Oxide superconductor and process for producing the same
Assignee: International Superconductivity Technology Center
•
Filing: 1992-04-01
•
Granted: 1995-03-07
•
Expires: 2012-04-01
Abstract
Abstract PCT No. PCT/JP92/00402 Sec. 371 Date Dec. 1, 1992 Sec. 102(e) Date Dec. 1, 1992 PCT Filed Apr. 1, 1992 PCT Pub. No. WO92/17407 PCT Pub. Date Oct. 15, 1992.An oxide superconductor comprising a crystal of LnBa2Cu3Oy (wherein Ln is at least one of rare earth elements including Y) and, finely dispersed therein, Ln2BaCuO5 and a composite oxide of PtBaCuO having an average particle diameter of 0.1 to 10 mu m is disclosed. The oxide superconductor is produced by melting a raw material powder comprising a composite oxide of Ln, Ba and Cu, rapidly solidifying the melt, pulverizing the resultant solid, mixing a Pt powder with the pulverized mixture, forming a resultant mixture, heating a resultant formed body to bring the formed body to a partially-molten state and cooling the partially-molten material.
Inventors
- 👤 Masato Murakami
- 👤 Tsutomu Takata
- 👤 Koji Yamaguchi
- 👤 Akihiro Kondoh
- 👤 Naoki Koshizuka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:22
CPC Classifications
C; C01; C01G; C01G55/00; C01G55/002; C01G3/00; C01G3/006; C04; C04B; C04B35/00; C04B35/01; C04B35/45; C04B35/4504; C04B35/4508; C01P; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/40; C01P2006/42; C01P2006/80; Y; Y10; Y10S; Y10S505/00; Y10S505/775; Y10S505/776; Y10S505/779; Y10S505/78; Y10S505/781; Y10S505/785
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
78 words
An oxide superconductor comprising a crystal of LnBa 2 Cu 3 O y wherein Ln is at least one element selected from the group consisting of Y, Sm, Eu, Gd, Dy, Ho, Er and Yb as an oxide superconducting phase and, finely dispersed therein, Ln 2 BaCuO 5 as a 211 phase and PtBa 4 Cu 2 O y as a composite oxide of Pt, Ba and Cu having an average particle diameter of 0.1 to 10 μm.
Claim 2
Dependent Claim
78 words
An oxide superconductor comprising a crystal of LnBa 2 Cu 3 O y wherein Ln is at least one element selected from the group consisting of Y, Sm, Eu, Gd, Dy, Ho, Er and Yb as an oxide superconducting phase and, finely dispersed therein, Ln 2 BaCuO 5 as a 211 phase and PtBa 4 Cu 2 O y as a composite oxide of Pt, Ba and Cu having an average particle diameter of 0.1 to 10 μm.
Claim 3
Dependent Claim
174 words
A process for producing an oxide superconductor, which comprises mixing at least an oxide of one element selected from the group consisting of Y, Sm, Eu, Gd, Dy, Ho, Er and Yb, hereinafter referred to as "Ln", with a powder of BaCO 3 and CuO to prepare a mixed powder, heating the mixed powder, and melting the mixed powder to form a molten material, rapidly cooling and solidifying the molten material to form a solidified material, pulverizing the solidified material to form a fine powder, mixing 0.2 to 2.0% by weight of a platinum powder with the pulverized fine powder, forming a body with the resultant mixture, heating the formed body to bring it to a partially-molten state and then cooling the partially-molten formed body to finely disperse Ln 2 BaCuO 5 as a 211 phase and a platinum compound of the formula PtBa 4 Cu 2 O y in a crystal of an oxide superconductor comprising LnBa 2 Cu 3 O y , where y is a number sufficient to permit oxide superconductivity.
Claim 4
Dependent Claim
174 words
A process for producing an oxide superconductor, which comprises mixing at least an oxide of one element selected from the group consisting of Y, Sm, Eu, Gd, Dy, Ho, Er and Yb, hereinafter referred to as "Ln", with a powder of BaCO 3 and CuO to prepare a mixed powder, heating the mixed powder, and melting the mixed powder to form a molten material, rapidly cooling and solidifying the molten material to form a solidified material, pulverizing the solidified material to form a fine powder, mixing 0.2 to 2.0% by weight of a platinum powder with the pulverized fine powder, forming a body with the resultant mixture, heating the formed body to bring it to a partially-molten state and then cooling the partially-molten formed body to finely disperse Ln 2 BaCuO 5 as a 211 phase and a platinum compound of the formula PtBa 4 Cu 2 O y in a crystal of an oxide superconductor comprising LnBa 2 Cu 3 O y , where y is a number sufficient to permit oxide superconductivity.
Claim 5
Dependent Claim
29 words
The process according to claim 2, wherein the platinum compound is a composite oxide of Pt, Ba and Cu having an average particle diameter of 0.1 to 10 μm.
Claim 6
Dependent Claim
24 words
The process according to claim 2, wherein the average particle diameter of the pulverized fine powder after rapid solidification is 0.1 to 10 μm.
Claim 7
Dependent Claim
28 words
The process according to claim 2, wherein, after the formed body is brought to a partially-molten state, it is cooled at a rate of 0.5 to 10° C./hr.
Claim 8
Dependent Claim
182 words
A process for producing an oxide superconductor, characterized by heating a mixed powder comprised of a composite oxide of Y, Ba and Cu to a temperature in the range of from 1300° to 1450° C. to form a mixed phase comprising Y 2 O 3 and a liquid phase, rapidly cooling the mixed phase to form a solidified material, pulverizing the solidified material to provide a powder having an average particle diameter of 0.1 to 10 μm, adding and mixing said powder with a platinum powder in an amount of 0.2 to 2.0% by weight, forming the mixture into a formed body, heating the formed body to a temperature in the range of from 1050° to 1200° C. to bring the formed body to a partially-molten state, thereby forming a mixed phase comprising a 211 phase and a liquid phase, and cooling said formed body at a rate of 0.5 to 10° C./hr to disperse the 211 phase and a platinum compound of the formula PtBa 4 Cu 2 O 4 in a crystal of LnBa 2 Cu 3 O y .
Claim 9
Dependent Claim
182 words
A process for producing an oxide superconductor, characterized by heating a mixed powder comprised of a composite oxide of Y, Ba and Cu to a temperature in the range of from 1300° to 1450° C. to form a mixed phase comprising Y 2 O 3 and a liquid phase, rapidly cooling the mixed phase to form a solidified material, pulverizing the solidified material to provide a powder having an average particle diameter of 0.1 to 10 μm, adding and mixing said powder with a platinum powder in an amount of 0.2 to 2.0% by weight, forming the mixture into a formed body, heating the formed body to a temperature in the range of from 1050° to 1200° C. to bring the formed body to a partially-molten state, thereby forming a mixed phase comprising a 211 phase and a liquid phase, and cooling said formed body at a rate of 0.5 to 10° C./hr to disperse the 211 phase and a platinum compound of the formula PtBa 4 Cu 2 O 4 in a crystal of LnBa 2 Cu 3 O y .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-06 | 1998-09-05 | 1999-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-06 | 2002-09-05 | 2003-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-06 | 2006-09-05 | 2007-03-07 | $7700.00 | Window Closed / Lapsed |