US5387378A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Integral asymmetric fluoropolymer pervaporation membranes and method of making the same
Assignee: Tulane University
•
Filing: 1993-04-21
•
Granted: 1995-02-07
•
Expires: 2013-04-21
Abstract
Abstract The present invention provides a method for fabricating an asymmetric fluoropolymer membrane comprised of a fluoropolymer material, the membrane having a first surface comprised of a dense layer of the fluoropolymer material, and an opposite second surface comprised of a porous layer of the fluoropolymer material, comprising the steps of: (a) dissolving a fluoropolymer material in a solvent to form a solution; (b) depositing the solution on a casting surface; and (c) removing the solvent from the solution, thereby precipitating the membrane therefrom. The present invention also provides asymmetric fluoropolymer membranes comprised of a fluoropolymer material, wherein the membrane has a first surface comprised of a dense layer of the fluoropolymer material, and an opposite second surface comprised of a porous layer of the fluoropolymer material, and provides compositions for making the same. The present invention further provides a method for separating one or more organic compounds from a mixture of organic compounds or one or more organic compounds from water by pervaporation or vapor permeation, comprising the steps of: (a) placing an asymmetric fluoropolymer membrane comprised of a fluoropolymer material into a suitable pervaporation or vapor permeation apparatus such that the membrane forms a selectively permeable barrier to one or more compounds of the mixture, the membrane having a first surface comprised of a dense layer of the fluoropolymer material, and an opposite second surface comprised of a porous layer of the fluoropolymer material; (b) contacting the first surface of the membrane with the mixture; and (c) transporting permeate through the membrane by creating a difference in the partial pressure of the compounds between the first and second surfaces of the membrane.
Inventors
- 👤 Peter N. Pintauro
- 👤 Kangzhuang Jian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 15:07
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/30; B01D71/32; B01D71/34; B01D61/00; B01D61/36; B01D61/362; B01D67/00; B01D67/0002; B01D67/0009; B01D67/00091; B01D69/00; B01D69/02; B01D2323/00; B01D2323/08; B01D2323/081; B01D2323/12; B01D2325/00; B01D2325/04
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
115 words
A method for fabricating an asymmetric fluoropolymer membrane comprised of a fluoropolymer material, the membrane having a first surface comprised of a dense layer of the fluoropolymer material, and an opposite second surface comprised of a porous layer of the fluoropolymer material, comprising the steps of: (a) dissolving a fluoropolymer material in a solvent mixture comprised of a low boiling point solvent and a high boiling point solvent to form a solution; (b) depositing the solution on a casting surface; and (c) removing the solvent mixture from the solution, thereby precipitating the asymmetric fluoropolymer membrane therefrom such that the first surface of the membrane precipitates at the interface of the casting surface and the solution.
Claim 2
Independent Claim
115 words
A method for fabricating an asymmetric fluoropolymer membrane comprised of a fluoropolymer material, the membrane having a first surface comprised of a dense layer of the fluoropolymer material, and an opposite second surface comprised of a porous layer of the fluoropolymer material, comprising the steps of: (a) dissolving a fluoropolymer material in a solvent mixture comprised of a low boiling point solvent and a high boiling point solvent to form a solution; (b) depositing the solution on a casting surface; and (c) removing the solvent mixture from the solution, thereby precipitating the asymmetric fluoropolymer membrane therefrom such that the first surface of the membrane precipitates at the interface of the casting surface and the solution.
Claim 3
Dependent Claim
35 words
The method of claim 1, further comprising the step of heating the solution at a temperature of between about 45°-60° C. for between about 30-60 minutes prior to depositing the solution on the casting surface.
Claim 4
Dependent Claim
21 words
The method of claim 1, wherein the removing step comprises evaporating the solvent from the solution by air drying the solution.
Claim 5
Dependent Claim
50 words
The method of claim 1, wherein the removing step further comprises the steps of: (a) evaporating the solvent by air drying the solution for a sufficient period of time until the surface of the solution at the air interface has gelled; and (b) immersing the solution in a precipitation bath.
Claim 6
Dependent Claim
24 words
The method of claim 1, wherein the fluoropolymer material is selected from the group consisting of a fluoropolymer, a fluorinated copolymer, and mixtures thereof.
Claim 7
Dependent Claim
22 words
The method of claim 5, wherein the fluoropolymer material is selected from the group consisting of polyvinylidene fluoride, polytetrafluoroethylene, polyhexafluoropropylene, and polyvinylchlorotrifluoroethylene.
Claim 8
Dependent Claim
28 words
The method of claim 1, wherein the low boiling point solvent boils at between about 40°-60° C. and the high boiling solvent boils at between about 140°-200° C.
Claim 9
Dependent Claim
17 words
The method of claim 1, wherein the high boiling point solvent has a strong affinity for water.
Claim 10
Dependent Claim
32 words
The method of claim 1, wherein the low boiling point solvent is acetone and the high boiling point solvent is selected from the group consisting of dimethylacetamide, dimethylformamide, dimethylsulfoxide and mixtures thereof.
Claim 11
Dependent Claim
41 words
The method of claim 1, wherein the mixture of solvents comprises between about 75-90 vol % acetone and between about 10-25 vol % of a high boiling point solvent selected from the group consisting of dimethylacetamide, dimethylformamide, dimethylsulfoxide and mixtures thereof.
Claim 12
Dependent Claim
15 words
The method of claim 1, wherein the casting surface comprises a suitable inert support surface.
Claim 13
Dependent Claim
23 words
The method of claim 11, wherein the casting surface is selected from the group consisting of glass, metal, plastic, paper, and non-woven fabric.
Claim 14
Dependent Claim
46 words
The method of claim 1, wherein the solution comprises between about 10-16 wt % polyvinylidene fluoride, between about 65-75 wt % acetone and between about 10-25 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 15
Dependent Claim
43 words
The method of claim 3, wherein the solution comprises about 12 wt % polyvinylidene fluoride, about 73 wt % acetone, and about 15 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 16
Dependent Claim
43 words
The method of claim 4, wherein the solution comprises about 14 wt % polyvinylidene fluoride, about 73 wt % acetone and about 13 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 17
Dependent Claim
47 words
The method of claim 1, wherein the solution comprises between about 10-16 wt % polyvinylidene fluoride/polytetrafluoroethylene copolymer, between about 60-80 wt % acetone and between about 10-25 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 18
Dependent Claim
44 words
The method of claim 1, wherein the solution comprises about 12 wt % polyvinylidene fluoride/polyhexafluoropropylene copolymer, about 76 wt % acetone and about 12 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 19
Dependent Claim
44 words
The method of claim 1, wherein the solution comprises about 12 wt % polyvinylidene fluoride/polyhexafluoropropylene copolymer about 64 wt % acetone, and about 24 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 20
Dependent Claim
54 words
The method of claim 1, wherein the solution comprises between about 8-12 wt % polyvinylidene fluoride, between about 2-6 wt % polyvinylidene fluoride/polyvinylchlorotrifluoroethylene copolymer between about 65-75 wt % acetone, and between about 10-25 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 21
Dependent Claim
50 words
The method of claim 19, wherein the solution comprises about 9.8 wt % polyvinylidene fluoride, about 4.2 wt % polyvinylidene fluoride/polyvinylchlorotrifluoroethylene copolymer about 73 wt % acetone, and about 13 wt % of a high boiling point solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof.
Claim 22
Dependent Claim
37 words
The method of claim 1, and further comprising prior to the removing step the step of controlling air temperature and humidity wherein the air temperature is between about 20°-45° C. and the humidity is between about 45-85%.
Claim 23
Dependent Claim
16 words
The method of claim 3, wherein the solution is air dried for between about 0.5-3.0 hours.
Claim 24
Dependent Claim
16 words
The method of claim 4, wherein the solution is air dried for between about 1-30 minutes.
Claim 25
Dependent Claim
26 words
The method of claim 4, wherein the precipitation bath comprises a liquid selected from the group consisting of water, acetone, dimethylacetamide, dimethylformamide, dimethylsulfoxide, and mixtures thereof.
Claim 26
Dependent Claim
87 words
The method of claim 4, wherein the precipitation bath, comprises three baths: a first precipitation bath comprising about 50-60 vol % water, about 35-45 vol % acetone, and about 5-15 vol % of a solvent selected from the group consisting of dimethylformamide, dimethylacetamide, dimethylsulfoxide and mixtures thereof; a second precipitation bath comprising about 55-75 vol % water and about 25-45 vol % acetone; and a third precipitation bath comprising water and wherein the immersing step comprises placing the solution successively in the first, second and third baths.
Claim 27
Dependent Claim
52 words
The method of claim 4, wherein the precipitation bath comprises two baths: a first precipitation bath comprising about 25 vol % acetone and about 75 vol % water and a second precipitation bath consisting of water and wherein the immersing step comprises placing the solution successively in the first and second baths.
Claim 28
Dependent Claim
17 words
The method of claim 4, wherein the temperature of the precipitation baths is between about 0°-25° C.
Claim 29
Dependent Claim
17 words
The method of claim 4, wherein the temperature of the precipitation baths is preferably about 15° C.
References Cited (Backward Citations)
US3133132A
Cited
US3483282A
Cited
US3615024A
Cited
US4203847A
Cited
JPS54135674A
Cited
US4232087A
Cited
US4376140A
Cited
US4307135A
Cited
US4414280A
Cited
US4557955A
Cited
JPS5891733A
Cited
US4613544A
Cited
EP0245863A2
Cited
US4784880A
Cited
US5171611A
Cited
US5190654A
Cited
US5238471A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-06 | 1998-08-08 | 1999-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-06 | 2002-08-08 | 2003-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-06 | 2006-08-08 | 2007-02-07 | $7700.00 | Window Closed / Lapsed |