Hole-trap-compensated scintillator material and computed tomography machine containing the same
Assignee: General Electric Co
•
Filing: 1994-05-27
•
Granted: 1995-02-21
•
Expires: 2014-05-27
Abstract
Abstract Afterglow in a luminescent material in which a significant factor in afterglow is the release of holes from hole traps in the scintillator material is substantially reduced by adding cerium as a hole-trapping species to the scintillator composition which successfully competes with the hole traps in the basic scintillator composition. In gadolinium gallium garnet activated with chromium, the addition of cerium in the range of 0.2 to 0.255 weight percent reduces afterglow in this manner while exhibiting excellent stability to x-ray damage after exposure to an initial pair of x-ray pulses.
Inventors
- 👤 Veneta G. Tsoukala
- 👤 Charles D. Greskovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:53
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7776; C09K11/7701; C09K11/7715; C09K11/7716; G; G01; G01T; G01T1/00; G01T1/16; G01T1/20; G01T1/202; G01T1/2023; G01T1/29; G01T1/2914; G01T1/2985
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
153 words
A crystalline scintillator composition consisting of: gadolinium gallium garnet having the formula Gd 3 Ga 5 O 12 ; chromium in a concentration in said garnet equivalent to chromium oxide being between 0.05 and 1.0 weight percent of the overall scintillator composition which is effective to render said scintillator composition luminescent in response to high-energy stimulating radiation consisting of x-rays; and a hole trapping species, cerium, in a concentration in said garnet of about 0.2 to about 0.255 weight percent of the overall scintillator composition which is effective to reduce the afterglow level relative to the afterglow level of said scintillator composition in the absence of said hole trapping species while allowing the scintillator to withstand said radiation with essentially no damage after receiving an initial dose of said radiation; said chromium being substituted in said formula for said Ga and said hole trapping species being substituted in said formula for said Gd.
Claim 2
Dependent Claim
153 words
A crystalline scintillator composition consisting of: gadolinium gallium garnet having the formula Gd 3 Ga 5 O 12 ; chromium in a concentration in said garnet equivalent to chromium oxide being between 0.05 and 1.0 weight percent of the overall scintillator composition which is effective to render said scintillator composition luminescent in response to high-energy stimulating radiation consisting of x-rays; and a hole trapping species, cerium, in a concentration in said garnet of about 0.2 to about 0.255 weight percent of the overall scintillator composition which is effective to reduce the afterglow level relative to the afterglow level of said scintillator composition in the absence of said hole trapping species while allowing the scintillator to withstand said radiation with essentially no damage after receiving an initial dose of said radiation; said chromium being substituted in said formula for said Ga and said hole trapping species being substituted in said formula for said Gd.
Claim 3
Dependent Claim
14 words
The scintillator composition recited in claim 1 wherein said crystalline scintillator composition is polycrystalline.
Claim 4
Dependent Claim
13 words
The crystalline scintillator composition of claim 2 wherein said scintillator composition is transparent.
Claim 5
Dependent Claim
28 words
The scintillator composition recited in claim 1 wherein said concentration of cerium is between about 0.214 weight percent and about 0.255 weight percent of the overall scintillator composition.
Claim 6
Dependent Claim
32 words
The scintillator composition recited in claim 1 wherein said concentration of cerium is about 0.255 weight percent of the overall scintillator composition and said initial dose of radiation totals about 480 RADs.
Claim 7
Dependent Claim
151 words
In a computed tomography machine of the type having a solid state scintillator, the improvement comprising: the scintillator being gadolinium gallium garnet having the formula Gd 3 Ga 5 O 12 , chromium in a concentration in said garnet equivalent to chromium oxide being between 0.05 and 1.0 weight percent of the scintillator which is effective to render said scintillator luminescent in response to high energy stimulating radiation consisting of x-rays produced by said machine, and cerium in a concentration in said garnet of between 0.2 and 0.255 weight percent of the scintillator which is effective to reduce the afterglow level relative to the afterglow level in the absence of cerium and to enable said scintillator to exhibit essentially zero x-ray damage after receiving an initial dose of said x-rays, said chromium being substituted in said formula for said Ga and said cerium being substituted in said formula for said Gd.
Claim 8
Dependent Claim
151 words
In a computed tomography machine of the type having a solid state scintillator, the improvement comprising: the scintillator being gadolinium gallium garnet having the formula Gd 3 Ga 5 O 12 , chromium in a concentration in said garnet equivalent to chromium oxide being between 0.05 and 1.0 weight percent of the scintillator which is effective to render said scintillator luminescent in response to high energy stimulating radiation consisting of x-rays produced by said machine, and cerium in a concentration in said garnet of between 0.2 and 0.255 weight percent of the scintillator which is effective to reduce the afterglow level relative to the afterglow level in the absence of cerium and to enable said scintillator to exhibit essentially zero x-ray damage after receiving an initial dose of said x-rays, said chromium being substituted in said formula for said Ga and said cerium being substituted in said formula for said Gd.
Claim 9
Dependent Claim
19 words
The computed tomography machine recited in claim 6 wherein said weight percent of chromium is between 0.1 and 0.6.
Claim 10
Dependent Claim
13 words
The computed tomography machine recited in claim 6 wherein said scintillator is polycrystalline.
Claim 11
Dependent Claim
13 words
The computed tomography machine recited in claim 8 wherein said scintillator is transparent.
References Cited (Backward Citations)
US3591517A
Cited
DE2719611A1
Cited
JPS62501169A
Cited
DE3530180A1
Cited
DE3704813A1
Cited
JPS63309583A
Cited
US4824598A
Cited
US5057692A
Cited
EP0467044A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-20 | 1998-08-22 | 1999-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-20 | 2002-08-22 | 2003-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-20 | 2006-08-22 | 2007-02-21 | $7700.00 | Window Closed / Lapsed |