; Y10T442/60; Y10T442/637; Y10T442/64; Y10T442/641
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
87 words
A process for producing a point-bonded nonwoven fabric of conjugate fibers having strong bond points, said conjugate fibers comprising a polyolefin and a polyamide, comprising: a) depositing said conjugate fibers on a forming surface to form a nonwoven web, b) passing said web into a nip formed by two abutting bonding rolls, said bonding rolls being heated to a temperature lower than about 10° C. below the melting point of said polyolefin and providing a nip pressure on raised points between about 3,000 to about 180,000 psi.
Claim 2
Dependent Claim
87 words
A process for producing a point-bonded nonwoven fabric of conjugate fibers having strong bond points, said conjugate fibers comprising a polyolefin and a polyamide, comprising: a) depositing said conjugate fibers on a forming surface to form a nonwoven web, b) passing said web into a nip formed by two abutting bonding rolls, said bonding rolls being heated to a temperature lower than about 10° C. below the melting point of said polyolefin and providing a nip pressure on raised points between about 3,000 to about 180,000 psi.
Claim 3
Dependent Claim
33 words
The process of claim 1 wherein said point bonded fabric has a machine direction grab tensile strength of at least 15 lbs as measured in accordance with Federal Standard Methods 191A, Method 5100.
Claim 4
Dependent Claim
31 words
The process of claim 1 wherein said point bonded fabric has a grab tensile strength of at least 25 lbs as measured in accordance with Federal Standard Methods 191A, Method 5100.
Claim 5
Dependent Claim
22 words
The process of claim 1 wherein said conjugate fibers have a configuration selected from the group consisting of sheath/core and island-in-sea configurations.
Claim 6
Dependent Claim
13 words
The process of claim 1 wherein said conjugate fibers have a sheath/core configuration.
Claim 7
Dependent Claim
30 words
The process of claim 1 wherein said bonding rolls are heated to a temperature between about 20° C. to about 60° C. lower than the melting point of said polyolefin.
Claim 8
Dependent Claim
26 words
The process of claim 1 wherein said polyolefin is selected from the group consisting of polyethylene, polypropylene, polybutylene, polypentene, polyvinyl acetate, and copolymers and blends thereof.
Claim 9
Dependent Claim
18 words
The process of claim 1 wherein said polyolefin is selected from the group consisting of polypropylene and polyethylene.
Claim 10
Dependent Claim
36 words
The process of claim 1 wherein said polyamide is selected from the group consisting of polycaprolactam, polyhexamethylenediamine adipamide, copolymers of caprolactam and hexamethylenediamine adipamide, copolymers of caprolactam or hexamethylenediamine adipamide and ethylene oxide, and blends thereof.
Claim 11
Dependent Claim
16 words
A point bonded nonwoven fabric of conjugate fibers produced according to the process of claim 1.
Claim 12
Dependent Claim
101 words
A point bonded nonwoven conjugate fiber web having point bonds that are stronger than the conjugate fibers comprising said web, said conjugate fibers comprising a polyolefin component and a polyamide component, said polymer components being arranged to occupy substantially distinct sections of each of said conjugate fibers along the length of said fibers, and said bond points being formed in a nip between two abutting heated bonding rolls which are heated to a temperature lower than about 10° C. below the melting point of said polyolefin and providing a nip pressure on raised points between about 3,000 to about 180,000 psi.
Claim 13
Dependent Claim
101 words
A point bonded nonwoven conjugate fiber web having point bonds that are stronger than the conjugate fibers comprising said web, said conjugate fibers comprising a polyolefin component and a polyamide component, said polymer components being arranged to occupy substantially distinct sections of each of said conjugate fibers along the length of said fibers, and said bond points being formed in a nip between two abutting heated bonding rolls which are heated to a temperature lower than about 10° C. below the melting point of said polyolefin and providing a nip pressure on raised points between about 3,000 to about 180,000 psi.
Claim 14
Dependent Claim
25 words
The point bonded nonwoven web of claim 11 wherein said conjugate fibers have a configuration selected from the group consisting of sheath/core and island-in-sea configurations.
Claim 15
Dependent Claim
16 words
The point bonded nonwoven web of claim 11 wherein said conjugate fibers have a sheath/core configuration.
Claim 16
Dependent Claim
33 words
The point bonded nonwoven web of claim 11 wherein said bonding rolls are heated to a temperature between about 20° C. to about 60° C. lower than the melting point of said polyolefin.
Claim 17
Dependent Claim
29 words
The point bonded nonwoven web of claim 11 wherein said polyolefin is selected from the group consisting of polyethylene, polypropylene, polybutylene, polypentene, polyvinyl acetate, and copolymers and blends thereof.
Claim 18
Dependent Claim
39 words
The point bonded nonwoven web of claim 11 wherein said polyamide is selected from the group consisting of polycaprolactam, polyhexamethylenediamine adipamide, copolymers of caprolactam and hexamethylenediamine adipamide, copolymers of caprolactam or hexamethylenediamine adipamide and ethylene oxide, and blends thereof.
Claim 19
Dependent Claim
50 words
A point bonded nonwoven fiber web having a wide bonding temperature range, said fiber web comprising conjugate fibers which comprise a polyolefin component and a polyamide component and said polymer components being arranged to occupy substantially distinct sections of each of said conjugate fibers along the length of said fibers.
Claim 20
Dependent Claim
50 words
A point bonded nonwoven fiber web having a wide bonding temperature range, said fiber web comprising conjugate fibers which comprise a polyolefin component and a polyamide component and said polymer components being arranged to occupy substantially distinct sections of each of said conjugate fibers along the length of said fibers.
Claim 21
Dependent Claim
16 words
The nonwoven web of claim 17 wherein said conjugate fibers have a sheath/core or island-in-sea configuration.
Claim 22
Dependent Claim
27 words
The nonwoven web of claim 17 wherein said polyolefin is selected from the group consisting of polyethylene, polypropylene, polybutylene, polypentene, polyvinyl acetate, and copolymers and blends thereof.
Claim 23
Dependent Claim
37 words
The nonwoven web of claim 17 wherein said polyamide is selected from the group consisting of polycaprolactam, polyhexamethylenediamine adipamide, copolymers of caprolactam and hexamethylenediamine adipamide, copolymers of caprolactam or hexamethylenediamine adipamide and ethylene oxide, and blends thereof.
References Cited (Backward Citations)
US3117906A
Cited
US3200440A
Cited
US3297807A
Cited
US3536802A
Cited
US3780149A
Cited
US3725192A
Cited
US4035219A
Cited
US3788940A
Cited
US3855045A
Cited
US3895151A
Cited
US3940302A
Cited
US3787162A
Cited
US3924045A
Cited
US4005169A
Cited
US4211816A
Cited
US4396366A
Cited
US4306929A
Cited
US4424258A
Cited
US4424257A
Cited
EP0088744A2
Cited
US4774124A
Cited
US4601949A
Cited
US4588630A
Cited
US4555430A
Cited
US4596742A
Cited
US4761322A
Cited
US5071705A
Cited
US5143786A
Cited
US4806299A
Cited
US4981749A
Cited
US4830904A
Cited
US5167764A
Cited
US5207970A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-12 | 1998-12-12 | 1999-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-12 | 2002-12-12 | 2003-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-12 | 2006-12-12 | 2007-06-13 | $7700.00 | Window Closed / Lapsed |