Method for making submicrometer carbides, submicrometer solid solution carbides, and the material resulting therefrom
Assignee: Borchers Americas Inc
•
Filing: 1993-08-09
•
Granted: 1995-01-10
•
Expires: 2013-08-09
Abstract
Abstract A method for making submicrometer metallic carbides and submicrometer solid solution metallic carbides from sources of at least one metallic oxide and carbon involves the rapid heating of a reactive particulate mixture of at least one metallic oxide and carbon in order to achieve a resulting particulate size of less than 1 micrometer. Submicrometer sized metallic carbides and solid solution metallic carbides have found great use in commercial ceramic applications. It has been found that the smaller sized particles produce a product having superior toughness and hardness. In addition, the submicrometer sized solid solution metallic carbide resulting from this method is also disclosed.
Inventors
- 👤 Stephen D. Dunmead
- 👤 William G. Moore
- 👤 Alan W. Weimer
- 👤 Glenn A. Eisman
- 👤 John P. Henley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:49
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/5622; B; B82; B82Y; B82Y30/00; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/921; C01B32/949; C04B35/5611; C04B35/5626; C04B35/622; C04B35/626; C04B35/62605; C04B35/6261; C04B35/62615; C04B35/62645; C04B35/6265; C04B35/62675; C04B35/6268; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3231; C04B2235/3232; C04B2235/3244; C04B2235/3251; C04B2235/3256; C04B2235/3258; C04B2235/38; C04B2235/3817; C04B2235/3839; C04B2235/3843; C04B2235/3847; C04B2235/42; C04B2235/422; C04B2235/424; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5445; C04B2235/5454; C04B2235/70; C04B2235/74; C04B2235/76; C04B2235/761
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
161 words
A method for making a particulate ceramic composition, consisting essentially of: rapidly carbothermally reducing a reactive particulate mixture of (a) at least one metallic oxide selected from the group consisting of the oxides of the Group IVB (Ti, Zr, Hf), Group VB (V, Nb, Ta); Group VIB (Cr, Mo, W) transition metals, and combinations thereof and (b) a carbon source by heating the reactive particulate mixture at a rate of between about 100K/sec to about 100,000,000K/sec in a substantially non-oxidizing atmosphere to an elevated temperature that makes carbothermal reduction of the reactive particulate mixture thermodynamically favorable; and holding the particulate mixture at the elevated temperature for a residence time sufficient to substantially convert said reactive particulate mixture into at least one product selected from the group consisting of (i) one or more metallic carbides, (ii) one or more metallic carbide precursors, (iii) one or more solid solution carbides, and (iv) one or more solid solution metallic carbide precursors, and combinations thereof.
Claim 2
Independent Claim
161 words
A method for making a particulate ceramic composition, consisting essentially of: rapidly carbothermally reducing a reactive particulate mixture of (a) at least one metallic oxide selected from the group consisting of the oxides of the Group IVB (Ti, Zr, Hf), Group VB (V, Nb, Ta); Group VIB (Cr, Mo, W) transition metals, and combinations thereof and (b) a carbon source by heating the reactive particulate mixture at a rate of between about 100K/sec to about 100,000,000K/sec in a substantially non-oxidizing atmosphere to an elevated temperature that makes carbothermal reduction of the reactive particulate mixture thermodynamically favorable; and holding the particulate mixture at the elevated temperature for a residence time sufficient to substantially convert said reactive particulate mixture into at least one product selected from the group consisting of (i) one or more metallic carbides, (ii) one or more metallic carbide precursors, (iii) one or more solid solution carbides, and (iv) one or more solid solution metallic carbide precursors, and combinations thereof.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein said product is a tungsten carbide precursor and the elevated temperature is within a range of from 1673K to 2673K.
Claim 4
Dependent Claim
17 words
The method of claim 1, wherein said residence time is from about 0.1 second to 30 minutes.
Claim 5
Dependent Claim
17 words
The method of claim 1, wherein said residence time is from about 0.1 second to 5 minutes.
Claim 6
Dependent Claim
17 words
The method of claim 1, wherein said residence time is from about 0.1 second to 30 seconds.
Claim 7
Dependent Claim
17 words
The method of claim 1, wherein said residence time is from about 0.1 second to 10 seconds.
Claim 8
Dependent Claim
22 words
The method of claim 1, wherein said heating rate is in the range of from about 10 2 to 10 8 K/second.
Claim 9
Dependent Claim
22 words
The method of claim 1, wherein said heating rate is in the range of from about 10 3 to 10 6 K/second.
Claim 10
Dependent Claim
22 words
The method of claim 1, wherein said heating rate is in the range of from about 10 4 to 10 5 K/second.
Claim 11
Dependent Claim
31 words
The method of claim 1, wherein said product is at least one metallic carbide selected from the group consisting of titanium carbide, zirconium carbide, hafnium carbide, tantalum carbide, and molybdenum carbide.
Claim 12
Dependent Claim
36 words
The method of claim 1, wherein said product is a tungsten carbide precursor that has a size of from about 0.01 to 0.2 micrometer and is capable of being further converted to substantially pure tungsten carbide.
Claim 13
Dependent Claim
38 words
The method of claim 1, wherein said product is at least one solid solution carbide selected from the group consisting of tungsten-titanium carbide, molybdenum-tantalum carbide, titanium-tantalum carbide, tungsten-titanium-tantalum carbide, hafnium-tantalum carbide, titanium-hafnium carbide, tantalum-tungsten carbide, and titanium-tantalum-hafnium carbide.
Claim 14
Dependent Claim
28 words
The method of claim 1, wherein said product is at least one solid solution metallic carbide precursor selected from the group consisting of tungsten-molybdenum carbide and tungsten-vanadium carbide.
Claim 15
Dependent Claim
27 words
The method of claim 1, wherein said step of preparing a reactive precursor is accomplished by milling the metallic oxide(s) and the carbon source with WC-Co media.
Claim 16
Dependent Claim
12 words
The method of claim 1, wherein said carbon source includes carbon black.
Claim 17
Dependent Claim
13 words
The method of claim 15, wherein the carbon black is acetylene carbon black.
Claim 18
Dependent Claim
76 words
The method of claim 1, wherein the product is a precursor selected from (ii) or (iv) and the precursor is subjected to a finishing step in which an amount of carbon sufficient to convert the precursor to a finished product is admixed with the precursor to form a mixture that is then heated to a finishing temperature and maintained at that temperature for a period of time sufficient to convert the precursor to a finished product.
Claim 19
Dependent Claim
52 words
The method of claim 17, wherein the precursor is a tungsten carbide precursor, a tungsten-molybdenum carbide precursor, a tungsten-titanium carbide precursor or a tungsten-vanadium carbide precursor and the finishing temperature is from about 1473 to about 1673K and the time at the finishing temperature is from about 15 to about 180 minutes.
Claim 20
Dependent Claim
16 words
The method of claim 17, wherein the mixture is subjected to a mixing action during finishing.
Claim 21
Dependent Claim
64 words
A solid solution metallic carbide, comprising at least two different metallic components, wherein the solid solution metallic carbide has a mean particle diameter between about 0.01 micrometer and about 1.0 micrometer, the two different metallic components being selected from the group consisting of Group IVB (Ti, Zr, Hf), Group VB (V, Nb, Ta), and Group VIB (Cr, Mo, W) transition metals, and combinations thereof.
Claim 22
Dependent Claim
64 words
A solid solution metallic carbide, comprising at least two different metallic components, wherein the solid solution metallic carbide has a mean particle diameter between about 0.01 micrometer and about 1.0 micrometer, the two different metallic components being selected from the group consisting of Group IVB (Ti, Zr, Hf), Group VB (V, Nb, Ta), and Group VIB (Cr, Mo, W) transition metals, and combinations thereof.
Claim 23
Dependent Claim
71 words
The solid solution metallic carbide of claim 20, wherein one of the two metallic components serves as a grain growth inhibitor and is present in an amount that is greater than 0 wt-% but less than 10 wt-%, the other metallic component is present in an amount that is greater than 90 wt-% but less than 100 wt-%, and the grain growth inhibitor is intimately admixed with the other metallic component.
Claim 24
Dependent Claim
41 words
A particulate metallic carbide having a mean as synthesized particle diameter that is between 0.01 micrometer and 0.3 micrometer and a metallic component that is selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and W.
Claim 25
Dependent Claim
41 words
A particulate metallic carbide having a mean as synthesized particle diameter that is between 0.01 micrometer and 0.3 micrometer and a metallic component that is selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo and W.
Claim 26
Dependent Claim
28 words
The metallic carbide of claim 22, wherein the metallic carbide is tungsten carbide and the mean as synthesized particle diameter that is between 0.01 micrometer and 0.2 micrometer.
References Cited (Backward Citations)
US1610061A
Cited
US3713865A
Cited
US3802847A
Cited
US4008090A
Cited
US3932594A
Cited
US4216009A
Cited
US4256496A
Cited
US4460697A
Cited
US4752456A
Cited
US4454105A
Cited
US4664899A
Cited
US4921531A
Cited
US4891341A
Cited
US4983354A
Cited
US5126121A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-01-09 | 1998-07-11 | 1999-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-01-09 | 2002-07-11 | 2003-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-01-09 | 2006-07-11 | 2007-01-10 | $7700.00 | Window Closed / Lapsed |