Thixotropic foamable organosiloxane compositions
Assignee: Dow Silicones Corp
•
Filing: 1994-05-18
•
Granted: 1995-05-09
•
Expires: 2014-05-18
Abstract
Abstract The presence in foamable, curable organosiloxane compositions of a hydrogenated glyceride of an ethylenically unsaturated carboxylic acid imparts sufficient thixotropy to the uncured composition to inhibit flow without adversely affecting desirable properties of the cured foam such as density and texture.
Inventors
- 👤 Brian P. Loiselle
- 👤 Thomas G. Jacobs, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:07
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
161 words
In an improved foamable organosiloxane composition comprising A. a liquid polyorganosiloxane containing at least two reactive groups per molecule selected from the group consisting of silanol groups and alkenyl radicals; B. an amount sufficient to foam and cure said composition of an organohydrogensiloxane containing at least three silicon-bonded hydrogen atoms per molecule wherein there is no more than one of said hydrogen atoms per silicon atom; C. a compound containing at least one carbinol or silanol group per molecule, and D. as the catalyst, an amount of a metal from the platinum group of the periodic table or a compound of said metal sufficient to promote foaming and curing of said composition, the improvement comprising the presence in said composition of a thixotropic additive in an amount sufficient to prevent substantial flowing of said composition prior to curing, said additive consisting essentially of the hydrogenated glyceride of at least one ethylenically unsaturated hydroxycarboxylic acid containing from 12 to 20 carbon atoms.
Claim 2
Dependent Claim
161 words
In an improved foamable organosiloxane composition comprising A. a liquid polyorganosiloxane containing at least two reactive groups per molecule selected from the group consisting of silanol groups and alkenyl radicals; B. an amount sufficient to foam and cure said composition of an organohydrogensiloxane containing at least three silicon-bonded hydrogen atoms per molecule wherein there is no more than one of said hydrogen atoms per silicon atom; C. a compound containing at least one carbinol or silanol group per molecule, and D. as the catalyst, an amount of a metal from the platinum group of the periodic table or a compound of said metal sufficient to promote foaming and curing of said composition, the improvement comprising the presence in said composition of a thixotropic additive in an amount sufficient to prevent substantial flowing of said composition prior to curing, said additive consisting essentially of the hydrogenated glyceride of at least one ethylenically unsaturated hydroxycarboxylic acid containing from 12 to 20 carbon atoms.
Claim 3
Dependent Claim
98 words
A composition according to claim 1 wherein said polyorganosiloxane is a polydiorganosiloxane wherein at least 90 percent of the repeating units are diorganosiloxane units represented by the general formula R 1 R 2 SiO where R 1 and R 2 are individually selected from monovalent unsubstituted and substituted hydrocarbon radicals that typically contain from 1 to 10 carbon atoms, said alkenyl radicals are vinyl radicals, any silanol-containing polyorganosiloxane constitutes at least a portion of ingredient A; said compound containing at least one carbinol group per molecule as an alcohol, and said thixotropic additive is a hydrogenated castor oil.
Claim 4
Dependent Claim
130 words
A composition according to claim 2 wherein said thixotropic additive constitutes from 0.5 to 5 weight percent of said composition; the monovalent hydrocarbon radicals present in said polyorganosiloxane and said organohydrogensiloxane are selected from the group consisting of alkyl, phenyl and 3,3,3-trifluoropropyl; said composition cures by a hydrosilation reaction; said organohydrogensiloxane comprises 1) a linear organosiloxane copolymer exhibiting a viscosity of from 0.01 to 10 Pa.s at 25° C. and consisting essentially of dialkylsiloxane and alkylhydrogensiloxane units with trialkylsiloxy terminal units, and 2) a linear polyorganohydrogensiloxane; the molar ratio of silicon-bonded hydrogen atoms to the combination of alkenyl radicals, silanol groups and carbinol groups is from 3.5:1 to 5.5:1; and said composition further comprises a non-linear organosiloxane copolymer comprising trimethylsiloxy and SiO 4/2 units and at least one non-reinforcing filler.
Claim 5
Dependent Claim
61 words
A composition according to claim 3 where said thixotropic additive constitutes from 1 to 4 weight percent of said composition, at least one of the hydrocarbon radicals bonded to each silicon atom of said polyorganosiloxane and said organohydrogensiloxane is a methyl radical, and said linear organosiloxane copolymer constitutes at least half of the total weight of organohydrogensiloxane present in said composition.
Claim 6
Dependent Claim
26 words
A composition according to claim 1 wherein said composition is packaged in at least two containers, said organohydrogensiloxane and said catalyst being located in different containers.
References Cited (Backward Citations)
US3923705A
Cited
US4026843A
Cited
US4189545A
Cited
US4490488A
Cited
US4497919A
Cited
EP0198536A1
Cited
US4590222A
Cited
US4599367A
Cited
JPH0238309A
Cited
US5225452A
Cited
US5252627A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-05-08 | 1998-11-07 | 1999-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-05-08 | 2002-11-07 | 2003-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-05-08 | 2006-11-07 | 2007-05-09 | $7700.00 | Window Closed / Lapsed |