Semiconductor gamma ray detector including compositionally graded, leakage current blocking potential barrier layers and method of fabricating the detector
Assignee: Raytheon Co
•
Filing: 1993-06-11
•
Granted: 1995-02-21
•
Expires: 2013-06-11
Abstract
Abstract A P-type/intrinsic/N-type (P-I-N) gamma ray detector (10) includes a semiconductor detector layer (12) of intrinsic cadmium telluride (CdTe) or cadmium zinc telluride (CdZnTe). P- and N-doped semiconductor layers (14,16) of mercury cadmium telluride (HgCdTe) are formed on the opposite surfaces (12a,12b) of the detector layer (12), and ohmic metal contacts (18,20) are formed on the doped layers (14,16). The composition of the doped layers (14,16) is Hg 1-x Cd x Te, and is graded such that x progressively decreases with distance from the detector layer (12) toward the ohmic contacts (18,20). This causes the bandgap of the doped layers (14,16) to also decrease from the detector layer (12) toward the ohmic contacts (18,20), forming potential barriers (E1,E2) which block leakage currents constituted by injection of minority carriers from the ohmic contacts (18,20) into the detector layer (12) and provide low resistance between the doped layers (14,16) and ohmic contacts (18,20). The detector layer (12) and doped layers (14,16) are annealed during fabrication, causing diffusion of mercury from the doped layers (14,16) into the detector layer (12) and diffusion of cadmium from the detector layer (12) into the doped layers (14,16), thereby increasing the heights of the potential barriers (E1,E2).
Inventors
- 👤 David R. Rhiger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 09:49
CPC Classifications
H; H10; H10F; H10F30/00; H10F30/20; H10F30/29
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
105 words
A ray detector, comprising: a wide bandgap substantially intrinsic semiconductor detector layer; a P-doped semiconductor layer which is formed on a first surface of the detector layer and has a composition which is graded such that the bandgap of the P-doped layer decreases with distance from said first surface; a first ohmic contact formed on the P-doped layer; an N-doped semiconductor layer which is formed on a second surface of the detector layer and has a composition which is graded such that the bandgap of the N-doped layer decreases with distance from said second surface; and a second ohmic contact formed on the N-doped layer.
Claim 2
Dependent Claim
105 words
A ray detector, comprising: a wide bandgap substantially intrinsic semiconductor detector layer; a P-doped semiconductor layer which is formed on a first surface of the detector layer and has a composition which is graded such that the bandgap of the P-doped layer decreases with distance from said first surface; a first ohmic contact formed on the P-doped layer; an N-doped semiconductor layer which is formed on a second surface of the detector layer and has a composition which is graded such that the bandgap of the N-doped layer decreases with distance from said second surface; and a second ohmic contact formed on the N-doped layer.
Claim 3
Dependent Claim
46 words
A detector as in claim 1, in which: the detector layer is formed of a material selected from the group consisting of cadmium telluride (CdTe) and cadmium zinc telluride (CdZnTe); and the P-doped layer and the N-doped layer are each formed of mercury cadmium telluride (HgCdTe).
Claim 4
Dependent Claim
51 words
A detector as in claim 2, in which: the concentration of cadmium (Cd) in the detector layer is higher than in the P-doped layer and in the N-doped layer; and the concentration of mercury (Hg) in the P-doped layer and in the N-doped layer is higher than in the detector layer.
Claim 5
Dependent Claim
55 words
A detector as in claim 3, in which: cadmium from the detector layer is diffused into the P-doped layer and into the N-doped layer across said first and second surfaces respectively; and mercury from the P-doped layer and from the N-doped layer is diffused into the detector layer across said first and second surfaces respectively.
Claim 6
Dependent Claim
81 words
A detector as in claim 2, in which: said composition of the P-doped layer is Hg 1-x Cd x Te and varies from approximately 0.6≦×≦1.0 at said first suffice to approximately 0≦×≦0.4 at the interface of the P-doped layer and the first ohmic contact; and said composition of the N-doped layer is Hg 1-x Cd x Te and varies from approximately 0.6≦×≦1.0 at said first surface to approximately 0≦×≦0.4 at the interface of the N-doped layer and the second ohmic contact.
Claim 7
Dependent Claim
29 words
A detector as in claim 5, in which the doping concentration in the P-doped layer and in the N-doped layer is approximately 10 16 -10 18 ions/cm 3 .
Claim 8
Dependent Claim
21 words
A detector as in claim 6, in which the P-doped layer and the N-doped layer are each approximately 2-50 micrometers thick.
Claim 9
Dependent Claim
81 words
A detector as in claim 2, in which: said composition of the P-doped layer is Hg 1-x Cd x Te and varies from approximately x=0.8 at said first surface to approximately x=0.2 at the interface of the P-doped layer and the first ohmic contact; and said composition of the N-doped layer is Hg 1-x Cd x Te and varies from approximately x=0.8 at said second surface to approximately x=0.2 at the interface of the N-doped layer and the second ohmic contact.
Claim 10
Dependent Claim
26 words
A detector as in claim 8, in which the doping concentration in the P-doped layer and in the N-doped is approximately 10 18 ions/cm 3 .
Claim 11
Dependent Claim
21 words
A detector as in claim 9, in which the P-doped layer and the N-doped layer are each approximately 20 micrometers thick.
Claim 12
Dependent Claim
16 words
A detector as in claim 10, in which the detector layer is approximately 1,000 micrometers thick.
Claim 13
Dependent Claim
52 words
A detector as in claim 1, in which: the detector layer is formed of a compound material selected from groups II and VI of the periodic table; and the P-doped layer and the N-doped layer are formed of a ternary compound material selected from groups II and VI of the periodic table.
Claim 14
Dependent Claim
52 words
A detector as in claim 1, in which: the detector layer is formed of a compound material selected from groups III and V of the periodic table; and the P-doped layer and the N-doped layer are formed of a ternary compound material selected from groups III and V of the periodic table.
Claim 15
Independent Claim
112 words
A method of fabricating a ray detector, comprising the steps of: (a) providing a wide bandgap substantially intrinsic semiconductor detector layer; (b) forming a P-doped semiconductor layer on a first surface of the detector layer having a composition which is goaded such that the bandgap of the P-doped layer decreases with distance from said first surface; (c) forming a first ohmic contact on the P-doped layer; (d) forming an N-doped semiconductor layer on a second surface of the detector layer having a composition which is graded such that the bandgap of the N-doped layer decreases with distance from said second surface; and (e) forming a second ohmic contact on the N-doped layer.
Claim 16
Independent Claim
112 words
A method of fabricating a ray detector, comprising the steps of: (a) providing a wide bandgap substantially intrinsic semiconductor detector layer; (b) forming a P-doped semiconductor layer on a first surface of the detector layer having a composition which is goaded such that the bandgap of the P-doped layer decreases with distance from said first surface; (c) forming a first ohmic contact on the P-doped layer; (d) forming an N-doped semiconductor layer on a second surface of the detector layer having a composition which is graded such that the bandgap of the N-doped layer decreases with distance from said second surface; and (e) forming a second ohmic contact on the N-doped layer.
Claim 17
Dependent Claim
56 words
A method as in claim 14, in which: step (a) comprises providing the detector layer of a material selected from the group consisting of cadmium telluride (CdTe) and cadmium zinc telluride (CdZnTe); step (b) comprises forming the P-doped layer of mercury cadmium telluride (HgCdTe); and step (d) comprises forming the N-doped layer of mercury cadmium telluride.
Claim 18
Dependent Claim
101 words
A method as in claim 15, in which steps (b) and (d) in combination comprise annealing the detector layer, P-doped layer and N-doped layer at a first temperature and a time duration sufficient to diffuse cadmium from the detector layer into the P-doped layer and into the N-doped layer across said first and second surfaces respectively, and to diffuse mercury from the P-doped layer and from the N-doped layer into the detector layer across said first and second surfaces respectively but less than a second temperature sufficient to cause significant movement of dopant ions in said P-doped and N-doped semiconductor layers.
Claim 19
Dependent Claim
39 words
A method as in claim 16, in which steps (b) and (d) in combination comprise annealing the detector layer, P-doped layer and N-doped layer in a mercury vapor at a temperature of approximately 400°-450° C. for approximately 0.5-4 hours.
Claim 20
Dependent Claim
39 words
A method as in claim 16, in which steps (b) and (d) in combination comprise annealing the detector layer, P-doped layer and N-doped layer in a mercury vapor at a temperature of approximately 400°-450° C. for approximately one hour.
Claim 21
Dependent Claim
39 words
A method as in claim 15, in which: step (b) comprises liquid phase epitaxy (LPE) using a mercury melt including a P-type dopant; and step (d) comprises liquid phase epitaxy (LPE) using a mercury melt including an N-type dopant.
Claim 22
Dependent Claim
66 words
A method as in claim 14 further including the step of: (f) annealing said detector layer, said P-doped layer and said N-doped layer at a first temperature and a time duration sufficient to diffuse semiconductor atoms in both directions across said first and second surfaces but less than a second temperature sufficient to cause significant movement of dopant ions in said P-doped and N-doped semiconductor layers.
Claim 23
Dependent Claim
74 words
A method as in claim 14, in which: step (a) comprises providing the detector layer of a compound material selected from groups II and VI of the periodic table; step (b) comprises forming the P-doped layer of a compound ternary material selected from groups II and VI of the periodic table; and step (d) comprises forming the N-doped layer of a compound ternary material selected from groups II and VI of the periodic table.
Claim 24
Dependent Claim
74 words
A method as in claim 14, in which: step (a) comprises providing the detector layer of a compound material selected from groups III and V of the periodic table; step (b) comprises forming the P-doped layer of a compound ternary material selected from groups III and V of the periodic table; and step (d) comprises forming the N-doped layer of a compound ternary material selected from groups III and V of the periodic table.
References Cited (Backward Citations)
US4801984A
Cited
US5162891A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-20 | 1998-08-22 | 1999-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-20 | 2002-08-22 | 2003-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-20 | 2006-08-22 | 2007-02-21 | $7700.00 | Window Closed / Lapsed |