Thin film semiconductor device and method of production
Assignee: Seiko Epson Corp
•
Filing: 1993-12-27
•
Granted: 1995-02-14
•
Expires: 2013-12-27
Abstract
Abstract A thin film semiconductor device having a silicon thin film semiconductor layer deposited on an ordinary glass substrate at low temperatures of not over 600 DEG C. The silicon film has at least about a 40% degree of crystallinity and mainly {111} preferred orientation. The thin film can be formed by a low pressure chemical vapor deposition process using monosilane (SiH4) as a source gas at a total reactor pressure of about 15 mTorr or less or at a silane partial pressure of about 10 mTorr or less at a vapor phase deposition temperature of not more than about 600 DEG C.
Inventors
- 👤 Mitsutoshi Miyasaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:11
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/031; H10D30/0312; H10D30/0314; H10D30/0321; H10D30/60; H10D30/67; H10D30/6729; H10D30/673; H10D30/6731; H10D30/674; H10D30/6741; H10D30/6743; H10D30/6745; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/2921; H10P14/32; H10P14/3202; H10P14/3238; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3438; H10P14/3441; H10P14/3442; H10P14/3444; Y; Y10; Y10S; Y10S148/00; Y10S148/15
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
112 words
A method of forming a MOSFET thin film transistor including a thin film layer of silicon to serve as an active layer of a transistor, comprising the steps of: providing a substrate; placing the substrate into a reactor; depositing a thin film silicon layer having a thickness of less than about 1400 Å on the substrate in the reactor by chemical vapor deposition by flowing gas through the reactor at a speed of at least about 1.7 SCCM/mTorr and using monosilane (SiH 4 ) as a source gas at one of a total reactor pressure of about 15 mTorr or less and a silane partial pressure of about 10 mTorr or less.
Claim 2
Independent Claim
112 words
A method of forming a MOSFET thin film transistor including a thin film layer of silicon to serve as an active layer of a transistor, comprising the steps of: providing a substrate; placing the substrate into a reactor; depositing a thin film silicon layer having a thickness of less than about 1400 Å on the substrate in the reactor by chemical vapor deposition by flowing gas through the reactor at a speed of at least about 1.7 SCCM/mTorr and using monosilane (SiH 4 ) as a source gas at one of a total reactor pressure of about 15 mTorr or less and a silane partial pressure of about 10 mTorr or less.
Claim 3
Dependent Claim
23 words
The method of claim 1, wherein the temperature in the reactor, during silicon deposition, is about 600° C. or less during silicon deposition.
Claim 4
Dependent Claim
16 words
The method of claim 1, wherein the total reactor pressure is about 15 mTorr or less.
Claim 5
Dependent Claim
16 words
The method of claim 1, wherein the silane partial pressure is about 10 mTorr or less.
Claim 6
Dependent Claim
69 words
The method of claim 1, wherein the reaction conditions are controlled so that the silicon thin film formed has a refractive index of 4.06 or less for light having a wavelength of 589.3 nm in air, a refractive index of 4.46 or more for light having a wavelength of 308 nm in air and an extinction index of 0.81 or less for light having a wavelength of 404.7 nm.
Claim 7
Dependent Claim
33 words
The method of claim 1, wherein the reaction conditions are controlled so that the resulting silicon thin film has a degree of crystallinity of about 40% or more, when measured by Raman spectroscopy.
Claim 8
Dependent Claim
21 words
The method of claim 1, wherein the reactor conditions are controlled so that the silicon film has mainly {111} preferred orientation.
Claim 9
Dependent Claim
23 words
The method of claim 1, including depositing an underlayer of insulating material on the substrate and depositing the silicon layer on the underlayer.
Claim 10
Dependent Claim
20 words
The method of claim 1, wherein the monosilane gas in the reactor is pumped at about 1.7 SCCM/mTorr or more.
Claim 11
Dependent Claim
20 words
The method of claim 1, wherein the monosilane gas in the reactor is pumped at more than about 1.78 SCCM/mTorr.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-13 | 1998-08-15 | 1999-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-13 | 2002-08-15 | 2003-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-13 | 2006-08-15 | 2007-02-14 | $7700.00 | Window Closed / Lapsed |