US5397732A
Expired / Lapsed
US
⏱️ 0.0 years remaining
PBLOCOS with sandwiched thin silicon nitride layer
Assignee: Transpacific IP Ltd
•
Filing: 1993-07-22
•
Granted: 1995-03-14
•
Expires: 2013-07-22
Abstract
Abstract A method of forming a silicon oxide isolation region with reduced bird's beak length on the surface of a silicon substrate is described. A layer of silicon oxide is formed on the surface of the silicon substrate. A first layer of silicon nitride is formed on the surface of the silicon oxide layer, to prevent diffusion of oxygen into the silicon oxide layer and the substrate during subsequent oxidation steps, thereby reducing the bird's beak length. A layer of polysilicon is formed on the surface of the silicon nitride layer. A second layer of silicon nitride is formed on the surface of the polysilicon layer. The second silicon nitride layer, the polysilicon layer and the first silicon nitride layer are patterned to form an oxidation mask and to form an opening over the silicon oxide layer. The silicon substrate is ion implanted through the opening to form a channel stop implant. The silicon substrate and silicon oxide layer in the region not masked by the oxidation mask are oxidized to form the silicon oxide isolation region. A thin surface oxide layer forms on the surface of the second silicon nitride layer during this oxidation step. The thin surface oxide layer and second silicon nitride layer are removed. The polysilicon layer is oxidized, and then removed. The first silicon nitride layer is then removed. Finally, the silicon oxide layer is removed to complete formation of the silicon oxide isolation region.
Inventors
- 👤 Chung-Zen Chen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:48
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/61; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/10; H10W10/13
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
235 words
A method of forming a silicon oxide isolation region with reduced bird's beak length, on the surface of a silicon substrate, comprising: forming a layer of silicon oxide on the surface of said silicon substrate; forming a first layer of silicon nitride having a thickness of between about 300 and 400 Angstroms on the surface of said silicon oxide layer, to prevent diffusion of oxygen into said silicon oxide layer and said silicon substrate during subsequent oxidation steps, thereby reducing said bird's beak length; forming a layer of polysilicon in-situ doped on the surface of said first silicon nitride layer; forming a second layer of silicon nitride on the surface of said polysilicon layer; patterning said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer to form an oxidation mask and to form an opening over said silicon oxide layer; ion implanting said silicon substrate through said opening to form a channel stop implant; oxidizing said silicon substrate in the area not masked by said oxidation mask, to form said silicon oxide isolation region, wherein during the oxidizing step a thin surface oxide layer forms on the surface of said second silicon nitride layer; removing said thin surface oxide layer; simultaneously removing said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer; and removing said silicon oxide layer, to complete formation of said silicon oxide isolation region.
Claim 2
Independent Claim
235 words
A method of forming a silicon oxide isolation region with reduced bird's beak length, on the surface of a silicon substrate, comprising: forming a layer of silicon oxide on the surface of said silicon substrate; forming a first layer of silicon nitride having a thickness of between about 300 and 400 Angstroms on the surface of said silicon oxide layer, to prevent diffusion of oxygen into said silicon oxide layer and said silicon substrate during subsequent oxidation steps, thereby reducing said bird's beak length; forming a layer of polysilicon in-situ doped on the surface of said first silicon nitride layer; forming a second layer of silicon nitride on the surface of said polysilicon layer; patterning said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer to form an oxidation mask and to form an opening over said silicon oxide layer; ion implanting said silicon substrate through said opening to form a channel stop implant; oxidizing said silicon substrate in the area not masked by said oxidation mask, to form said silicon oxide isolation region, wherein during the oxidizing step a thin surface oxide layer forms on the surface of said second silicon nitride layer; removing said thin surface oxide layer; simultaneously removing said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer; and removing said silicon oxide layer, to complete formation of said silicon oxide isolation region.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein said simultaneously removing said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer is by etching in phosphoric acid at a temperature of between about 160° and 180° C.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein said ion implanting is performed after formation of said silicon oxide isolation region.
Claim 5
Dependent Claim
32 words
The method of claim 1 wherein formation of said opening over said silicon oxide layer is by a reactive ion etch, in which said silicon oxide layer acts as an etch stop.
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein said thin surface oxide layer is removed by etching with hydrofluoric acid.
Claim 7
Dependent Claim
18 words
The method of claim 1 wherein removal of said silicon oxide layer is by etching with hydrofluoric acid.
Claim 8
Independent Claim
242 words
A method for fabricating semiconductor devices having silicon oxide isolation structures, comprising: providing a silicon substrate; forming a layer of silicon oxide on the surface of said silicon substrate; forming a first layer of silicon nitride having a thickness of between about 300 and 400 Angstroms on the surface of said silicon oxide layer, to prevent diffusion of oxygen into said silicon oxide layer and said silicon substrate during subsequent oxidation steps, thereby reducing said bird's beak length; forming a layer of polysilicon on the surface of said silicon nitride layer; forming a second layer of silicon nitride on the surface of said polysilicon layer; patterning said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer to form oxidation masks and to form openings over said silicon oxide layer; ion implanting said silicon substrate through said openings to form channel stop implants; oxidizing said silicon substrate in the area not masked by said oxidation masks, to form said silicon oxide isolation structures, during which a thin surface oxide layer forms on the surface of said second silicon nitride layer; removing said thin surface oxide layer; removing said second silicon nitride layer; oxidizing said polysilicon layer; removing said oxidized polysilicon layer; removing said first silicon nitride layer; removing said silicon oxide layer, to complete formation of said silicon oxide isolation structures; and forming said semiconductor devices on and in said silicon substrate, and between said silicon oxide isolation structures.
Claim 9
Independent Claim
242 words
A method for fabricating semiconductor devices having silicon oxide isolation structures, comprising: providing a silicon substrate; forming a layer of silicon oxide on the surface of said silicon substrate; forming a first layer of silicon nitride having a thickness of between about 300 and 400 Angstroms on the surface of said silicon oxide layer, to prevent diffusion of oxygen into said silicon oxide layer and said silicon substrate during subsequent oxidation steps, thereby reducing said bird's beak length; forming a layer of polysilicon on the surface of said silicon nitride layer; forming a second layer of silicon nitride on the surface of said polysilicon layer; patterning said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer to form oxidation masks and to form openings over said silicon oxide layer; ion implanting said silicon substrate through said openings to form channel stop implants; oxidizing said silicon substrate in the area not masked by said oxidation masks, to form said silicon oxide isolation structures, during which a thin surface oxide layer forms on the surface of said second silicon nitride layer; removing said thin surface oxide layer; removing said second silicon nitride layer; oxidizing said polysilicon layer; removing said oxidized polysilicon layer; removing said first silicon nitride layer; removing said silicon oxide layer, to complete formation of said silicon oxide isolation structures; and forming said semiconductor devices on and in said silicon substrate, and between said silicon oxide isolation structures.
Claim 10
Dependent Claim
11 words
The method of claim 7 wherein said polysilicon layer is undoped.
Claim 11
Dependent Claim
32 words
The method of claim 7 wherein formation of said openings over said silicon oxide layer is by a reactive ion etch, in which said silicon oxide layer acts as an etch stop.
Claim 12
Dependent Claim
18 words
The method of claim 7 wherein said thin surface oxide layer is removed by etching with hydrofluoric acid.
Claim 13
Dependent Claim
26 words
The method of claim 7 wherein said second silicon nitride layer is removed by phosphoric acid at a temperature of between about 160° and 180° C.
Claim 14
Dependent Claim
18 words
The method of claim 7 wherein removal of said oxidized polysilicon layer is by etching with hydrofluoric acid.
Claim 15
Dependent Claim
29 words
The method of claim 7 wherein removal of said first silicon nitride layer is by etching with phosphoric acid at a temperature of between about 160° and 180° C.
Claim 16
Independent Claim
259 words
A method of forming a silicon oxide isolation region with reduced bird's beak length, on the surface of a silicon substrate, comprising: forming a layer of silicon oxide on the surface of said silicon substrate; forming a first layer of silicon nitride having a thickness of between about 300 and 400 Angstroms on the surface of said silicon oxide layer, to prevent diffusion of oxygen into said silicon oxide layer and said silicon substrate during subsequent oxidation steps, thereby reducing said bird's beak length; forming a layer of undoped polysilicon on the surface of said first silicon nitride layer; forming a second layer of silicon nitride on the surface of said polysilicon layer; patterning said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer to form an oxidation mask and to form an opening over said silicon oxide layer; ion implanting said silicon substrate through said opening to form a channel stop implant; oxidizing said silicon substrate in the area not masked by said oxidation mask, to form said silicon oxide isolation region, wherein during the oxidizing step a thin surface oxide layer forms on the surface of said second silicon nitride layer; removing said thin surface oxide layer; removing said second silicon nitride layer; oxidizing said polysilicon layer; removing said oxidized polysilicon layer, whereby said first silicon nitride layer prevents oxide thinning at the field oxide--gate oxide interface during subsequent gate oxide formation; removing said first silicon nitride layer; and removing said silicon oxide layer, to complete formation of said silicon oxide isolation region.
Claim 17
Independent Claim
259 words
A method of forming a silicon oxide isolation region with reduced bird's beak length, on the surface of a silicon substrate, comprising: forming a layer of silicon oxide on the surface of said silicon substrate; forming a first layer of silicon nitride having a thickness of between about 300 and 400 Angstroms on the surface of said silicon oxide layer, to prevent diffusion of oxygen into said silicon oxide layer and said silicon substrate during subsequent oxidation steps, thereby reducing said bird's beak length; forming a layer of undoped polysilicon on the surface of said first silicon nitride layer; forming a second layer of silicon nitride on the surface of said polysilicon layer; patterning said second silicon nitride layer, said polysilicon layer, and said first silicon nitride layer to form an oxidation mask and to form an opening over said silicon oxide layer; ion implanting said silicon substrate through said opening to form a channel stop implant; oxidizing said silicon substrate in the area not masked by said oxidation mask, to form said silicon oxide isolation region, wherein during the oxidizing step a thin surface oxide layer forms on the surface of said second silicon nitride layer; removing said thin surface oxide layer; removing said second silicon nitride layer; oxidizing said polysilicon layer; removing said oxidized polysilicon layer, whereby said first silicon nitride layer prevents oxide thinning at the field oxide--gate oxide interface during subsequent gate oxide formation; removing said first silicon nitride layer; and removing said silicon oxide layer, to complete formation of said silicon oxide isolation region.
Claim 18
Dependent Claim
26 words
The method of claim 14 wherein said oxidized polysilicon layer is removed by a dip-back etch using hydrofluoric acid, for between about 1 and 3 minutes.
Claim 19
Dependent Claim
19 words
The method of claim 14 wherein said ion implanting is performed after formation of said silicon oxide isolation region.
Claim 20
Dependent Claim
32 words
The method of claim 14 wherein formation of said opening over said silicon oxide layer is by a reactive ion etch, in which said silicon oxide layer acts as an etch stop.
Claim 21
Dependent Claim
31 words
The method of claim 14 wherein said first and second silicon nitride layers are separately removed by etching with phosphoric acid at a temperature of between about 160° and 180° C.
Claim 22
Dependent Claim
18 words
The method of claim 14 wherein removal of said silicon oxide layer is by etching with hydrofluoric acid.
References Cited (Backward Citations)
JPS5739551A
Cited
JPS6181649A
Cited
JPS61244041A
Cited
JPS63137457A
Cited
US4829019A
Cited
JPH01187950A
Cited
US5002898A
Cited
US5215930A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-13 | 1998-09-12 | 1999-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-13 | 2002-09-12 | 2003-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-13 | 2006-09-12 | 2007-03-14 | $7700.00 | Window Closed / Lapsed |