Foam metallic glass
Assignee: Yale University
•
Filing: 1993-02-05
•
Granted: 1995-01-24
•
Expires: 2013-02-05
Abstract
Abstract A method of making a solid foam material including the steps of heating in a chamber a starting material that is normally solid at room temperature to a temperature that is above its melting point, injecting a blowing liquid into the melted material to produce a mixture; and rapidly decompressing the mixture to produce the solid foam material.
Inventors
- 👤 Robert E. Apfel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:58
CPC Classifications
C; C22; C22C; C22C45/00; C22C45/003; C22C1/00; C22C1/08; C22C1/11; C22C1/083; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12479
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
72 words
A method of making a solid foam material comprising: in a chamber heating a starting material that is normally solid at room temperature to a temperature that is above its melting point; injecting a blowing liquid into the melted material to produce a mixture; and rapidly decompressing the mixture to vaporize the blowing liquid so that its latent heat of vaporization cools the starting material sufficiently to produce the solid foam material.
Claim 2
Independent Claim
72 words
A method of making a solid foam material comprising: in a chamber heating a starting material that is normally solid at room temperature to a temperature that is above its melting point; injecting a blowing liquid into the melted material to produce a mixture; and rapidly decompressing the mixture to vaporize the blowing liquid so that its latent heat of vaporization cools the starting material sufficiently to produce the solid foam material.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein the starting material is an organic material.
Claim 4
Dependent Claim
13 words
The method of claim 1 wherein the starting material is a metallic material.
Claim 5
Dependent Claim
13 words
The method of claim 3 wherein the starting material is an organo-metallic material.
Claim 6
Dependent Claim
14 words
The method of claim 3 wherein the starting material is a metallic alloy material.
Claim 7
Dependent Claim
22 words
The method of claim 1 further comprising increasing the pressure of a gas in said chamber prior to injecting the blowing liquid.
Claim 8
Dependent Claim
37 words
The method of claim 6 wherein the pressure increasing step increases the pressure to a level that is high enough to prevent boiling of the blowing liquid when said blowing liquid is injected into the melted material.
Claim 9
Dependent Claim
20 words
The method of claim 1 further comprising introducing an inert gas into said chamber prior to heating the starting material.
Claim 10
Dependent Claim
24 words
The method of claim 1 wherein said decompression step involves dropping the pressure surrounding the melted mixture to no greater than about one atmosphere.
Claim 11
Dependent Claim
18 words
The method of claim 1 wherein said decompression step involves creating a partial vacuum around the melted mixture.
Claim 12
Dependent Claim
18 words
The method of claim 1 further comprising introducing a filler material into voids formed by the foam structure.
Claim 13
Dependent Claim
16 words
The method of claim 1 wherein the solid foam material exhibits an amorphous and/or microcrystalline structure.
Claim 14
Dependent Claim
29 words
The method of claim 1 wherein the step of injecting comprises mixing the injected blowing liquid in the melted material to disperse the blowing liquid throughout said melted material.
Claim 15
Dependent Claim
27 words
A material comprising: a bulk metallic material having an uninterrupted foam glass and/or microcrystallite structure over dimensions greater than 1 mm in each of three orthogonal directions.
Claim 16
Dependent Claim
27 words
A material comprising: a bulk metallic material having an uninterrupted foam glass and/or microcrystallite structure over dimensions greater than 1 mm in each of three orthogonal directions.
Claim 17
Dependent Claim
30 words
The material of claim 14 wherein the bulk metallic material has an uninterrupted foam glass and/or microcrystallite structure over dimensions greater than 1 cm in each of three orthogonal directions.
Claim 18
Dependent Claim
13 words
The material of claim 14 wherein the metallic material is an organo-metallic material.
References Cited (Backward Citations)
US2434775A
Cited
US3592628A
Cited
US3725318A
Cited
US4096218A
Cited
US3970732A
Cited
FR2282479A1
Cited
US4454087A
Cited
US4834816A
Cited
US4743417A
Cited
US4598101A
Cited
US4939296A
Cited
US5181549A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-01-23 | 1998-07-25 | 1999-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-01-23 | 2002-07-25 | 2003-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-01-23 | 2006-07-25 | 2007-01-24 | $7700.00 | Window Closed / Lapsed |